Eigenschaften
Allgemein
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Dichte | 2.64 g/cm³ Show Material materials with Dichte of 2.64 g/cm³ | H32 | AA Standards, ASTM B211, ASTM B316 |
2.7 g/cm³ Show Material materials with Dichte of 2.7 g/cm³ | H32 |
Mechanisch
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Elastizitätsmodul | 71.0 GPa Show Material materials with Elastizitätsmodul of 71.0 GPa | H32 | AA Standards, ASTM B211, ASTM B316 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Poissonzahl | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Schubmodule | 26.0 - 26.5 GPa Show Material materials with Schubmodule of 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | ||
Zugfestigkeit | 300.0 MPa Show Material materials with Zugfestigkeit of 300.0 MPa | H32 | AA Standards, ASTM B211 | |
300.0 - 360.0 MPa Show Material materials with Zugfestigkeit of 300.0 - 360.0 MPa | H32 | AA Standards, ASTM B316 | ||
350.0 MPa Show Material materials with Zugfestigkeit of 350.0 MPa | H32 |
Thermisch
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 2.4e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.4e-05 1/K | H32 | |||
20 °C | 2.41e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.41e-05 1/K | H32 | AA Standards, ASTM B211, ASTM B316 | ||
100 °C | 2.41e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.41e-05 1/K | H32 | AA Standards, ASTM B211, ASTM B316 | ||
Max. Betriebstemperatur | 150.0 °C Show Material materials with Max. Betriebstemperatur of 150.0 °C | Typical for Wrought 5000 Series Aluminium | |||
Schmelzpunkt | 565.0 - 640.0 °C Show Material materials with Schmelzpunkt of 565.0 - 640.0 °C | H32 | AA Standards, ASTM B211, ASTM B316 | ||
570.0 °C Show Material materials with Schmelzpunkt of 570.0 °C | H32 | ||||
Spezifische Wärmekapazität | 910.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 910.0 J/(kg·K) | H32 | |||
Wärmeleitfähigkeit | 109.0 - 117.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 109.0 - 117.0 W/(m·K) | H32 | AA Standards, ASTM B211, ASTM B316 |
Elektrisch
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Elektrische Leitfähigkeit | 16000000.0 - 17000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 16000000.0 - 17000000.0 S/m | H32 | AA Standards, ASTM B211, ASTM B316 |
spezifischer Widerstand | 5.88e-08 - 6.25e-08 Ω·m Show Material materials with spezifischer Widerstand of 5.88e-08 - 6.25e-08 Ω·m | H32 | AA Standards, ASTM B211, ASTM B316 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 93.0 - 95.4 % Show Material materials with Aluminium of 93.0 - 95.4 % | H32 | |
Andere | 0.15 % Show Material materials with Andere of 0.15 % | H32 | |
Chrom | 0.05 - 0.2 % Show Material materials with Chrom of 0.05 - 0.2 % | H32 | AA Standards, ASTM B211, ASTM B316 |
Eisen | 0.40 % Show Material materials with Eisen of 0.40 % | H32 | AA Standards, ASTM B211, ASTM B316 |
0.4 % Show Material materials with Eisen of 0.4 % | H32 | ||
Kupfer | 0.1 % Show Material materials with Kupfer of 0.1 % | H32 | AA Standards, ASTM B211, ASTM B316 |
Magnesium | 4.5 - 5.6 % Show Material materials with Magnesium of 4.5 - 5.6 % | H32 | AA Standards, ASTM B211, ASTM B316 |
Mangan | 0.05 - 0.2 % Show Material materials with Mangan of 0.05 - 0.2 % | H32 | AA Standards, ASTM B211, ASTM B316 |
Silizium | 0.3 % Show Material materials with Silizium of 0.3 % | H32 | AA Standards, ASTM B211, ASTM B316 |
Zink | 0.1 % Show Material materials with Zink of 0.1 % | H32 | AA Standards, ASTM B211, ASTM B316 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: kein Schadensfall im Betrieb, eingeschränkte Schäden bei den Labortests (O, H111, H12, H32, H14, H34), c (H18, H38), d (H192, H392), general: sehr gut, ohne Schutz in industrieller oder Seewasser-Atmosphäre (O, H111, H12, H32, H14, H34, H18, H38), b (H192, H392) | |
| General machinability | General: poor (O, H111, H12, H32), sufficient (H14, H34, H18, H38), good to acceptable (H192, H392) | |
| Workability | general (condition): good (O, H111), acceptable (H12, H32, H14, H34), poor(H18, H38), d (H192, H392) | |