Eigenschaften
Allgemein
| Property | Value | Condition |
|---|---|---|
Dichte | 2.69 g/cm³ Show Material materials with Dichte of 2.69 g/cm³ | H34 |
2.7 g/cm³ Show Material materials with Dichte of 2.7 g/cm³ | H34 |
Mechanisch
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Dehnung | -195 °C | 30 % Show Material materials with Dehnung of 30 % | H34 | Elongation in 50 mm | |
-80 °C | 21 % Show Material materials with Dehnung of 21 % | H34 | Elongation in 50 mm | ||
4.0 % Show Material materials with Dehnung of 4.0 % | H34 | AA Standards, ASTM B209 | A50 | ||
4.0 % Show Material materials with Dehnung of 4.0 % | H34 | AA Standards, ASTM B234 | A100 | ||
5.0 % Show Material materials with Dehnung of 5.0 % | H34 | AA Standards, ASTM B209 | A50 | ||
6.0 % Show Material materials with Dehnung of 6.0 % | H34 | AA Standards, ASTM B209, ASTM B547 | A50 | ||
6.0 % Show Material materials with Dehnung of 6.0 % | H34 | AA Standards, ASTM B234 | A100 | ||
7.3 % Show Material materials with Dehnung of 7.3 % | H34 | ||||
9.0 % Show Material materials with Dehnung of 9.0 % | H34 | AA Standards, ASTM B209 | A100 | ||
10.0 % Show Material materials with Dehnung of 10.0 % | H34 | AA Standards, ASTM B209, ASTM B547 | A50 | ||
0 °C | 18 % Show Material materials with Dehnung of 18 % | H34 | Elongation in 50 mm | ||
24 °C | 16 % Show Material materials with Dehnung of 16 % | H34 | Elongation in 50 mm | ||
100 °C | 18 % Show Material materials with Dehnung of 18 % | H34 | Elongation in 50 mm | ||
150 °C | 32 % Show Material materials with Dehnung of 32 % | H34 | Elongation in 50 mm | ||
205 °C | 45 % Show Material materials with Dehnung of 45 % | H34 | Elongation in 50 mm | ||
260 °C | 80 % Show Material materials with Dehnung of 80 % | H34 | Elongation in 50 mm | ||
315 °C | 110 % Show Material materials with Dehnung of 110 % | H34 | Elongation in 50 mm | ||
370 °C | 130 % Show Material materials with Dehnung of 130 % | H34 | Elongation in 50 mm | ||
Elastizitätsmodul | 70 GPa Show Material materials with Elastizitätsmodul of 70 GPa | H34 | |||
71.0 GPa Show Material materials with Elastizitätsmodul of 71.0 GPa | H34 | ||||
Härte, Brinell | 81.0 [-] Show Material materials with Härte, Brinell of 81.0 [-] | H34 | AA Standards | ||
81.0 [-] Show Material materials with Härte, Brinell of 81.0 [-] | H34 | 500 kg load, 10 mm ball | |||
Kompressionsmodul | 71.0 MPa Show Material materials with Kompressionsmodul of 71.0 MPa | H34 | |||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | |||
Poissonzahl | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | |||
Scherfestigkeit | 179.0 MPa Show Material materials with Scherfestigkeit of 179.0 MPa | H34 | |||
Schubmodule | 26.0 - 26.5 GPa Show Material materials with Schubmodule of 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | |||
Streckgrenze | -196 °C | 285 MPa Show Material materials with Streckgrenze of 285 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
-80 °C | 250 MPa Show Material materials with Streckgrenze of 250 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
-28 °C | 240 MPa Show Material materials with Streckgrenze of 240 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
200.0 MPa Show Material materials with Streckgrenze of 200.0 MPa | H34 | AA Standards, ASTM B209, ASTM B234, ASTM B547 | RP02 | ||
240.0 MPa Show Material materials with Streckgrenze of 240.0 MPa | H34 | AA Standards | RP02 | ||
240.0 MPa Show Material materials with Streckgrenze of 240.0 MPa | H34 | ||||
24 °C | 240 MPa Show Material materials with Streckgrenze of 240 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
100 °C | 235 MPa Show Material materials with Streckgrenze of 235 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
149 °C | 195 MPa Show Material materials with Streckgrenze of 195 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
204 °C | 130 MPa Show Material materials with Streckgrenze of 130 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
260 °C | 75 MPa Show Material materials with Streckgrenze of 75 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
316 °C | 50 MPa Show Material materials with Streckgrenze of 50 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
371 °C | 29 MPa Show Material materials with Streckgrenze of 29 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
Zugfestigkeit | -195 °C | 435 MPa Show Material materials with Zugfestigkeit of 435 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
-80 °C | 317 MPa Show Material materials with Zugfestigkeit of 317 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
270.0 - 325.0 MPa Show Material materials with Zugfestigkeit of 270.0 - 325.0 MPa | H34 | AA Standards, ASTM B209, ASTM B547 | |||
270.0 MPa Show Material materials with Zugfestigkeit of 270.0 MPa | H34 | AA Standards, ASTM B234 | |||
300.0 MPa Show Material materials with Zugfestigkeit of 300.0 MPa | H34 | ||||
0 °C | 303 MPa Show Material materials with Zugfestigkeit of 303 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
305.0 MPa Show Material materials with Zugfestigkeit of 305.0 MPa | H34 | AA Standards | |||
24 °C | 303 MPa Show Material materials with Zugfestigkeit of 303 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
100 °C | 295 MPa Show Material materials with Zugfestigkeit of 295 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
150 °C | 235 MPa Show Material materials with Zugfestigkeit of 235 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
205 °C | 180 MPa Show Material materials with Zugfestigkeit of 180 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
260 °C | 117 MPa Show Material materials with Zugfestigkeit of 117 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
315 °C | 74 MPa Show Material materials with Zugfestigkeit of 74 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
370 °C | 40 MPa Show Material materials with Zugfestigkeit of 40 MPa | H34 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture |
Thermisch
| Property | Value | Condition | Comment |
|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 2.4e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.4e-05 1/K | H34 | |
Max. Betriebstemperatur | 150.0 °C Show Material materials with Max. Betriebstemperatur of 150.0 °C | Typical for Wrought 5000 Series Aluminium | |
Schmelzpunkt | 600.0 °C Show Material materials with Schmelzpunkt of 600.0 °C | H34 | |
Spezifische Wärmekapazität | 900.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 900.0 J/(kg·K) | H34 | |
Wärmeleitfähigkeit | 130.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 130.0 W/(m·K) | H34 |
Elektrisch
| Property | Value | Comment |
|---|---|---|
Elektrische Leitfähigkeit | 18000000.0 - 31000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 18000000.0 - 31000000.0 S/m | Typical for Wrought 5000 Series Aluminium |
spezifischer Widerstand | 3.3e-08 - 5e-08 Ω·m Show Material materials with spezifischer Widerstand of 3.3e-08 - 5e-08 Ω·m | Typical for Wrought 5000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 94.5 - 97.1 % Show Material materials with Aluminium of 94.5 - 97.1 % | H34 | |
Andere | 0.15 % Show Material materials with Andere of 0.15 % | H34 | |
Chrom | 0.05 - 0.2 % Show Material materials with Chrom of 0.05 - 0.2 % | H34 | AA Standards, ASTM B209, ASTM B234, ASTM B547 |
Eisen | 0.40 % Show Material materials with Eisen of 0.40 % | H34 | AA Standards, ASTM B209, ASTM B234, ASTM B547 |
0.4 % Show Material materials with Eisen of 0.4 % | H34 | ||
Kupfer | 0.1 % Show Material materials with Kupfer of 0.1 % | H34 | AA Standards, ASTM B209, ASTM B234, ASTM B547 |
Magnesium | 2.4 - 3.0 % Show Material materials with Magnesium of 2.4 - 3.0 % | H34 | AA Standards, ASTM B209, ASTM B234, ASTM B547 |
Mangan | 0.5 - 1.0 % Show Material materials with Mangan of 0.5 - 1.0 % | H34 | AA Standards, ASTM B209, ASTM B234, ASTM B547 |
Silizium | 0.25 % Show Material materials with Silizium of 0.25 % | H34 | AA Standards, ASTM B209, ASTM B234, ASTM B547 |
Titan | 0.2 % Show Material materials with Titan of 0.2 % | H34 | AA Standards, ASTM B209, ASTM B234, ASTM B547 |
Zink | 0.25 % Show Material materials with Zink of 0.25 % | H34 | AA Standards, ASTM B209, ASTM B234, ASTM B547 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (O, H32, H111), sufficient (H34) | |
| Workability | general (condition): good (O), acceptable (H32, H34, H111) | |