Eigenschaften
Allgemein
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Dichte | 2.7 g/cm³ Show Material materials with Dichte of 2.7 g/cm³ | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B247, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547, BS EN 573-3, BS EN 755-2 | Extrusion |
2.7 g/cm³ Show Material materials with Dichte of 2.7 g/cm³ | T6 |
Mechanisch
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Bending Fatigue Strength | 95.0 MPa Show Material materials with Bending Fatigue Strength of 95.0 MPa | T6 | AA Standards | |||
Dehnung | -195 °C | 22 % Show Material materials with Dehnung of 22 % | T6 | Elongation in 50 mm | ||
-80 °C | 18 % Show Material materials with Dehnung of 18 % | T6 | Elongation in 50 mm | |||
4.0 % Show Material materials with Dehnung of 4.0 % | T6 | AA Standards, ASTM B209 | A50 | |||
4.0 % Show Material materials with Dehnung of 4.0 % | T6 | AA Standards, ASTM B247 | A100 | |||
5.0 % Show Material materials with Dehnung of 5.0 % | T6 | AA Standards, ASTM B247 | A50 | |||
5.0 % Show Material materials with Dehnung of 5.0 % | T6 | AA Standards, ASTM B247 | A100 | |||
6.0 % Show Material materials with Dehnung of 6.0 % | T6 | AA Standards, ASTM B209 | A50 | |||
6.0 % Show Material materials with Dehnung of 6.0 % | T6 | AA Standards, ASTM B247 | A100 | |||
7.0 % Show Material materials with Dehnung of 7.0 % | T6 | AA Standards, ASTM B247 | A50 | |||
7.0 % Show Material materials with Dehnung of 7.0 % | T6 | AA Standards, ASTM B247 | A100 | |||
8.0 % Show Material materials with Dehnung of 8.0 % | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B247, ASTM B345, ASTM B483 | A50 | |||
8.0 % Show Material materials with Dehnung of 8.0 % | T6 | AA Standards, ASTM B234 | A100 | |||
9.0 % Show Material materials with Dehnung of 9.0 % | T6 | AA Standards, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B316, ASTM B345 | A100 | |||
9.4 % Show Material materials with Dehnung of 9.4 % | T6 | |||||
10.0 % Show Material materials with Dehnung of 10.0 % | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B247, ASTM B313, ASTM B345, ASTM B483, ASTM B547 | A50 | |||
10.0 % Show Material materials with Dehnung of 10.0 % | T6 | AA Standards, ASTM B210, ASTM B234, ASTM B483 | A100 | |||
12.0 % Show Material materials with Dehnung of 12.0 % | T6 | AA Standards, ASTM B210, ASTM B234, ASTM B241, ASTM B483 | A50 | |||
15.0 % Show Material materials with Dehnung of 15.0 % | T6 | AA Standards | A100 | |||
0 °C | 17 % Show Material materials with Dehnung of 17 % | T6 | Elongation in 50 mm | |||
24 °C | 17 % Show Material materials with Dehnung of 17 % | T6 | Elongation in 50 mm | |||
100 °C | 18 % Show Material materials with Dehnung of 18 % | T6 | Elongation in 50 mm | |||
150 °C | 20 % Show Material materials with Dehnung of 20 % | T6 | Elongation in 50 mm | |||
205 °C | 28 % Show Material materials with Dehnung of 28 % | T6 | Elongation in 50 mm | |||
260 °C | 60 % Show Material materials with Dehnung of 60 % | T6 | Elongation in 50 mm | |||
315 °C | 85 % Show Material materials with Dehnung of 85 % | T6 | Elongation in 50 mm | |||
370 °C | 95 % Show Material materials with Dehnung of 95 % | T6 | Elongation in 50 mm | |||
Elastizitätsmodul | 69.0 GPa Show Material materials with Elastizitätsmodul of 69.0 GPa | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B247, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547 | |||
70.0 GPa Show Material materials with Elastizitätsmodul of 70.0 GPa | T6 | BS EN 573-3, BS EN 755-2 | Extrusion | |||
Härte, Brinell | 95.0 [-] Show Material materials with Härte, Brinell of 95.0 [-] | T6 | AA Standards, BS EN 573-3, BS EN 755-2 | Extrusion | ||
95.0 [-] Show Material materials with Härte, Brinell of 95.0 [-] | T6 | 500 kg load, 10 mm ball | ||||
Kompressionsmodul | 69.7 MPa Show Material materials with Kompressionsmodul of 69.7 MPa | T6 | ||||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 6000 Series Aluminium | ||||
Poissonzahl | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | Typical for Wrought 6000 Series Aluminium | ||||
Scherfestigkeit | 207.0 MPa Show Material materials with Scherfestigkeit of 207.0 MPa | T6 | ||||
Schubmodule | 26.0 - 26.5 GPa Show Material materials with Schubmodule of 26.0 - 26.5 GPa | Typical for Wrought 6000 Series Aluminium | ||||
Streckgrenze | -196 °C | 324 MPa Show Material materials with Streckgrenze of 324 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
-80 °C | 290 MPa Show Material materials with Streckgrenze of 290 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
-28 °C | 283 MPa Show Material materials with Streckgrenze of 283 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
230.0 MPa Show Material materials with Streckgrenze of 230.0 MPa | T6 | AA Standards, ASTM B247 | RP02 | |||
235.0 MPa Show Material materials with Streckgrenze of 235.0 MPa | T6 | AA Standards, ASTM B247 | RP02 | |||
240.0 MPa Show Material materials with Streckgrenze of 240.0 MPa | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B247, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547, BS EN 573-3, BS EN 755-2 | Extrusion | RP02 | ||
270.0 MPa Show Material materials with Streckgrenze of 270.0 MPa | T6 | |||||
275.0 MPa Show Material materials with Streckgrenze of 275.0 MPa | T6 | AA Standards | RP02 | |||
24 °C | 276 MPa Show Material materials with Streckgrenze of 276 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
100 °C | 262 MPa Show Material materials with Streckgrenze of 262 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
149 °C | 214 MPa Show Material materials with Streckgrenze of 214 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
204 °C | 103 MPa Show Material materials with Streckgrenze of 103 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
260 °C | 34 MPa Show Material materials with Streckgrenze of 34 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
316 °C | 19 MPa Show Material materials with Streckgrenze of 19 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
371 °C | 12 MPa Show Material materials with Streckgrenze of 12 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
Zugfestigkeit | -195 °C | 415 MPa Show Material materials with Zugfestigkeit of 415 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
-80 °C | 338 MPa Show Material materials with Zugfestigkeit of 338 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
255.0 MPa Show Material materials with Zugfestigkeit of 255.0 MPa | T6 | AA Standards, ASTM B247 | ||||
260.0 MPa Show Material materials with Zugfestigkeit of 260.0 MPa | T6 | AA Standards, ASTM B221, ASTM B241, ASTM B247, ASTM B345, BS EN 573-3, BS EN 755-2 | Extrusion | |||
290.0 MPa Show Material materials with Zugfestigkeit of 290.0 MPa | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | ||||
310.0 MPa Show Material materials with Zugfestigkeit of 310.0 MPa | T6 | AA Standards | ||||
0 °C | 325 MPa Show Material materials with Zugfestigkeit of 325 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
24 °C | 310 MPa Show Material materials with Zugfestigkeit of 310 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
100 °C | 290 MPa Show Material materials with Zugfestigkeit of 290 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
150 °C | 235 MPa Show Material materials with Zugfestigkeit of 235 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
205 °C | 130 MPa Show Material materials with Zugfestigkeit of 130 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
260 °C | 52 MPa Show Material materials with Zugfestigkeit of 52 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
315 °C | 32 MPa Show Material materials with Zugfestigkeit of 32 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
370 °C | 21 MPa Show Material materials with Zugfestigkeit of 21 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture |
Thermisch
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 2.4e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.4e-05 1/K | T6 | ||||
20 °C | 2.36e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.36e-05 1/K | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B247, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547 | |||
100 °C | 2.36e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.36e-05 1/K | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B247, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547 | |||
200 °C | 0.0000243 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 0.0000243 1/K | T6 | derived value between 20°C and the mentioned temperature | |||
300 °C | 0.0000254 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 0.0000254 1/K | T6 | derived value between 20°C and the mentioned temperature | |||
Schmelzpunkt | 580.0 - 650.0 °C Show Material materials with Schmelzpunkt of 580.0 - 650.0 °C | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B247, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547 | |||
580.0 °C Show Material materials with Schmelzpunkt of 580.0 °C | T6 | |||||
650.0 °C Show Material materials with Schmelzpunkt of 650.0 °C | T6 | BS EN 573-3, BS EN 755-2 | Extrusion | |||
Spezifische Wärmekapazität | 900.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 900.0 J/(kg·K) | T6 | ||||
100 °C | 960 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 960 J/(kg·K) | T6 | derived value for 23-100°C | |||
Wärmeleitfähigkeit | 155.0 - 180.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 155.0 - 180.0 W/(m·K) | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B247, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547 | |||
166.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 166.0 W/(m·K) | T6 | BS EN 573-3, BS EN 755-2 | Extrusion | |||
170.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 170.0 W/(m·K) | T6 | |||||
23 °C | 167.4 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 167.4 W/(m·K) | T6 | derived value | |||
25 °C | 154.9 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 154.9 W/(m·K) | T6 | derived value |
Elektrisch
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Elektrische Leitfähigkeit | 23000000.0 - 27000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 23000000.0 - 27000000.0 S/m | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B247, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547 | ||
25000000 S/m Show Material materials with Elektrische Leitfähigkeit of 25000000 S/m | T6 | Typical/derived value | |||
Specific Electrical conductivity | 43.0 % IACS Show Material materials with Specific Electrical conductivity of 43.0 % IACS | T6 | Typical value | ||
spezifischer Widerstand | 3.7e-08 - 4.35e-08 Ω·m Show Material materials with spezifischer Widerstand of 3.7e-08 - 4.35e-08 Ω·m | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B247, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547 | ||
4e-08 Ω·m Show Material materials with spezifischer Widerstand of 4e-08 Ω·m | T6 | Typical value | |||
4e-08 Ω·m Show Material materials with spezifischer Widerstand of 4e-08 Ω·m | T6 | BS EN 573-3, BS EN 755-2 | Extrusion |
Chemical properties
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Aluminium | 95.9 - 98.6 % Show Material materials with Aluminium of 95.9 - 98.6 % | T6 | |||
Andere | 0.05 % Show Material materials with Andere of 0.05 % | T6 | BS EN 573-3, BS EN 755-2 | Extrusion | Total |
0.15 % Show Material materials with Andere of 0.15 % | T6 | ||||
Chrom | 0.04 - 0.35 % Show Material materials with Chrom of 0.04 - 0.35 % | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B247, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547, BS EN 573-3, BS EN 755-2 | Extrusion | |
Eisen | 0.70 % Show Material materials with Eisen of 0.70 % | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B247, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547 | ||
0.7 % Show Material materials with Eisen of 0.7 % | T6 | BS EN 573-3, BS EN 755-2 | Extrusion | ||
Kupfer | 0.15 - 0.4 % Show Material materials with Kupfer of 0.15 - 0.4 % | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B247, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547, BS EN 573-3, BS EN 755-2 | Extrusion | |
Magnesium | 0.8 - 1.2 % Show Material materials with Magnesium of 0.8 - 1.2 % | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B247, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547, BS EN 573-3, BS EN 755-2 | Extrusion | |
Mangan | 0.15 % Show Material materials with Mangan of 0.15 % | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B247, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547, BS EN 573-3, BS EN 755-2 | Extrusion | |
Silizium | 0.4 - 0.8 % Show Material materials with Silizium of 0.4 - 0.8 % | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B247, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547, BS EN 573-3, BS EN 755-2 | Extrusion | |
Titan | 0.15 % Show Material materials with Titan of 0.15 % | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B247, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547, BS EN 573-3, BS EN 755-2 | Extrusion | |
Zink | 0.25 % Show Material materials with Zink of 0.25 % | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B247, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547, BS EN 573-3, BS EN 755-2 | Extrusion |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Heavy duty structures (Rail coaches, Truck frames, Ship building, Bridges and Military bridges, Aerospace applications including helicopter rotor), Skins (Tube, Pylons and Towers, Transport, Boilermaking, Motorboats, Rivets). | |
| Brazing | general: possible with commercial processes and methods | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests (O, T6, T651, T652, T6510, T6511), no damage during operation, limited damage during laboratory tests (T4, T451, T4510, T4511), general: good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (O), sufficient (T4, T451, T4510, T4511, T6, T651, T652, T6510, T6511) | |
| Soldering general | Good | |
| Welding | Gas: Good; Arc: Very Good; Resistance: Good | |
| Workability | general (condition): good (O), acceptable (T4, T451, T4510, T4511), poor(T6, T651, T652, T6510, T6511) | |