Eigenschaften
Allgemein
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Dichte | 2.69 g/cm³ Show Material materials with Dichte of 2.69 g/cm³ | O | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
2.69 g/cm³ Show Material materials with Dichte of 2.69 g/cm³ | O | ||
2.7 g/cm³ Show Material materials with Dichte of 2.7 g/cm³ | O |
Mechanisch
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Bending Fatigue Strength | 85.0 MPa Show Material materials with Bending Fatigue Strength of 85.0 MPa | O | AA Standards | ||
Dauerfestigkeit | 83 MPa Show Material materials with Dauerfestigkeit of 83 MPa | O | for 5x10⁸ cycles | ||
Dehnung | 15.0 % Show Material materials with Dehnung of 15.0 % | O | AA Standards, ASTM B209 | A50 | |
17.0 % Show Material materials with Dehnung of 17.0 % | O | AA Standards, ASTM B209 | A50 | ||
18.0 % Show Material materials with Dehnung of 18.0 % | O | AA Standards, ASTM B209 | A100 | ||
19.0 % Show Material materials with Dehnung of 19.0 % | O | AA Standards, ASTM B209, ASTM B313 | A50 | ||
20.0 % Show Material materials with Dehnung of 20.0 % | O | AA Standards, ASTM B209, ASTM B313, ASTM B547 | A50 | ||
21.0 % Show Material materials with Dehnung of 21.0 % | O | ||||
24.0 % Show Material materials with Dehnung of 24.0 % | O | AA Standards | A50 | ||
24 % Show Material materials with Dehnung of 24 % | O | ||||
Elastizitätsmodul | 69.0 GPa Show Material materials with Elastizitätsmodul of 69.0 GPa | O | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 | ||
69 GPa Show Material materials with Elastizitätsmodul of 69 GPa | O | ||||
Härte, Brinell | 36.0 [-] Show Material materials with Härte, Brinell of 36.0 [-] | O | AA Standards | ||
36.0 [-] Show Material materials with Härte, Brinell of 36.0 [-] | O | 500 kg load, 10 mm ball | |||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | |||
Poissonzahl | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | |||
Scherfestigkeit | 105.0 MPa Show Material materials with Scherfestigkeit of 105.0 MPa | O | |||
Schubmodule | 25.9 GPa Show Material materials with Schubmodule of 25.9 GPa | O | |||
Streckgrenze | -196 °C | 70 MPa Show Material materials with Streckgrenze of 70 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
-80 °C | 60 MPa Show Material materials with Streckgrenze of 60 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
-28 °C | 55 MPa Show Material materials with Streckgrenze of 55 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
40.0 MPa Show Material materials with Streckgrenze of 40.0 MPa | O | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 | RP02 | ||
50.0 MPa Show Material materials with Streckgrenze of 50.0 MPa | O | ||||
55.0 MPa Show Material materials with Streckgrenze of 55.0 MPa | O | AA Standards | RP02 | ||
24 °C | 55 MPa Show Material materials with Streckgrenze of 55 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
100 °C | 55 MPa Show Material materials with Streckgrenze of 55 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
149 °C | 55 MPa Show Material materials with Streckgrenze of 55 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
204 °C | 50 MPa Show Material materials with Streckgrenze of 50 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
260 °C | 41 MPa Show Material materials with Streckgrenze of 41 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
316 °C | 29 MPa Show Material materials with Streckgrenze of 29 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
371 °C | 18 MPa Show Material materials with Streckgrenze of 18 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
Zugfestigkeit | -195 °C | 255 MPa Show Material materials with Zugfestigkeit of 255 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
-80 °C | 152 MPa Show Material materials with Zugfestigkeit of 152 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
125.0 - 165.0 MPa Show Material materials with Zugfestigkeit of 125.0 - 165.0 MPa | O | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B547 | |||
125.0 MPa Show Material materials with Zugfestigkeit of 125.0 MPa | O | AA Standards, ASTM B483 | |||
140.0 MPa Show Material materials with Zugfestigkeit of 140.0 MPa | O | ||||
145.0 MPa Show Material materials with Zugfestigkeit of 145.0 MPa | O | AA Standards | |||
0 °C | 145 MPa Show Material materials with Zugfestigkeit of 145 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
24 °C | 145 MPa Show Material materials with Zugfestigkeit of 145 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
100 °C | 145 MPa Show Material materials with Zugfestigkeit of 145 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
150 °C | 130 MPa Show Material materials with Zugfestigkeit of 130 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
205 °C | 97 MPa Show Material materials with Zugfestigkeit of 97 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
260 °C | 62 MPa Show Material materials with Zugfestigkeit of 62 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
315 °C | 40 MPa Show Material materials with Zugfestigkeit of 40 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
370 °C | 27 MPa Show Material materials with Zugfestigkeit of 27 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture |
Thermisch
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 2.4e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.4e-05 1/K | O | |||
20 °C | 2.38e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.38e-05 1/K | O | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 | ||
100 °C | 2.38e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.38e-05 1/K | O | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 | ||
Max. Betriebstemperatur | 150.0 °C Show Material materials with Max. Betriebstemperatur of 150.0 °C | Typical for Wrought 5000 Series Aluminium | |||
Schmelzpunkt | 625.0 - 650.0 °C Show Material materials with Schmelzpunkt of 625.0 - 650.0 °C | O | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 | ||
630.0 °C Show Material materials with Schmelzpunkt of 630.0 °C | O | ||||
Spezifische Wärmekapazität | 900.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 900.0 J/(kg·K) | O | |||
Wärmeleitfähigkeit | 190.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 190.0 W/(m·K) | O | |||
193 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 193 W/(m·K) | O | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Elektrisch
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Elektrische Leitfähigkeit | 29000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 29000000.0 S/m | O | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 | |
29000000 S/m Show Material materials with Elektrische Leitfähigkeit of 29000000 S/m | O | Typical/derived value | ||
Specific Electrical conductivity | 50.0 % IACS Show Material materials with Specific Electrical conductivity of 50.0 % IACS | O | Typical value | |
spezifischer Widerstand | 3.45e-08 Ω·m Show Material materials with spezifischer Widerstand of 3.45e-08 Ω·m | O | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 96.3 - 98.9 % Show Material materials with Aluminium of 96.3 - 98.9 % | O | |
Andere | 0.15 % Show Material materials with Andere of 0.15 % | O | |
Chrom | 0.1 % Show Material materials with Chrom of 0.1 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Eisen | 0.70 % Show Material materials with Eisen of 0.70 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
0.7 % Show Material materials with Eisen of 0.7 % | O | ||
Kupfer | 0.2 % Show Material materials with Kupfer of 0.2 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Magnesium | 1.1 - 1.8 % Show Material materials with Magnesium of 1.1 - 1.8 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Mangan | 0.1 % Show Material materials with Mangan of 0.1 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Silizium | 0.4 % Show Material materials with Silizium of 0.4 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Zink | 0.25 % Show Material materials with Zink of 0.25 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: not suitable (O), poor (H32, H34), sufficient (H36, H38) | |
| Workability | general (condition): good (O, H32), acceptable (H34), poor(H36, H38) | |