Eigenschaften
Allgemein
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Dichte | 2.7 g/cm³ Show Material materials with Dichte of 2.7 g/cm³ | T94 | AA Standards, ASTM B211 |
Mechanisch
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Dehnung | 14.0 % Show Material materials with Dehnung of 14.0 % | T94 | ||
Elastizitätsmodul | 69.0 GPa Show Material materials with Elastizitätsmodul of 69.0 GPa | T94 | AA Standards, ASTM B211 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 6000 Series Aluminium | ||
Poissonzahl | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | Typical for Wrought 6000 Series Aluminium | ||
Schubmodule | 26.0 - 26.5 GPa Show Material materials with Schubmodule of 26.0 - 26.5 GPa | Typical for Wrought 6000 Series Aluminium | ||
Streckgrenze | 325.0 MPa Show Material materials with Streckgrenze of 325.0 MPa | T94 | AA Standards, ASTM B211 | RP02 |
370.0 MPa Show Material materials with Streckgrenze of 370.0 MPa | T94 | |||
Zugfestigkeit | 370.0 MPa Show Material materials with Zugfestigkeit of 370.0 MPa | T94 | AA Standards, ASTM B211 | |
430.0 MPa Show Material materials with Zugfestigkeit of 430.0 MPa | T94 |
Thermisch
| Property | Temperature | Value | Condition | Related Standards |
|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 2.4e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.4e-05 1/K | T94 | ||
20 °C | 2.36e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.36e-05 1/K | T94 | AA Standards, ASTM B211 | |
100 °C | 2.36e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.36e-05 1/K | T94 | AA Standards, ASTM B211 | |
Schmelzpunkt | 580.0 - 650.0 °C Show Material materials with Schmelzpunkt of 580.0 - 650.0 °C | T94 | AA Standards, ASTM B211 | |
580.0 °C Show Material materials with Schmelzpunkt of 580.0 °C | T94 | |||
Spezifische Wärmekapazität | 900.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 900.0 J/(kg·K) | T94 | ||
Wärmeleitfähigkeit | 155.0 - 180.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 155.0 - 180.0 W/(m·K) | T94 | AA Standards, ASTM B211 | |
170.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 170.0 W/(m·K) | T94 |
Elektrisch
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Elektrische Leitfähigkeit | 23000000.0 - 27000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 23000000.0 - 27000000.0 S/m | T94 | AA Standards, ASTM B211 |
spezifischer Widerstand | 3.7e-08 - 4.35e-08 Ω·m Show Material materials with spezifischer Widerstand of 3.7e-08 - 4.35e-08 Ω·m | T94 | AA Standards, ASTM B211 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 95.9 - 98.6 % Show Material materials with Aluminium of 95.9 - 98.6 % | T94 | |
Andere | 0.15 % Show Material materials with Andere of 0.15 % | T94 | |
Chrom | 0.04 - 0.35 % Show Material materials with Chrom of 0.04 - 0.35 % | T94 | AA Standards, ASTM B211 |
Eisen | 0.70 % Show Material materials with Eisen of 0.70 % | T94 | AA Standards, ASTM B211 |
0.7 % Show Material materials with Eisen of 0.7 % | T94 | ||
Kupfer | 0.15 - 0.4 % Show Material materials with Kupfer of 0.15 - 0.4 % | T94 | AA Standards, ASTM B211 |
Magnesium | 0.8 - 1.2 % Show Material materials with Magnesium of 0.8 - 1.2 % | T94 | AA Standards, ASTM B211 |
Mangan | 0.15 % Show Material materials with Mangan of 0.15 % | T94 | AA Standards, ASTM B211 |
Silizium | 0.4 - 0.8 % Show Material materials with Silizium of 0.4 - 0.8 % | T94 | AA Standards, ASTM B211 |
Titan | 0.15 % Show Material materials with Titan of 0.15 % | T94 | AA Standards, ASTM B211 |
Zink | 0.25 % Show Material materials with Zink of 0.25 % | T94 | AA Standards, ASTM B211 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: possible with commercial processes and methods | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests (O, T6, T651, T652, T6510, T6511), no damage during operation, limited damage during laboratory tests (T4, T451, T4510, T4511), general: good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (O), sufficient (T4, T451, T4510, T4511, T6, T651, T652, T6510, T6511) | |
| Workability | general (condition): good (O), acceptable (T4, T451, T4510, T4511), poor(T6, T651, T652, T6510, T6511) | |