Eigenschaften
Allgemein
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Dichte | 2.78 g/cm³ Show Material materials with Dichte of 2.78 g/cm³ | T53 | AA Standards, ASTM B221 |
2.78 g/cm³ Show Material materials with Dichte of 2.78 g/cm³ | T53 | ||
2.9 g/cm³ Show Material materials with Dichte of 2.9 g/cm³ | T53 |
Mechanisch
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Dauerfestigkeit | 231 MPa Show Material materials with Dauerfestigkeit of 231 MPa | T53 | fo 5x10⁸ cycles | ||
Dehnung | -269 °C | 16 % Show Material materials with Dehnung of 16 % | T53 | Elongation in 50 mm | |
-196 °C | 16 % Show Material materials with Dehnung of 16 % | T53 | Elongation in 50 mm | ||
-80 °C | 13 % Show Material materials with Dehnung of 13 % | T53 | Elongation in 50 mm | ||
-28 °C | 14 % Show Material materials with Dehnung of 14 % | T53 | Elongation in 50 mm | ||
9.0 % Show Material materials with Dehnung of 9.0 % | T53 | AA Standards, ASTM B221 | A100 | ||
10.0 % Show Material materials with Dehnung of 10.0 % | T53 | AA Standards, ASTM B221 | A50 | ||
10.0 % Show Material materials with Dehnung of 10.0 % | T53 | ||||
24 °C | 15 % Show Material materials with Dehnung of 15 % | T53 | Elongation in 50 mm | ||
100 °C | 20 % Show Material materials with Dehnung of 20 % | T53 | Elongation in 50 mm | ||
149 °C | 35 % Show Material materials with Dehnung of 35 % | T53 | Elongation in 50 mm | ||
204 °C | 60 % Show Material materials with Dehnung of 60 % | T53 | Elongation in 50 mm | ||
Elastizitätsmodul | 71.0 GPa Show Material materials with Elastizitätsmodul of 71.0 GPa | T53 | |||
Kompressionsmodul | 72.4 MPa Show Material materials with Kompressionsmodul of 72.4 MPa | T53 | |||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 7000 Series Aluminium | |||
Poissonzahl | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | Typical for Wrought 7000 Series Aluminium | |||
Scherfestigkeit | 221.0 MPa Show Material materials with Scherfestigkeit of 221.0 MPa | T53 | |||
Schubmodule | 26.9 GPa Show Material materials with Schubmodule of 26.9 GPa | T53 | |||
Streckgrenze | -269 °C | 483 MPa Show Material materials with Streckgrenze of 483 MPa | T53 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
-196 °C | 421 MPa Show Material materials with Streckgrenze of 421 MPa | T53 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
-80 °C | 379 MPa Show Material materials with Streckgrenze of 379 MPa | T53 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
-28 °C | 359 MPa Show Material materials with Streckgrenze of 359 MPa | T53 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
305.0 MPa Show Material materials with Streckgrenze of 305.0 MPa | T53 | AA Standards, ASTM B221 | RP02 | ||
350.0 MPa Show Material materials with Streckgrenze of 350.0 MPa | T53 | ||||
24 °C | 345 MPa Show Material materials with Streckgrenze of 345 MPa | T53 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
100 °C | 283 MPa Show Material materials with Streckgrenze of 283 MPa | T53 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
149 °C | 145 MPa Show Material materials with Streckgrenze of 145 MPa | T53 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
204 °C | 83 MPa Show Material materials with Streckgrenze of 83 MPa | T53 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
Zugfestigkeit | -269 °C | 641 MPa Show Material materials with Zugfestigkeit of 641 MPa | T53 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
-196 °C | 538 MPa Show Material materials with Zugfestigkeit of 538 MPa | T53 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
-80 °C | 441 MPa Show Material materials with Zugfestigkeit of 441 MPa | T53 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
-28 °C | 421 MPa Show Material materials with Zugfestigkeit of 421 MPa | T53 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
345.0 MPa Show Material materials with Zugfestigkeit of 345.0 MPa | T53 | AA Standards, ASTM B221 | |||
400.0 MPa Show Material materials with Zugfestigkeit of 400.0 MPa | T53 | ||||
24 °C | 392 MPa Show Material materials with Zugfestigkeit of 392 MPa | T53 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
100 °C | 303 MPa Show Material materials with Zugfestigkeit of 303 MPa | T53 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
149 °C | 165 MPa Show Material materials with Zugfestigkeit of 165 MPa | T53 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
204 °C | 97 MPa Show Material materials with Zugfestigkeit of 97 MPa | T53 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture |
Thermisch
| Property | Value | Condition | Comment |
|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 2.3e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.3e-05 1/K | T53 | |
Schmelzpunkt | 610.0 °C Show Material materials with Schmelzpunkt of 610.0 °C | T53 | |
Spezifische Wärmekapazität | 880.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 880.0 J/(kg·K) | T53 | |
Wärmeleitfähigkeit | 121.0 - 170.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 121.0 - 170.0 W/(m·K) | Typical for Wrought 7000 Series Aluminium |
Elektrisch
| Property | Value | Condition | Comment |
|---|---|---|---|
Elektrische Leitfähigkeit | 22000000 S/m Show Material materials with Elektrische Leitfähigkeit of 22000000 S/m | T53 | Typical/derived value |
Specific Electrical conductivity | 38.0 % IACS Show Material materials with Specific Electrical conductivity of 38.0 % IACS | T53 | Typical value |
spezifischer Widerstand | 4.54e-08 Ω·m Show Material materials with spezifischer Widerstand of 4.54e-08 Ω·m | T53 | Typical value |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 91.0 - 94.7 % Show Material materials with Aluminium of 91.0 - 94.7 % | T53 | |
Andere | 0.15 % Show Material materials with Andere of 0.15 % | T53 | |
Chrom | 0.06 - 0.2 % Show Material materials with Chrom of 0.06 - 0.2 % | T53 | AA Standards, ASTM B221 |
Eisen | 0.40 % Show Material materials with Eisen of 0.40 % | T53 | AA Standards, ASTM B221 |
0.4 % Show Material materials with Eisen of 0.4 % | T53 | ||
Kupfer | 0.1 % Show Material materials with Kupfer of 0.1 % | T53 | AA Standards, ASTM B221 |
Magnesium | 1.0 - 1.8 % Show Material materials with Magnesium of 1.0 - 1.8 % | T53 | AA Standards, ASTM B221 |
Mangan | 0.2 - 0.7 % Show Material materials with Mangan of 0.2 - 0.7 % | T53 | AA Standards, ASTM B221 |
Silizium | 0.35 % Show Material materials with Silizium of 0.35 % | T53 | AA Standards, ASTM B221 |
Titan | 0.01 - 0.06 % Show Material materials with Titan of 0.01 - 0.06 % | T53 | AA Standards, ASTM B221 |
Zink | 4.0 - 5.0 % Show Material materials with Zink of 4.0 - 5.0 % | T53 | AA Standards, ASTM B221 |
Zirkonium | 0.08 - 0.2 % Show Material materials with Zirkonium of 0.08 - 0.2 % | T53 | AA Standards, ASTM B221 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen | |