Eigenschaften
Allgemein
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Dichte | 2.66 g/cm³ Show Material materials with Dichte of 2.66 g/cm³ | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B313, ASTM B547 |
2.66 g/cm³ Show Material materials with Dichte of 2.66 g/cm³ | O | ||
2.7 g/cm³ Show Material materials with Dichte of 2.7 g/cm³ | O |
Mechanisch
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Bending Fatigue Strength | 115.0 MPa Show Material materials with Bending Fatigue Strength of 115.0 MPa | O | AA Standards | ||
Dauerfestigkeit | 117 MPa Show Material materials with Dauerfestigkeit of 117 MPa | O | for 5x10⁸ cycles | ||
Dehnung | -195 °C | 46 % Show Material materials with Dehnung of 46 % | O | Elongation in 50 mm | |
-80 °C | 35 % Show Material materials with Dehnung of 35 % | O | Elongation in 50 mm | ||
9.0 % Show Material materials with Dehnung of 9.0 % | O | AA Standards, ASTM B210 | A100 | ||
10.0 % Show Material materials with Dehnung of 10.0 % | O | AA Standards, ASTM B210 | A50 | ||
12.0 % Show Material materials with Dehnung of 12.0 % | O | AA Standards, ASTM B209 | A50 | ||
13.0 % Show Material materials with Dehnung of 13.0 % | O | AA Standards, ASTM B209, ASTM B313 | A50 | ||
16.0 % Show Material materials with Dehnung of 16.0 % | O | AA Standards, ASTM B209, ASTM B313, ASTM B547 | A50 | ||
16.0 % Show Material materials with Dehnung of 16.0 % | O | AA Standards, ASTM B209 | A100 | ||
18.0 % Show Material materials with Dehnung of 18.0 % | O | AA Standards, ASTM B209, ASTM B547 | A50 | ||
21.0 % Show Material materials with Dehnung of 21.0 % | O | ||||
22.0 % Show Material materials with Dehnung of 22.0 % | O | AA Standards, ASTM B211 | A100 | ||
25.0 % Show Material materials with Dehnung of 25.0 % | O | AA Standards, ASTM B211 | A50 | ||
27.0 % Show Material materials with Dehnung of 27.0 % | O | AA Standards | A50 | ||
0 °C | 32 % Show Material materials with Dehnung of 32 % | O | Elongation in 50 mm | ||
24 °C | 30 % Show Material materials with Dehnung of 30 % | O | Elongation in 50 mm | ||
100 °C | 36 % Show Material materials with Dehnung of 36 % | O | Elongation in 50 mm | ||
150 °C | 50 % Show Material materials with Dehnung of 50 % | O | Elongation in 50 mm | ||
205 °C | 60 % Show Material materials with Dehnung of 60 % | O | Elongation in 50 mm | ||
260 °C | 80 % Show Material materials with Dehnung of 80 % | O | Elongation in 50 mm | ||
315 °C | 110 % Show Material materials with Dehnung of 110 % | O | Elongation in 50 mm | ||
370 °C | 130 % Show Material materials with Dehnung of 130 % | O | Elongation in 50 mm | ||
Elastizitätsmodul | 70.0 GPa Show Material materials with Elastizitätsmodul of 70.0 GPa | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B313, ASTM B547 | ||
70 GPa Show Material materials with Elastizitätsmodul of 70 GPa | O | ||||
Härte, Brinell | 58.0 [-] Show Material materials with Härte, Brinell of 58.0 [-] | O | AA Standards | ||
58.0 [-] Show Material materials with Härte, Brinell of 58.0 [-] | O | 500 kg load, 10 mm ball | |||
Kompressionsmodul | 70.7 MPa Show Material materials with Kompressionsmodul of 70.7 MPa | O | |||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | |||
Poissonzahl | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | |||
Scherfestigkeit | 152.0 MPa Show Material materials with Scherfestigkeit of 152.0 MPa | O | |||
Schubmodule | 25.9 GPa Show Material materials with Schubmodule of 25.9 GPa | O | |||
Streckgrenze | -196 °C | 130 MPa Show Material materials with Streckgrenze of 130 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
-80 °C | 115 MPa Show Material materials with Streckgrenze of 115 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
-28 °C | 115 MPa Show Material materials with Streckgrenze of 115 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
75.0 MPa Show Material materials with Streckgrenze of 75.0 MPa | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B313, ASTM B547 | RP02 | ||
94.0 MPa Show Material materials with Streckgrenze of 94.0 MPa | O | ||||
115.0 MPa Show Material materials with Streckgrenze of 115.0 MPa | O | AA Standards | RP02 | ||
24 °C | 115 MPa Show Material materials with Streckgrenze of 115 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
100 °C | 115 MPa Show Material materials with Streckgrenze of 115 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
149 °C | 110 MPa Show Material materials with Streckgrenze of 110 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
204 °C | 105 MPa Show Material materials with Streckgrenze of 105 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
260 °C | 75 MPa Show Material materials with Streckgrenze of 75 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
316 °C | 50 MPa Show Material materials with Streckgrenze of 50 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
317 °C | 29 MPa Show Material materials with Streckgrenze of 29 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
Zugfestigkeit | -195 °C | 360 MPa Show Material materials with Zugfestigkeit of 360 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
-80 °C | 248 MPa Show Material materials with Zugfestigkeit of 248 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
205.0 - 285.0 MPa Show Material materials with Zugfestigkeit of 205.0 - 285.0 MPa | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B313, ASTM B547 | |||
240.0 MPa Show Material materials with Zugfestigkeit of 240.0 MPa | O | AA Standards | |||
0 °C | 240 MPa Show Material materials with Zugfestigkeit of 240 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
24 °C | 240 MPa Show Material materials with Zugfestigkeit of 240 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
100 °C | 240 MPa Show Material materials with Zugfestigkeit of 240 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
150 °C | 200 MPa Show Material materials with Zugfestigkeit of 200 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
205 °C | 152 MPa Show Material materials with Zugfestigkeit of 152 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
260 °C | 117 MPa Show Material materials with Zugfestigkeit of 117 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
315 °C | 75 MPa Show Material materials with Zugfestigkeit of 75 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
370 °C | 40 MPa Show Material materials with Zugfestigkeit of 40 MPa | O | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture |
Thermisch
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 2.4e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.4e-05 1/K | O | |||
20 °C | 2.3899999999999998e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.3899999999999998e-05 1/K | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B313, ASTM B547 | ||
100 °C | 2.3899999999999998e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.3899999999999998e-05 1/K | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B313, ASTM B547 | ||
Max. Betriebstemperatur | 150.0 °C Show Material materials with Max. Betriebstemperatur of 150.0 °C | Typical for Wrought 5000 Series Aluminium | |||
Schmelzpunkt | 590.0 - 645.0 °C Show Material materials with Schmelzpunkt of 590.0 - 645.0 °C | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B313, ASTM B547 | ||
590.0 °C Show Material materials with Schmelzpunkt of 590.0 °C | O | ||||
Spezifische Wärmekapazität | 900.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 900.0 J/(kg·K) | O | |||
Wärmeleitfähigkeit | 126 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 126 W/(m·K) | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B313, ASTM B547 | ||
130.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 130.0 W/(m·K) | O |
Elektrisch
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Elektrische Leitfähigkeit | 19000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 19000000.0 S/m | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B313, ASTM B547 |
spezifischer Widerstand | 5.26e-08 Ω·m Show Material materials with spezifischer Widerstand of 5.26e-08 Ω·m | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B313, ASTM B547 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 94.4 - 96.8 % Show Material materials with Aluminium of 94.4 - 96.8 % | O | |
Andere | 0.15 % Show Material materials with Andere of 0.15 % | O | |
Chrom | 0.15 - 0.35 % Show Material materials with Chrom of 0.15 - 0.35 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B313, ASTM B547 |
Eisen | 0.40 % Show Material materials with Eisen of 0.40 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B313, ASTM B547 |
0.4 % Show Material materials with Eisen of 0.4 % | O | ||
Kupfer | 0.1 % Show Material materials with Kupfer of 0.1 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B313, ASTM B547 |
Magnesium | 3.1 - 3.9 % Show Material materials with Magnesium of 3.1 - 3.9 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B313, ASTM B547 |
Mangan | 0.1 % Show Material materials with Mangan of 0.1 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B313, ASTM B547 |
Silizium | 0.25 % Show Material materials with Silizium of 0.25 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B313, ASTM B547 |
Titan | 0.2 % Show Material materials with Titan of 0.2 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B313, ASTM B547 |
Zink | 0.2 % Show Material materials with Zink of 0.2 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B313, ASTM B547 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (O, H32), sufficient (H34, H36, H38) | |
| Workability | general (condition): good (O), acceptable (H32, H34), poor(H36, H38) | |