Eigenschaften
Allgemein
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Dichte | 2.72 g/cm³ Show Material materials with Dichte of 2.72 g/cm³ | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
2.72 g/cm³ Show Material materials with Dichte of 2.72 g/cm³ | O | ||
2.8 g/cm³ Show Material materials with Dichte of 2.8 g/cm³ | O |
Mechanisch
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Bending Fatigue Strength | 95.0 MPa Show Material materials with Bending Fatigue Strength of 95.0 MPa | O | AA Standards | ||
Dauerfestigkeit | 14 MPa Show Material materials with Dauerfestigkeit of 14 MPa | O | for 5x10⁸ cycles | ||
Dehnung | -195 °C | 38 % Show Material materials with Dehnung of 38 % | O | Elongation in 50 mm | |
-80 °C | 30 % Show Material materials with Dehnung of 30 % | O | Elongation in 50 mm | ||
9.0 % Show Material materials with Dehnung of 9.0 % | O | AA Standards, ASTM B209 | A50 | ||
12.0 % Show Material materials with Dehnung of 12.0 % | O | AA Standards, ASTM B209 | A50 | ||
14.0 % Show Material materials with Dehnung of 14.0 % | O | AA Standards, ASTM B209 | A100 | ||
15.0 % Show Material materials with Dehnung of 15.0 % | O | AA Standards, ASTM B209, ASTM B313 | A50 | ||
16.0 % Show Material materials with Dehnung of 16.0 % | O | AA Standards, ASTM B209, ASTM B547 | A50 | ||
18.0 % Show Material materials with Dehnung of 18.0 % | O | AA Standards, ASTM B209, ASTM B313, ASTM B547 | A50 | ||
18.0 % Show Material materials with Dehnung of 18.0 % | O | ||||
20.0 % Show Material materials with Dehnung of 20.0 % | O | AA Standards | A50 | ||
22.0 % Show Material materials with Dehnung of 22.0 % | O | AA Standards | A100 | ||
0 °C | 26 % Show Material materials with Dehnung of 26 % | O | Elongation in 50 mm | ||
24 °C | 25 % Show Material materials with Dehnung of 25 % | O | Elongation in 50 mm | ||
100 °C | 25 % Show Material materials with Dehnung of 25 % | O | Elongation in 50 mm | ||
150 °C | 35 % Show Material materials with Dehnung of 35 % | O | Elongation in 50 mm | ||
205 °C | 55 % Show Material materials with Dehnung of 55 % | O | Elongation in 50 mm | ||
260 °C | 70 % Show Material materials with Dehnung of 70 % | O | Elongation in 50 mm | ||
315 °C | 80 % Show Material materials with Dehnung of 80 % | O | Elongation in 50 mm | ||
370 °C | 90 % Show Material materials with Dehnung of 90 % | O | Elongation in 50 mm | ||
Elastizitätsmodul | 69.0 GPa Show Material materials with Elastizitätsmodul of 69.0 GPa | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 | ||
69 GPa Show Material materials with Elastizitätsmodul of 69 GPa | O | ||||
Härte, Brinell | 45.0 [-] Show Material materials with Härte, Brinell of 45.0 [-] | O | AA Standards | ||
45.0 [-] Show Material materials with Härte, Brinell of 45.0 [-] | O | 500 kg load, 10 mm ball | |||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 3000 Series Aluminium | |||
Poissonzahl | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | Typical for Wrought 3000 Series Aluminium | |||
Scherfestigkeit | 110.0 MPa Show Material materials with Scherfestigkeit of 110.0 MPa | O | |||
Schubmodule | 25.0 GPa Show Material materials with Schubmodule of 25.0 GPa | O | |||
Streckgrenze | -200 °C | 90 MPa Show Material materials with Streckgrenze of 90 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
-100 °C | 80 MPa Show Material materials with Streckgrenze of 80 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
-30 °C | 69 MPa Show Material materials with Streckgrenze of 69 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
60.0 MPa Show Material materials with Streckgrenze of 60.0 MPa | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 | RP02 | ||
69.0 MPa Show Material materials with Streckgrenze of 69.0 MPa | O | ||||
70.0 MPa Show Material materials with Streckgrenze of 70.0 MPa | O | AA Standards | RP02 | ||
25 °C | 69 MPa Show Material materials with Streckgrenze of 69 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
100 °C | 69 MPa Show Material materials with Streckgrenze of 69 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
200 °C | 65 MPa Show Material materials with Streckgrenze of 65 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
300 °C | 34 MPa Show Material materials with Streckgrenze of 34 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
400 °C | 9 MPa Show Material materials with Streckgrenze of 9 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
Zugfestigkeit | -195 °C | 290 MPa Show Material materials with Zugfestigkeit of 290 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
-80 °C | 193 MPa Show Material materials with Zugfestigkeit of 193 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
150.0 - 200.0 MPa Show Material materials with Zugfestigkeit of 150.0 - 200.0 MPa | O | AA Standards, ASTM B209, ASTM B313, ASTM B547 | |||
160.0 - 200.0 MPa Show Material materials with Zugfestigkeit of 160.0 - 200.0 MPa | O | AA Standards, ASTM B221 | |||
170.0 MPa Show Material materials with Zugfestigkeit of 170.0 MPa | O | ||||
180.0 MPa Show Material materials with Zugfestigkeit of 180.0 MPa | O | AA Standards | |||
0 °C | 180 MPa Show Material materials with Zugfestigkeit of 180 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
24 °C | 180 MPa Show Material materials with Zugfestigkeit of 180 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
100 °C | 180 MPa Show Material materials with Zugfestigkeit of 180 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
150 °C | 152 MPa Show Material materials with Zugfestigkeit of 152 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
205 °C | 97 MPa Show Material materials with Zugfestigkeit of 97 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
260 °C | 70 MPa Show Material materials with Zugfestigkeit of 70 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
315 °C | 52 MPa Show Material materials with Zugfestigkeit of 52 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
370 °C | 35 MPa Show Material materials with Zugfestigkeit of 35 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture |
Thermisch
| Property | Temperature | Value | Condition | Related Standards |
|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 2.4e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.4e-05 1/K | O | ||
20 °C | 2.3899999999999998e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.3899999999999998e-05 1/K | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 | |
100 °C | 2.3899999999999998e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.3899999999999998e-05 1/K | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 | |
Schmelzpunkt | 630.0 - 655.0 °C Show Material materials with Schmelzpunkt of 630.0 - 655.0 °C | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 | |
630.0 °C Show Material materials with Schmelzpunkt of 630.0 °C | O | |||
Spezifische Wärmekapazität | 890.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 890.0 J/(kg·K) | O | ||
Wärmeleitfähigkeit | 160.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 160.0 W/(m·K) | O | ||
163 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 163 W/(m·K) | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
Elektrisch
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Elektrische Leitfähigkeit | 24000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 24000000.0 S/m | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 | |
24000000 S/m Show Material materials with Elektrische Leitfähigkeit of 24000000 S/m | O | Typical/derived value | ||
Specific Electrical conductivity | 42.0 % IACS Show Material materials with Specific Electrical conductivity of 42.0 % IACS | O | Typical value | |
spezifischer Widerstand | 4.17e-08 Ω·m Show Material materials with spezifischer Widerstand of 4.17e-08 Ω·m | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 95.6 - 98.2 % Show Material materials with Aluminium of 95.6 - 98.2 % | O | |
Andere | 0.15 % Show Material materials with Andere of 0.15 % | O | |
Eisen | 0.70 % Show Material materials with Eisen of 0.70 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
0.7 % Show Material materials with Eisen of 0.7 % | O | ||
Kupfer | 0.25 % Show Material materials with Kupfer of 0.25 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
Magnesium | 0.8 - 1.3 % Show Material materials with Magnesium of 0.8 - 1.3 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
Mangan | 1.0 - 1.5 % Show Material materials with Mangan of 1.0 - 1.5 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
Silizium | 0.3 % Show Material materials with Silizium of 0.3 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
Zink | 0.25 % Show Material materials with Zink of 0.25 % | O | AA Standards, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (O, H32), sufficient (H34, H36, H38) | |
| Workability | general (condition): good (O), acceptable (H32, H34), poor(H36, H38) | |