Eigenschaften
Allgemein
Mechanisch
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Bending Fatigue Strength | 95.0 MPa Show Material materials with Bending Fatigue Strength of 95.0 MPa | T651 | AA Standards | ||
Dehnung | -195 °C | 22 % Show Material materials with Dehnung of 22 % | T651 | Elongation in 50 mm | |
-80 °C | 18 % Show Material materials with Dehnung of 18 % | T651 | Elongation in 50 mm | ||
5.0 % Show Material materials with Dehnung of 5.0 % | T651 | AA Standards, ASTM B209 | A100 | ||
7.0 % Show Material materials with Dehnung of 7.0 % | T651 | AA Standards, ASTM B209 | A100 | ||
8.0 % Show Material materials with Dehnung of 8.0 % | T651 | AA Standards, ASTM B209 | A100 | ||
9.0 % Show Material materials with Dehnung of 9.0 % | T651 | AA Standards, ASTM B211 | A100 | ||
10.0 % Show Material materials with Dehnung of 10.0 % | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 | A50 | ||
11.0 % Show Material materials with Dehnung of 11.0 % | T651 | ||||
12.0 % Show Material materials with Dehnung of 12.0 % | T651 | AA Standards | A50 | ||
15.0 % Show Material materials with Dehnung of 15.0 % | T651 | AA Standards | A100 | ||
0 °C | 17 % Show Material materials with Dehnung of 17 % | T651 | Elongation in 50 mm | ||
24 °C | 17 % Show Material materials with Dehnung of 17 % | T651 | Elongation in 50 mm | ||
100 °C | 18 % Show Material materials with Dehnung of 18 % | T651 | Elongation in 50 mm | ||
150 °C | 20 % Show Material materials with Dehnung of 20 % | T651 | Elongation in 50 mm | ||
205 °C | 28 % Show Material materials with Dehnung of 28 % | T651 | Elongation in 50 mm | ||
260 °C | 60 % Show Material materials with Dehnung of 60 % | T651 | Elongation in 50 mm | ||
315 °C | 85 % Show Material materials with Dehnung of 85 % | T651 | Elongation in 50 mm | ||
370 °C | 95 % Show Material materials with Dehnung of 95 % | T651 | Elongation in 50 mm | ||
Elastizitätsmodul | 69.0 GPa Show Material materials with Elastizitätsmodul of 69.0 GPa | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 | ||
Härte, Brinell | 95.0 [-] Show Material materials with Härte, Brinell of 95.0 [-] | T651 | AA Standards | ||
95.0 [-] Show Material materials with Härte, Brinell of 95.0 [-] | T651 | 500 kg load, 10 mm ball | |||
Kompressionsmodul | 69.7 MPa Show Material materials with Kompressionsmodul of 69.7 MPa | T651 | |||
Plane-Strain Fracture Toughnes | -196 °C | 41.6 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 41.6 MPa·√m | T651 | For plate in T-L direction | |
24 °C | 29.1 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 29.1 MPa·√m | T651 | For plate in T-L direction | ||
Poissonzahl | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | Typical for Wrought 6000 Series Aluminium | |||
Scherfestigkeit | 207.0 MPa Show Material materials with Scherfestigkeit of 207.0 MPa | T651 | |||
Schubmodule | 26.0 - 26.5 GPa Show Material materials with Schubmodule of 26.0 - 26.5 GPa | Typical for Wrought 6000 Series Aluminium | |||
Streckgrenze | -196 °C | 324 MPa Show Material materials with Streckgrenze of 324 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
-80 °C | 290 MPa Show Material materials with Streckgrenze of 290 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
-28 °C | 283 MPa Show Material materials with Streckgrenze of 283 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
240.0 MPa Show Material materials with Streckgrenze of 240.0 MPa | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 | RP02 | ||
270.0 MPa Show Material materials with Streckgrenze of 270.0 MPa | T651 | ||||
275.0 MPa Show Material materials with Streckgrenze of 275.0 MPa | T651 | AA Standards | RP02 | ||
24 °C | 276 MPa Show Material materials with Streckgrenze of 276 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
100 °C | 262 MPa Show Material materials with Streckgrenze of 262 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
149 °C | 214 MPa Show Material materials with Streckgrenze of 214 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
204 °C | 103 MPa Show Material materials with Streckgrenze of 103 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
260 °C | 34 MPa Show Material materials with Streckgrenze of 34 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
316 °C | 19 MPa Show Material materials with Streckgrenze of 19 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
371 °C | 12 MPa Show Material materials with Streckgrenze of 12 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
Zugfestigkeit | -195 °C | 415 MPa Show Material materials with Zugfestigkeit of 415 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
-80 °C | 338 MPa Show Material materials with Zugfestigkeit of 338 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
275.0 MPa Show Material materials with Zugfestigkeit of 275.0 MPa | T651 | AA Standards, ASTM B209 | |||
290.0 MPa Show Material materials with Zugfestigkeit of 290.0 MPa | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 | |||
310.0 MPa Show Material materials with Zugfestigkeit of 310.0 MPa | T651 | AA Standards | |||
320.0 MPa Show Material materials with Zugfestigkeit of 320.0 MPa | T651 | ||||
0 °C | 325 MPa Show Material materials with Zugfestigkeit of 325 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
24 °C | 310 MPa Show Material materials with Zugfestigkeit of 310 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
100 °C | 290 MPa Show Material materials with Zugfestigkeit of 290 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
150 °C | 235 MPa Show Material materials with Zugfestigkeit of 235 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
205 °C | 130 MPa Show Material materials with Zugfestigkeit of 130 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
260 °C | 52 MPa Show Material materials with Zugfestigkeit of 52 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
315 °C | 32 MPa Show Material materials with Zugfestigkeit of 32 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
370 °C | 21 MPa Show Material materials with Zugfestigkeit of 21 MPa | T651 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture |
Thermisch
| Property | Temperature | Value | Condition | Related Standards |
|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 2.4e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.4e-05 1/K | T651 | ||
20 °C | 2.36e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.36e-05 1/K | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 | |
100 °C | 2.36e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.36e-05 1/K | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 | |
Schmelzpunkt | 580.0 - 650.0 °C Show Material materials with Schmelzpunkt of 580.0 - 650.0 °C | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 | |
580.0 °C Show Material materials with Schmelzpunkt of 580.0 °C | T651 | |||
Spezifische Wärmekapazität | 900.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 900.0 J/(kg·K) | T651 | ||
Wärmeleitfähigkeit | 155.0 - 180.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 155.0 - 180.0 W/(m·K) | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 | |
170.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 170.0 W/(m·K) | T651 |
Elektrisch
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Elektrische Leitfähigkeit | 23000000.0 - 27000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 23000000.0 - 27000000.0 S/m | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 |
spezifischer Widerstand | 3.7e-08 - 4.35e-08 Ω·m Show Material materials with spezifischer Widerstand of 3.7e-08 - 4.35e-08 Ω·m | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 95.9 - 98.6 % Show Material materials with Aluminium of 95.9 - 98.6 % | T651 | |
Andere | 0.15 % Show Material materials with Andere of 0.15 % | T651 | |
Chrom | 0.04 - 0.35 % Show Material materials with Chrom of 0.04 - 0.35 % | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 |
Eisen | 0.70 % Show Material materials with Eisen of 0.70 % | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 |
0.7 % Show Material materials with Eisen of 0.7 % | T651 | ||
Kupfer | 0.15 - 0.4 % Show Material materials with Kupfer of 0.15 - 0.4 % | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 |
Magnesium | 0.8 - 1.2 % Show Material materials with Magnesium of 0.8 - 1.2 % | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 |
Mangan | 0.15 % Show Material materials with Mangan of 0.15 % | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 |
Silizium | 0.4 - 0.8 % Show Material materials with Silizium of 0.4 - 0.8 % | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 |
Titan | 0.15 % Show Material materials with Titan of 0.15 % | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 |
Zink | 0.25 % Show Material materials with Zink of 0.25 % | T651 | AA Standards, ASTM B209, ASTM B211, ASTM B547 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: possible with commercial processes and methods | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests (O, T6, T651, T652, T6510, T6511), no damage during operation, limited damage during laboratory tests (T4, T451, T4510, T4511), general: good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (O), sufficient (T4, T451, T4510, T4511, T6, T651, T652, T6510, T6511) | |
| Workability | general (condition): good (O), acceptable (T4, T451, T4510, T4511), poor(T6, T651, T652, T6510, T6511) | |