Eigenschaften
Allgemein
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Dichte | 2.66 g/cm³ Show Material materials with Dichte of 2.66 g/cm³ | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547 |
2.66 g/cm³ Show Material materials with Dichte of 2.66 g/cm³ | O | ||
2.7 g/cm³ Show Material materials with Dichte of 2.7 g/cm³ | O |
Mechanisch
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Dehnung | -195 °C | 46 % Show Material materials with Dehnung of 46 % | O | Elongation in 50 mm | |
-80 °C | 35 % Show Material materials with Dehnung of 35 % | O | Elongation in 50 mm | ||
12.0 % Show Material materials with Dehnung of 12.0 % | O | AA Standards, ASTM B210, ASTM B221, ASTM B241, ASTM B345 | A100 | ||
14.0 % Show Material materials with Dehnung of 14.0 % | O | AA Standards, ASTM B210, ASTM B221, ASTM B241, ASTM B345 | A50 | ||
14.0 % Show Material materials with Dehnung of 14.0 % | O | AA Standards, ASTM B209 | A100 | ||
15.0 % Show Material materials with Dehnung of 15.0 % | O | AA Standards, ASTM B209 | A50 | ||
16.0 % Show Material materials with Dehnung of 16.0 % | O | AA Standards, ASTM B209, ASTM B313, ASTM B547 | A50 | ||
18.0 % Show Material materials with Dehnung of 18.0 % | O | AA Standards, ASTM B209, ASTM B313, ASTM B547 | A50 | ||
19.0 % Show Material materials with Dehnung of 19.0 % | O | ||||
22.0 % Show Material materials with Dehnung of 22.0 % | O | AA Standards | A50 | ||
0 °C | 32 % Show Material materials with Dehnung of 32 % | O | Elongation in 50 mm | ||
24 °C | 30 % Show Material materials with Dehnung of 30 % | O | Elongation in 50 mm | ||
100 °C | 36 % Show Material materials with Dehnung of 36 % | O | Elongation in 50 mm | ||
150 °C | 50 % Show Material materials with Dehnung of 50 % | O | Elongation in 50 mm | ||
205 °C | 60 % Show Material materials with Dehnung of 60 % | O | Elongation in 50 mm | ||
260 °C | 80 % Show Material materials with Dehnung of 80 % | O | Elongation in 50 mm | ||
315 °C | 110 % Show Material materials with Dehnung of 110 % | O | Elongation in 50 mm | ||
370 °C | 130 % Show Material materials with Dehnung of 130 % | O | Elongation in 50 mm | ||
Elastizitätsmodul | 71.0 GPa Show Material materials with Elastizitätsmodul of 71.0 GPa | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547 | ||
71 GPa Show Material materials with Elastizitätsmodul of 71 GPa | O | ||||
Kompressionsmodul | 72.4 MPa Show Material materials with Kompressionsmodul of 72.4 MPa | O | |||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | |||
Poissonzahl | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | |||
Scherfestigkeit | 160.0 MPa Show Material materials with Scherfestigkeit of 160.0 MPa | O | |||
Schubmodule | 26.4 GPa Show Material materials with Schubmodule of 26.4 GPa | O | |||
Streckgrenze | -196 °C | 131 MPa Show Material materials with Streckgrenze of 131 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
-80 °C | 117 MPa Show Material materials with Streckgrenze of 117 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
-28 °C | 117 MPa Show Material materials with Streckgrenze of 117 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
95.0 MPa Show Material materials with Streckgrenze of 95.0 MPa | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547 | RP02 | ||
110.0 MPa Show Material materials with Streckgrenze of 110.0 MPa | O | ||||
115.0 MPa Show Material materials with Streckgrenze of 115.0 MPa | O | AA Standards | RP02 | ||
24 °C | 117 MPa Show Material materials with Streckgrenze of 117 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
100 °C | 117 MPa Show Material materials with Streckgrenze of 117 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
149 °C | 110 MPa Show Material materials with Streckgrenze of 110 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
204 °C | 103 MPa Show Material materials with Streckgrenze of 103 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
260 °C | 76 MPa Show Material materials with Streckgrenze of 76 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
316 °C | 52 MPa Show Material materials with Streckgrenze of 52 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
Zugfestigkeit | -195 °C | 380 MPa Show Material materials with Zugfestigkeit of 380 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
-80 °C | 270 MPa Show Material materials with Zugfestigkeit of 270 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
240.0 - 305.0 MPa Show Material materials with Zugfestigkeit of 240.0 - 305.0 MPa | O | AA Standards, ASTM B209, ASTM B313, ASTM B547 | |||
240.0 - 315.0 MPa Show Material materials with Zugfestigkeit of 240.0 - 315.0 MPa | O | AA Standards, ASTM B210, ASTM B221, ASTM B241, ASTM B345 | |||
260.0 MPa Show Material materials with Zugfestigkeit of 260.0 MPa | O | AA Standards | |||
0 °C | 262 MPa Show Material materials with Zugfestigkeit of 262 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
270.0 MPa Show Material materials with Zugfestigkeit of 270.0 MPa | O | ||||
24 °C | 262 MPa Show Material materials with Zugfestigkeit of 262 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
100 °C | 262 MPa Show Material materials with Zugfestigkeit of 262 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
150 °C | 200 MPa Show Material materials with Zugfestigkeit of 200 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
205 °C | 152 MPa Show Material materials with Zugfestigkeit of 152 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
260 °C | 117 MPa Show Material materials with Zugfestigkeit of 117 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
315 °C | 75 MPa Show Material materials with Zugfestigkeit of 75 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
370 °C | 40 MPa Show Material materials with Zugfestigkeit of 40 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture |
Thermisch
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 2.4e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.4e-05 1/K | O | |||
20 °C | 2.38e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.38e-05 1/K | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547 | ||
100 °C | 2.38e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.38e-05 1/K | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547 | ||
Max. Betriebstemperatur | 150.0 °C Show Material materials with Max. Betriebstemperatur of 150.0 °C | Typical for Wrought 5000 Series Aluminium | |||
Schmelzpunkt | 585.0 - 640.0 °C Show Material materials with Schmelzpunkt of 585.0 - 640.0 °C | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547 | ||
590.0 °C Show Material materials with Schmelzpunkt of 590.0 °C | O | ||||
Spezifische Wärmekapazität | 900.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 900.0 J/(kg·K) | O | |||
Wärmeleitfähigkeit | 126 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 126 W/(m·K) | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547 | ||
130.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 130.0 W/(m·K) | O |
Elektrisch
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Elektrische Leitfähigkeit | 18000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 18000000.0 S/m | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547 |
spezifischer Widerstand | 5.56e-08 Ω·m Show Material materials with spezifischer Widerstand of 5.56e-08 Ω·m | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 93.0 - 96.3 % Show Material materials with Aluminium of 93.0 - 96.3 % | O | |
Andere | 0.15 % Show Material materials with Andere of 0.15 % | O | |
Chrom | 0.05 - 0.25 % Show Material materials with Chrom of 0.05 - 0.25 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547 |
Eisen | 0.50 % Show Material materials with Eisen of 0.50 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547 |
0.5 % Show Material materials with Eisen of 0.5 % | O | ||
Kupfer | 0.1 % Show Material materials with Kupfer of 0.1 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547 |
Magnesium | 3.5 - 4.5 % Show Material materials with Magnesium of 3.5 - 4.5 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547 |
Mangan | 0.2 - 0.7 % Show Material materials with Mangan of 0.2 - 0.7 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547 |
Silizium | 0.4 % Show Material materials with Silizium of 0.4 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547 |
Titan | 0.15 % Show Material materials with Titan of 0.15 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547 |
Zink | 0.25 % Show Material materials with Zink of 0.25 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests (O, H32, H116, H111), no damage during operation, limited damage during laboratory tests (H34, H36, H38), general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (O, H32, H116, H111), sufficient (H34, H36, H38) | |
| Workability | general (condition): good (O), acceptable (H32, H116, H111), poor(H36, H38) | |