Property | Value | Condition | Shape |
---|---|---|---|
Dichte | 2.8 g/cm³ Show Material materials with Dichte of 2.8 g/cm³ | T7351 | Sheet, Plate |
2.81 g/cm³ Show Material materials with Dichte of 2.81 g/cm³ | T7351 | ||
2.81 g/cm³ Show Material materials with Dichte of 2.81 g/cm³ | T7351 | Bar | |
3.1 g/cm³ Show Material materials with Dichte of 3.1 g/cm³ | T7351 | ||
Oberflächenrauigkeit | 0.4 Show Material materials with Oberflächenrauigkeit of 0.4 | T7351 | Sheet, Plate |
Abmessung
Mechanisch
Property | Temperature | Value | Condition | Shape | Related Standards | Comment |
---|---|---|---|---|---|---|
Dehnung | -195 °C | 14 % Show Material materials with Dehnung of 14 % | T7351 | Elongation in 50 mm | ||
-80 °C | 14 % Show Material materials with Dehnung of 14 % | T7351 | Elongation in 50 mm | |||
5.0 - 6.0 % Show Material materials with Dehnung of 5.0 - 6.0 % | T7351 | Sheet, Plate | ||||
5.0 % Show Material materials with Dehnung of 5.0 % | T7351 | AA Standards, ASTM B209 | A100 | |||
6.0 % Show Material materials with Dehnung of 6.0 % | T7351 | AA Standards, ASTM B209 | A100 | |||
7.0 % Show Material materials with Dehnung of 7.0 % | T7351 | AA Standards, ASTM B211 | A100 | |||
7.0 % Show Material materials with Dehnung of 7.0 % | T7351 | Sheet, Plate | AA Standards, ASTM B209 | A50 | ||
7.2 % Show Material materials with Dehnung of 7.2 % | T7351 | |||||
8.0 % Show Material materials with Dehnung of 8.0 % | T7351 | AA Standards, ASTM B211 | A50 | |||
9.0 % Show Material materials with Dehnung of 9.0 % | T7351 | AA Standards, ASTM B211 | A100 | |||
10.0 % Show Material materials with Dehnung of 10.0 % | T7351 | Bar | AA Standards, ASTM B211 | A50 | ||
0 °C | 13 % Show Material materials with Dehnung of 13 % | T7351 | Elongation in 50 mm | |||
24 °C | 13 % Show Material materials with Dehnung of 13 % | T7351 | Elongation in 50 mm | |||
100 °C | 15 % Show Material materials with Dehnung of 15 % | T7351 | Elongation in 50 mm | |||
150 °C | 30 % Show Material materials with Dehnung of 30 % | T7351 | Elongation in 50 mm | |||
205 °C | 55 % Show Material materials with Dehnung of 55 % | T7351 | Elongation in 50 mm | |||
260 °C | 65 % Show Material materials with Dehnung of 65 % | T7351 | Elongation in 50 mm | |||
315 °C | 70 % Show Material materials with Dehnung of 70 % | T7351 | Elongation in 50 mm | |||
370 °C | 70 % Show Material materials with Dehnung of 70 % | T7351 | Elongation in 50 mm | |||
Elastizitätsmodul | 72.0 GPa Show Material materials with Elastizitätsmodul of 72.0 GPa | T7351 | Sheet, Plate, Bar | |||
Härte, HBW | 126.0 - 140.0 [-] Show Material materials with Härte, HBW of 126.0 - 140.0 [-] | T7351 | Sheet, Plate | |||
Plane-Strain Fracture Toughnes | -196 °C | 32.1 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 32.1 MPa·√m | T7351 | For plate in T-L direction | ||
24 °C | 35.9 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 35.9 MPa·√m | T7351 | For plate in T-L direction | |||
Poissonzahl | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | Typical for Wrought 7000 Series Aluminium | ||||
Schubmodule | 26.4 - 27.1 GPa Show Material materials with Schubmodule of 26.4 - 27.1 GPa | Typical for Wrought 7000 Series Aluminium | ||||
Streckgrenze | -196 °C | 496 MPa Show Material materials with Streckgrenze of 496 MPa | T7351 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
-80 °C | 462 MPa Show Material materials with Streckgrenze of 462 MPa | T7351 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
-28 °C | 448 MPa Show Material materials with Streckgrenze of 448 MPa | T7351 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
330.0 MPa Show Material materials with Streckgrenze of 330.0 MPa | T7351 | AA Standards, ASTM B209 | RP02 | |||
340.0 MPa Show Material materials with Streckgrenze of 340.0 MPa | T7351 | AA Standards, ASTM B209 | RP02 | |||
340.0 - 390.0 MPa Show Material materials with Streckgrenze of 340.0 - 390.0 MPa | T7351 | Sheet, Plate | ||||
360.0 MPa Show Material materials with Streckgrenze of 360.0 MPa | T7351 | AA Standards, ASTM B209 | RP02 | |||
380.0 MPa Show Material materials with Streckgrenze of 380.0 MPa | T7351 | AA Standards, ASTM B211 | RP02 | |||
386.0 MPa Show Material materials with Streckgrenze of 386.0 MPa | T7351 | Bar | RP02 | |||
390.0 MPa Show Material materials with Streckgrenze of 390.0 MPa | T7351 | AA Standards, ASTM B209 | RP02 | |||
420.0 MPa Show Material materials with Streckgrenze of 420.0 MPa | T7351 | |||||
425.0 MPa Show Material materials with Streckgrenze of 425.0 MPa | T7351 | AA Standards, ASTM B211 | RP02 | |||
24 °C | 434 MPa Show Material materials with Streckgrenze of 434 MPa | T7351 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
100 °C | 400 MPa Show Material materials with Streckgrenze of 400 MPa | T7351 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
149 °C | 186 MPa Show Material materials with Streckgrenze of 186 MPa | T7351 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
204 °C | 90 MPa Show Material materials with Streckgrenze of 90 MPa | T7351 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
260 °C | 62 MPa Show Material materials with Streckgrenze of 62 MPa | T7351 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
316 °C | 45 MPa Show Material materials with Streckgrenze of 45 MPa | T7351 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
371 °C | 32 MPa Show Material materials with Streckgrenze of 32 MPa | T7351 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |||
Zugfestigkeit | -195 °C | 635 MPa Show Material materials with Zugfestigkeit of 635 MPa | T7351 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
-80 °C | 545 MPa Show Material materials with Zugfestigkeit of 545 MPa | T7351 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
420.0 MPa Show Material materials with Zugfestigkeit of 420.0 MPa | T7351 | AA Standards, ASTM B209 | ||||
430.0 - 475.0 MPa Show Material materials with Zugfestigkeit of 430.0 - 475.0 MPa | T7351 | Sheet, Plate | ||||
435.0 MPa Show Material materials with Zugfestigkeit of 435.0 MPa | T7351 | AA Standards, ASTM B209 | ||||
440.0 MPa Show Material materials with Zugfestigkeit of 440.0 MPa | T7351 | AA Standards, ASTM B209, ASTM B211 | ||||
455.0 MPa Show Material materials with Zugfestigkeit of 455.0 MPa | T7351 | AA Standards, ASTM B209, ASTM B211 | ||||
469.0 MPa Show Material materials with Zugfestigkeit of 469.0 MPa | T7351 | Bar | ||||
470.0 MPa Show Material materials with Zugfestigkeit of 470.0 MPa | T7351 | AA Standards, ASTM B211 | ||||
475.0 MPa Show Material materials with Zugfestigkeit of 475.0 MPa | T7351 | AA Standards, ASTM B209 | ||||
520.0 MPa Show Material materials with Zugfestigkeit of 520.0 MPa | T7351 | |||||
0 °C | 525 MPa Show Material materials with Zugfestigkeit of 525 MPa | T7351 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
24 °C | 503 MPa Show Material materials with Zugfestigkeit of 503 MPa | T7351 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
100 °C | 435 MPa Show Material materials with Zugfestigkeit of 435 MPa | T7351 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
150 °C | 215 MPa Show Material materials with Zugfestigkeit of 215 MPa | T7351 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
205 °C | 110 MPa Show Material materials with Zugfestigkeit of 110 MPa | T7351 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
260 °C | 75 MPa Show Material materials with Zugfestigkeit of 75 MPa | T7351 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
315 °C | 55 MPa Show Material materials with Zugfestigkeit of 55 MPa | T7351 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |||
370 °C | 40 MPa Show Material materials with Zugfestigkeit of 40 MPa | T7351 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture |
Thermisch
Property | Temperature | Value | Condition | Shape | Comment |
---|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 2.3e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.3e-05 1/K | T7351 | |||
2.35e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.35e-05 1/K | T7351 | Bar | |||
100 °C | 0.0000234 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 0.0000234 1/K | T7351 | Sheet, Plate | Mean values between 20°C and the mentioned temperature | |
200 °C | 0.0000243 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 0.0000243 1/K | T7351 | Sheet, Plate | Mean values between 20°C and the mentioned temperature | |
300 °C | 0.0000252 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 0.0000252 1/K | T7351 | Sheet, Plate | Mean values between 20°C and the mentioned temperature | |
Schmelzpunkt | 480.0 °C Show Material materials with Schmelzpunkt of 480.0 °C | T7351 | |||
635.0 °C Show Material materials with Schmelzpunkt of 635.0 °C | T7351 | Bar | |||
Spezifische Wärmekapazität | 862.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 862.0 J/(kg·K) | T7351 | Sheet, Plate | ||
910.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 910.0 J/(kg·K) | T7351 | ||||
Wärmeleitfähigkeit | 130.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 130.0 W/(m·K) | T7351 | |||
130.0 - 160.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 130.0 - 160.0 W/(m·K) | T7351 | Sheet, Plate | |||
134.0 - 160.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 134.0 - 160.0 W/(m·K) | T7351 | Bar |
Elektrisch
Property | Value | Condition | Shape | Comment |
---|---|---|---|---|
Elektrische Leitfähigkeit | 19000000.0 - 23000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 19000000.0 - 23000000.0 S/m | T7351 | Sheet, Plate | |
23000000 S/m Show Material materials with Elektrische Leitfähigkeit of 23000000 S/m | T7351 | Typical/derived value | ||
Specific Electrical conductivity | 40.0 % IACS Show Material materials with Specific Electrical conductivity of 40.0 % IACS | T7351 | Typical value | |
spezifischer Widerstand | 4.3099999999999996e-08 Ω·m Show Material materials with spezifischer Widerstand of 4.3099999999999996e-08 Ω·m | T7351 | Typical value | |
4.31e-08 Ω·m Show Material materials with spezifischer Widerstand of 4.31e-08 Ω·m | T7351 | Bar |
Chemical properties
Property | Value | Condition | Shape | Related Standards | Comment |
---|---|---|---|---|---|
Aluminium | 86.9 - 91.4 % Show Material materials with Aluminium of 86.9 - 91.4 % | T7351 | |||
Andere | 0.15 % Show Material materials with Andere of 0.15 % | T7351 | Sheet, Plate, Bar | Total | |
Chrom | 0.18 - 0.28 % Show Material materials with Chrom of 0.18 - 0.28 % | T7351 | Sheet, Plate, Bar | AA Standards, ASTM B209, ASTM B211 | |
Eisen | 0.50 % Show Material materials with Eisen of 0.50 % | T7351 | AA Standards, ASTM B209, ASTM B211 | ||
0.5 % Show Material materials with Eisen of 0.5 % | T7351 | Sheet, Plate, Bar | |||
Kupfer | 1.2 - 2.0 % Show Material materials with Kupfer of 1.2 - 2.0 % | T7351 | Sheet, Plate, Bar | AA Standards, ASTM B209, ASTM B211 | |
Magnesium | 2.1 - 2.9 % Show Material materials with Magnesium of 2.1 - 2.9 % | T7351 | Sheet, Plate, Bar | AA Standards, ASTM B209, ASTM B211 | |
Mangan | 0.3 % Show Material materials with Mangan of 0.3 % | T7351 | Sheet, Plate, Bar | AA Standards, ASTM B209, ASTM B211 | |
Silizium | 0.4 % Show Material materials with Silizium of 0.4 % | T7351 | Sheet, Plate, Bar | AA Standards, ASTM B209, ASTM B211 | |
Titan | 0.2 % Show Material materials with Titan of 0.2 % | T7351 | Sheet, Plate, Bar | AA Standards, ASTM B209, ASTM B211 | |
Zink | 5.1 - 6.1 % Show Material materials with Zink of 5.1 - 6.1 % | T7351 | Sheet, Plate, Bar | AA Standards, ASTM B209, ASTM B211 | |
Zirkonium | 0.25 % Show Material materials with Zirkonium of 0.25 % | T7351 |
Technological properties
Property | ||
---|---|---|
Anodizing | moderate | |
Application areas | Tool making, mould making and model making; Aerospace; Military technology | |
Brazing | general: no brazing is known or developed | |
Corrosion properties | Stress corrosion cracking: Operational damage in areas with tensile stresses transverse to the grain structure, limited damage to laboratory samples, general: good, without protection in industrial or seawater atmosphere | |
General machinability | General: poor (O), good to acceptable | |
Soldering general | not recommended | |
Welding | Resistance welding: good | |
Workability | general (condition): not suitable |