Eigenschaften
Allgemein
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Dichte | 2.68 g/cm³ Show Material materials with Dichte of 2.68 g/cm³ | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547 |
2.68 g/cm³ Show Material materials with Dichte of 2.68 g/cm³ | H34 | ||
2.7 g/cm³ Show Material materials with Dichte of 2.7 g/cm³ | H34 |
Mechanisch
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Bending Fatigue Strength | 125.0 MPa Show Material materials with Bending Fatigue Strength of 125.0 MPa | H34 | AA Standards | ||
Dauerfestigkeit | 125 MPa Show Material materials with Dauerfestigkeit of 125 MPa | H34 | for 5x10⁸ cycles | ||
Dehnung | -195 °C | 28 % Show Material materials with Dehnung of 28 % | H34 | Elongation in 50 mm | |
-80 °C | 21 % Show Material materials with Dehnung of 21 % | H34 | Elongation in 50 mm | ||
3.0 % Show Material materials with Dehnung of 3.0 % | H34 | AA Standards, ASTM B209 | A50 | ||
4.0 % Show Material materials with Dehnung of 4.0 % | H34 | AA Standards, ASTM B209, ASTM B313 | A50 | ||
6.0 % Show Material materials with Dehnung of 6.0 % | H34 | AA Standards, ASTM B209, ASTM B313, ASTM B547 | A50 | ||
9.0 % Show Material materials with Dehnung of 9.0 % | H34 | AA Standards, ASTM B209 | A100 | ||
9.1 % Show Material materials with Dehnung of 9.1 % | H34 | ||||
10.0 % Show Material materials with Dehnung of 10.0 % | H34 | AA Standards, ASTM B209, ASTM B547 | A50 | ||
12.0 % Show Material materials with Dehnung of 12.0 % | H34 | AA Standards | A100 | ||
0 °C | 18 % Show Material materials with Dehnung of 18 % | H34 | Elongation in 50 mm | ||
24 °C | 16 % Show Material materials with Dehnung of 16 % | H34 | Elongation in 50 mm | ||
100 °C | 18 % Show Material materials with Dehnung of 18 % | H34 | Elongation in 50 mm | ||
150 °C | 27 % Show Material materials with Dehnung of 27 % | H34 | Elongation in 50 mm | ||
205 °C | 45 % Show Material materials with Dehnung of 45 % | H34 | Elongation in 50 mm | ||
260 °C | 80 % Show Material materials with Dehnung of 80 % | H34 | Elongation in 50 mm | ||
315 °C | 110 % Show Material materials with Dehnung of 110 % | H34 | Elongation in 50 mm | ||
370 °C | 130 % Show Material materials with Dehnung of 130 % | H34 | Elongation in 50 mm | ||
Elastizitätsmodul | 70.0 GPa Show Material materials with Elastizitätsmodul of 70.0 GPa | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547 | ||
70 GPa Show Material materials with Elastizitätsmodul of 70 GPa | H34 | ||||
Härte, Brinell | 68.0 [-] Show Material materials with Härte, Brinell of 68.0 [-] | H34 | AA Standards | ||
68.0 [-] Show Material materials with Härte, Brinell of 68.0 [-] | H34 | 500 kg load, 10 mm ball | |||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | |||
Poissonzahl | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | |||
Scherfestigkeit | 145.0 MPa Show Material materials with Scherfestigkeit of 145.0 MPa | H34 | |||
Schubmodule | 25.9 GPa Show Material materials with Schubmodule of 25.9 GPa | H34 | |||
Streckgrenze | -196 °C | 248 MPa Show Material materials with Streckgrenze of 248 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
-80 °C | 221 MPa Show Material materials with Streckgrenze of 221 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
-28 °C | 214 MPa Show Material materials with Streckgrenze of 214 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
180.0 MPa Show Material materials with Streckgrenze of 180.0 MPa | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547 | RP02 | ||
210.0 MPa Show Material materials with Streckgrenze of 210.0 MPa | H34 | ||||
215.0 MPa Show Material materials with Streckgrenze of 215.0 MPa | H34 | AA Standards | RP02 | ||
24 °C | 214 MPa Show Material materials with Streckgrenze of 214 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
100 °C | 214 MPa Show Material materials with Streckgrenze of 214 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
149 °C | 186 MPa Show Material materials with Streckgrenze of 186 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
204 °C | 103 MPa Show Material materials with Streckgrenze of 103 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
260 °C | 52 MPa Show Material materials with Streckgrenze of 52 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
316 °C | 38 MPa Show Material materials with Streckgrenze of 38 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
371 °C | 21 MPa Show Material materials with Streckgrenze of 21 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
Zugfestigkeit | -195 °C | 380 MPa Show Material materials with Zugfestigkeit of 380 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
-80 °C | 275 MPa Show Material materials with Zugfestigkeit of 275 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
235.0 - 285.0 MPa Show Material materials with Zugfestigkeit of 235.0 - 285.0 MPa | H34 | AA Standards, ASTM B209, ASTM B313, ASTM B547 | |||
235.0 MPa Show Material materials with Zugfestigkeit of 235.0 MPa | H34 | AA Standards, ASTM B210, ASTM B211, ASTM B234, ASTM B483 | |||
260.0 MPa Show Material materials with Zugfestigkeit of 260.0 MPa | H34 | AA Standards | |||
0 °C | 262 MPa Show Material materials with Zugfestigkeit of 262 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
24 °C | 262 MPa Show Material materials with Zugfestigkeit of 262 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
100 °C | 262 MPa Show Material materials with Zugfestigkeit of 262 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
150 °C | 207 MPa Show Material materials with Zugfestigkeit of 207 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
205 °C | 165 MPa Show Material materials with Zugfestigkeit of 165 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
260 °C | 83 MPa Show Material materials with Zugfestigkeit of 83 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
315 °C | 52 MPa Show Material materials with Zugfestigkeit of 52 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
370 °C | 35 MPa Show Material materials with Zugfestigkeit of 35 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture |
Thermisch
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 2.4e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.4e-05 1/K | H34 | |||
20 °C | 2.38e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.38e-05 1/K | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547 | ||
100 °C | 2.38e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.38e-05 1/K | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547 | ||
Max. Betriebstemperatur | 150.0 °C Show Material materials with Max. Betriebstemperatur of 150.0 °C | Typical for Wrought 5000 Series Aluminium | |||
Schmelzpunkt | 605.0 - 650.0 °C Show Material materials with Schmelzpunkt of 605.0 - 650.0 °C | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547 | ||
610.0 °C Show Material materials with Schmelzpunkt of 610.0 °C | H34 | ||||
Spezifische Wärmekapazität | 900.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 900.0 J/(kg·K) | H34 | |||
Wärmeleitfähigkeit | 138 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 138 W/(m·K) | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547 | ||
140.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 140.0 W/(m·K) | H34 |
Elektrisch
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Elektrische Leitfähigkeit | 20000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 20000000.0 S/m | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547 |
spezifischer Widerstand | 5e-08 Ω·m Show Material materials with spezifischer Widerstand of 5e-08 Ω·m | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 95.8 - 97.7 % Show Material materials with Aluminium of 95.8 - 97.7 % | H34 | |
Andere | 0.15 % Show Material materials with Andere of 0.15 % | H34 | |
Chrom | 0.15 - 0.35 % Show Material materials with Chrom of 0.15 - 0.35 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547 |
Eisen | 0.40 % Show Material materials with Eisen of 0.40 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547 |
0.4 % Show Material materials with Eisen of 0.4 % | H34 | ||
Kupfer | 0.1 % Show Material materials with Kupfer of 0.1 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547 |
Magnesium | 2.2 - 2.8 % Show Material materials with Magnesium of 2.2 - 2.8 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547 |
Mangan | 0.1 % Show Material materials with Mangan of 0.1 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547 |
Silizium | 0.25 % Show Material materials with Silizium of 0.25 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547 |
Zink | 0.1 % Show Material materials with Zink of 0.1 % | H34 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: limited brazing | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (O, H32), sufficient (H34, H36, H38) | |
| Workability | general (condition): good (O), acceptable (H32, H34), poor(H36, H38) | |