Allgemein
Property | Value | Condition | Related Standards |
---|---|---|---|
Dichte | 2.71 g/cm³ Show Material materials with Dichte of 2.71 g/cm³ | H28 | AA Standards, ASTM B209 |
2.8 g/cm³ Show Material materials with Dichte of 2.8 g/cm³ | H28 |
Mechanisch
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Dehnung | 1.0 % Show Material materials with Dehnung of 1.0 % | H28 | AA Standards, ASTM B209 | A50 |
1.2 % Show Material materials with Dehnung of 1.2 % | H28 | |||
2.0 % Show Material materials with Dehnung of 2.0 % | H28 | AA Standards, ASTM B209 | A50 | |
4.0 % Show Material materials with Dehnung of 4.0 % | H28 | AA Standards, ASTM B209 | A50 | |
Elastizitätsmodul | 69.0 GPa Show Material materials with Elastizitätsmodul of 69.0 GPa | H28 | AA Standards, ASTM B209 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 1000 Series Aluminium | ||
Poissonzahl | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | Typical for Wrought 1000 Series Aluminium | ||
Schubmodule | 25.9 GPa Show Material materials with Schubmodule of 25.9 GPa | Typical for Wrought 1000 Series Aluminium | ||
Zugfestigkeit | 150.0 MPa Show Material materials with Zugfestigkeit of 150.0 MPa | H28 | AA Standards, ASTM B209 | |
170.0 MPa Show Material materials with Zugfestigkeit of 170.0 MPa | H28 |
Thermisch
Property | Temperature | Value | Condition | Related Standards |
---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 2.4e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.4e-05 1/K | H28 | ||
20 °C | 2.36e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.36e-05 1/K | H28 | AA Standards, ASTM B209 | |
100 °C | 2.36e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.36e-05 1/K | H28 | AA Standards, ASTM B209 | |
Schmelzpunkt | 640.0 - 655.0 °C Show Material materials with Schmelzpunkt of 640.0 - 655.0 °C | H28 | AA Standards, ASTM B209 | |
640.0 °C Show Material materials with Schmelzpunkt of 640.0 °C | H28 | |||
Spezifische Wärmekapazität | 900.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 900.0 J/(kg·K) | H28 | ||
Wärmeleitfähigkeit | 218.0 - 222.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 218.0 - 222.0 W/(m·K) | H28 | AA Standards, ASTM B209 | |
220.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 220.0 W/(m·K) | H28 |
Elektrisch
Property | Value | Condition | Related Standards |
---|---|---|---|
Elektrische Leitfähigkeit | 33000000.0 - 34000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 33000000.0 - 34000000.0 S/m | H28 | AA Standards, ASTM B209 |
spezifischer Widerstand | 2.94e-08 - 3.03e-08 Ω·m Show Material materials with spezifischer Widerstand of 2.94e-08 - 3.03e-08 Ω·m | H28 | AA Standards, ASTM B209 |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Aluminium | 99.0 % Show Material materials with Aluminium of 99.0 % | H28 | AA Standards, ASTM B209 |
99.0 - 100.0 % Show Material materials with Aluminium of 99.0 - 100.0 % | H28 | ||
Andere | 0.15 % Show Material materials with Andere of 0.15 % | H28 | |
Eisen | 1.0 % Show Material materials with Eisen of 1.0 % | H28 | |
Kupfer | 0.05 - 0.2 % Show Material materials with Kupfer of 0.05 - 0.2 % | H28 | AA Standards, ASTM B209 |
Mangan | 0.05 % Show Material materials with Mangan of 0.05 % | H28 | AA Standards, ASTM B209 |
Silizium | 1.0 % Show Material materials with Silizium of 1.0 % | H28 | |
Zink | 0.1 % Show Material materials with Zink of 0.1 % | H28 | AA Standards, ASTM B209 |
Technological properties
Property | ||
---|---|---|
Brazing | general: possible with commercial processes and methods | |
Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
General machinability | General: not suitable (O, H12), poor (H14, H16, H18) | |
Workability | general (condition): good (O, H12, H14), acceptable (H16), poor(H18) |