Eigenschaften
Allgemein
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Dichte | 2.66 g/cm³ Show Material materials with Dichte of 2.66 g/cm³ | H116 | AA Standards |
2.7 g/cm³ Show Material materials with Dichte of 2.7 g/cm³ | H116 |
Mechanisch
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Dehnung | 11.0 % Show Material materials with Dehnung of 11.0 % | H116 | ||
12.0 % Show Material materials with Dehnung of 12.0 % | H116 | AA Standards | A50 | |
Elastizitätsmodul | 71.0 GPa Show Material materials with Elastizitätsmodul of 71.0 GPa | H116 | AA Standards | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Poissonzahl | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Schubmodule | 26.0 - 26.5 GPa Show Material materials with Schubmodule of 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | ||
Streckgrenze | 205.0 MPa Show Material materials with Streckgrenze of 205.0 MPa | H116 | AA Standards | RP02 |
220.0 MPa Show Material materials with Streckgrenze of 220.0 MPa | H116 | |||
Zugfestigkeit | 290.0 MPa Show Material materials with Zugfestigkeit of 290.0 MPa | H116 | AA Standards | |
310.0 MPa Show Material materials with Zugfestigkeit of 310.0 MPa | H116 |
Thermisch
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 2.4e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.4e-05 1/K | H116 | |||
20 °C | 2.38e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.38e-05 1/K | H116 | AA Standards | ||
100 °C | 2.38e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.38e-05 1/K | H116 | AA Standards | ||
Max. Betriebstemperatur | 150.0 °C Show Material materials with Max. Betriebstemperatur of 150.0 °C | Typical for Wrought 5000 Series Aluminium | |||
Schmelzpunkt | 585.0 - 640.0 °C Show Material materials with Schmelzpunkt of 585.0 - 640.0 °C | H116 | AA Standards | ||
590.0 °C Show Material materials with Schmelzpunkt of 590.0 °C | H116 | ||||
Spezifische Wärmekapazität | 900.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 900.0 J/(kg·K) | H116 | |||
Wärmeleitfähigkeit | 126 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 126 W/(m·K) | H116 | AA Standards | ||
130.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 130.0 W/(m·K) | H116 |
Elektrisch
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Elektrische Leitfähigkeit | 18000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 18000000.0 S/m | H116 | AA Standards |
spezifischer Widerstand | 5.56e-08 Ω·m Show Material materials with spezifischer Widerstand of 5.56e-08 Ω·m | H116 | AA Standards |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 93.0 - 96.3 % Show Material materials with Aluminium of 93.0 - 96.3 % | H116 | |
Andere | 0.15 % Show Material materials with Andere of 0.15 % | H116 | |
Chrom | 0.05 - 0.25 % Show Material materials with Chrom of 0.05 - 0.25 % | H116 | AA Standards |
Eisen | 0.50 % Show Material materials with Eisen of 0.50 % | H116 | AA Standards |
0.5 % Show Material materials with Eisen of 0.5 % | H116 | ||
Kupfer | 0.1 % Show Material materials with Kupfer of 0.1 % | H116 | AA Standards |
Magnesium | 3.5 - 4.5 % Show Material materials with Magnesium of 3.5 - 4.5 % | H116 | AA Standards |
Mangan | 0.2 - 0.7 % Show Material materials with Mangan of 0.2 - 0.7 % | H116 | AA Standards |
Silizium | 0.4 % Show Material materials with Silizium of 0.4 % | H116 | AA Standards |
Titan | 0.15 % Show Material materials with Titan of 0.15 % | H116 | AA Standards |
Zink | 0.25 % Show Material materials with Zink of 0.25 % | H116 | AA Standards |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests (O, H32, H116, H111), no damage during operation, limited damage during laboratory tests (H34, H36, H38), general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (O, H32, H116, H111), sufficient (H34, H36, H38) | |
| Workability | general (condition): good (O), acceptable (H32, H116, H111), poor(H36, H38) | |