Eigenschaften
Allgemein
Mechanisch
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Bending Fatigue Strength | 70.0 MPa Show Material materials with Bending Fatigue Strength of 70.0 MPa | T6 | AA Standards | ||
Dauerfestigkeit | 69 MPa Show Material materials with Dauerfestigkeit of 69 MPa | T6 | fo 5x10⁸ cycles | ||
Dehnung | -195 °C | 24 % Show Material materials with Dehnung of 24 % | T6 | Elongation in 50 mm | |
-80 °C | 20 % Show Material materials with Dehnung of 20 % | T6 | Elongation in 50 mm | ||
7.0 % Show Material materials with Dehnung of 7.0 % | T6 | AA Standards, ASTM B241, ASTM B345 | A100 | ||
8.0 % Show Material materials with Dehnung of 8.0 % | T6 | AA Standards, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B483 | A50 | ||
9.0 % Show Material materials with Dehnung of 9.0 % | T6 | AA Standards, ASTM B221, ASTM B241 | A100 | ||
10.0 % Show Material materials with Dehnung of 10.0 % | T6 | AA Standards, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B483 | A50 | ||
10.0 % Show Material materials with Dehnung of 10.0 % | T6 | AA Standards, ASTM B210, ASTM B483 | A100 | ||
11.0 % Show Material materials with Dehnung of 11.0 % | T6 | ||||
12.0 % Show Material materials with Dehnung of 12.0 % | T6 | AA Standards, ASTM B210, ASTM B483 | A50 | ||
0 °C | 19 % Show Material materials with Dehnung of 19 % | T6 | Elongation in 50 mm | ||
24 °C | 18 % Show Material materials with Dehnung of 18 % | T6 | Elongation in 50 mm | ||
100 °C | 15 % Show Material materials with Dehnung of 15 % | T6 | Elongation in 50 mm | ||
150 °C | 20 % Show Material materials with Dehnung of 20 % | T6 | Elongation in 50 mm | ||
205 °C | 40 % Show Material materials with Dehnung of 40 % | T6 | Elongation in 50 mm | ||
260 °C | 75 % Show Material materials with Dehnung of 75 % | T6 | Elongation in 50 mm | ||
315 °C | 80 % Show Material materials with Dehnung of 80 % | T6 | Elongation in 50 mm | ||
370 °C | 105 % Show Material materials with Dehnung of 105 % | T6 | Elongation in 50 mm | ||
Elastizitätsmodul | 69.0 GPa Show Material materials with Elastizitätsmodul of 69.0 GPa | T6 | AA Standards, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B483 | ||
69 GPa Show Material materials with Elastizitätsmodul of 69 GPa | T6 | ||||
Härte, Brinell | 73.0 [-] Show Material materials with Härte, Brinell of 73.0 [-] | T6 | AA Standards | ||
73.0 [-] Show Material materials with Härte, Brinell of 73.0 [-] | T6 | 500 kg load, 10 mm ball | |||
Kompressionsmodul | 69.7 MPa Show Material materials with Kompressionsmodul of 69.7 MPa | T6 | |||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 6000 Series Aluminium | |||
Poissonzahl | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | Typical for Wrought 6000 Series Aluminium | |||
Scherfestigkeit | 152.0 MPa Show Material materials with Scherfestigkeit of 152.0 MPa | T6 | |||
Schubmodule | 26.0 - 26.5 GPa Show Material materials with Schubmodule of 26.0 - 26.5 GPa | Typical for Wrought 6000 Series Aluminium | |||
Streckgrenze | -196 °C | 248 MPa Show Material materials with Streckgrenze of 248 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
-80 °C | 228 MPa Show Material materials with Streckgrenze of 228 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
-28 °C | 221 MPa Show Material materials with Streckgrenze of 221 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
170.0 MPa Show Material materials with Streckgrenze of 170.0 MPa | T6 | AA Standards, ASTM B221, ASTM B241, ASTM B345 | RP02 | ||
195.0 MPa Show Material materials with Streckgrenze of 195.0 MPa | T6 | AA Standards, ASTM B210, ASTM B483 | RP02 | ||
210.0 MPa Show Material materials with Streckgrenze of 210.0 MPa | T6 | ||||
215.0 MPa Show Material materials with Streckgrenze of 215.0 MPa | T6 | AA Standards | RP02 | ||
24 °C | 214 MPa Show Material materials with Streckgrenze of 214 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
100 °C | 193 MPa Show Material materials with Streckgrenze of 193 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
149 °C | 133 MPa Show Material materials with Streckgrenze of 133 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
204 °C | 45 MPa Show Material materials with Streckgrenze of 45 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
260 °C | 24 MPa Show Material materials with Streckgrenze of 24 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
316 °C | 17 MPa Show Material materials with Streckgrenze of 17 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
371 °C | 14 MPa Show Material materials with Streckgrenze of 14 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
Zugfestigkeit | -195 °C | 325 MPa Show Material materials with Zugfestigkeit of 325 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
-80 °C | 262 MPa Show Material materials with Zugfestigkeit of 262 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
205.0 MPa Show Material materials with Zugfestigkeit of 205.0 MPa | T6 | AA Standards, ASTM B221, ASTM B241, ASTM B345 | |||
230.0 MPa Show Material materials with Zugfestigkeit of 230.0 MPa | T6 | AA Standards, ASTM B210, ASTM B483 | |||
240.0 MPa Show Material materials with Zugfestigkeit of 240.0 MPa | T6 | AA Standards | |||
0 °C | 248 MPa Show Material materials with Zugfestigkeit of 248 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
250.0 MPa Show Material materials with Zugfestigkeit of 250.0 MPa | T6 | ||||
24 °C | 240 MPa Show Material materials with Zugfestigkeit of 240 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
100 °C | 215 MPa Show Material materials with Zugfestigkeit of 215 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
150 °C | 145 MPa Show Material materials with Zugfestigkeit of 145 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
205 °C | 62 MPa Show Material materials with Zugfestigkeit of 62 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
260 °C | 31 MPa Show Material materials with Zugfestigkeit of 31 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
315 °C | 22 MPa Show Material materials with Zugfestigkeit of 22 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
370 °C | 16 MPa Show Material materials with Zugfestigkeit of 16 MPa | T6 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture |
Thermisch
| Property | Temperature | Value | Condition | Related Standards |
|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 2.3e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.3e-05 1/K | T6 | ||
20 °C | 2.3399999999999996e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.3399999999999996e-05 1/K | T6 | AA Standards, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B483 | |
100 °C | 2.3399999999999996e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.3399999999999996e-05 1/K | T6 | AA Standards, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B483 | |
Schmelzpunkt | 615.0 - 655.0 °C Show Material materials with Schmelzpunkt of 615.0 - 655.0 °C | T6 | AA Standards, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B483 | |
620.0 °C Show Material materials with Schmelzpunkt of 620.0 °C | T6 | |||
Spezifische Wärmekapazität | 900.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 900.0 J/(kg·K) | T6 | ||
Wärmeleitfähigkeit | 193.0 - 218.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 193.0 - 218.0 W/(m·K) | T6 | AA Standards, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B483 | |
200.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 200.0 W/(m·K) | T6 |
Elektrisch
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Elektrische Leitfähigkeit | 29000000.0 - 34000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 29000000.0 - 34000000.0 S/m | T6 | AA Standards, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B483 | |
31000000 S/m Show Material materials with Elektrische Leitfähigkeit of 31000000 S/m | T6 | Typical value | ||
Specific Electrical conductivity | 53.0 % IACS Show Material materials with Specific Electrical conductivity of 53.0 % IACS | T6 | Typical/Derived value | |
spezifischer Widerstand | 2.94e-08 - 3.45e-08 Ω·m Show Material materials with spezifischer Widerstand of 2.94e-08 - 3.45e-08 Ω·m | T6 | AA Standards, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B483 | |
3.3e-08 Ω·m Show Material materials with spezifischer Widerstand of 3.3e-08 Ω·m | T6 | Typical value |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 97.5 - 99.4 % Show Material materials with Aluminium of 97.5 - 99.4 % | T6 | |
Andere | 0.15 % Show Material materials with Andere of 0.15 % | T6 | |
Chrom | 0.1 % Show Material materials with Chrom of 0.1 % | T6 | AA Standards, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
Eisen | 0.35 % Show Material materials with Eisen of 0.35 % | T6 | AA Standards, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
0.35 % Show Material materials with Eisen of 0.35 % | T6 | ||
Kupfer | 0.1 % Show Material materials with Kupfer of 0.1 % | T6 | AA Standards, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
Magnesium | 0.45 - 0.9 % Show Material materials with Magnesium of 0.45 - 0.9 % | T6 | AA Standards, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
Mangan | 0.1 % Show Material materials with Mangan of 0.1 % | T6 | AA Standards, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
Silizium | 0.2 - 0.6 % Show Material materials with Silizium of 0.2 - 0.6 % | T6 | AA Standards, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
Titan | 0.1 % Show Material materials with Titan of 0.1 % | T6 | AA Standards, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
Zink | 0.1 % Show Material materials with Zink of 0.1 % | T6 | AA Standards, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: possible with commercial processes and methods | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: poor (T1, T4), sufficient (T5, T452, T6, T83, T831, T832) | |
| Workability | general (condition): acceptable (T1, T4, T5, T452), poor(T6, T83, T831, T832) | |