Eigenschaften
Allgemein
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Dichte | 2.79 g/cm³ Show Material materials with Dichte of 2.79 g/cm³ | T451 | AA Standards, ASTM B211 |
2.79 g/cm³ Show Material materials with Dichte of 2.79 g/cm³ | T451 | ||
3.0 g/cm³ Show Material materials with Dichte of 3.0 g/cm³ | T451 |
Mechanisch
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Bending Fatigue Strength | 125.0 MPa Show Material materials with Bending Fatigue Strength of 125.0 MPa | T451 | AA Standards | ||
Dehnung | -195 °C | 28 % Show Material materials with Dehnung of 28 % | T451 | Elongation in 50 mm | |
-80 °C | 24 % Show Material materials with Dehnung of 24 % | T451 | Elongation in 50 mm | ||
10.0 % Show Material materials with Dehnung of 10.0 % | T451 | AA Standards, ASTM B211 | A100 | ||
12.0 % Show Material materials with Dehnung of 12.0 % | T451 | AA Standards, ASTM B211 | A50 | ||
18.0 % Show Material materials with Dehnung of 18.0 % | T451 | ||||
20.0 % Show Material materials with Dehnung of 20.0 % | T451 | AA Standards | A100 | ||
0 °C | 23 % Show Material materials with Dehnung of 23 % | T451 | Elongation in 50 mm | ||
24 °C | 22 % Show Material materials with Dehnung of 22 % | T451 | Elongation in 50 mm | ||
100 °C | 18 % Show Material materials with Dehnung of 18 % | T451 | Elongation in 50 mm | ||
150 °C | 15 % Show Material materials with Dehnung of 15 % | T451 | Elongation in 50 mm | ||
205 °C | 35 % Show Material materials with Dehnung of 35 % | T451 | Elongation in 50 mm | ||
260 °C | 45 % Show Material materials with Dehnung of 45 % | T451 | Elongation in 50 mm | ||
315 °C | 65 % Show Material materials with Dehnung of 65 % | T451 | Elongation in 50 mm | ||
370 °C | 70 % Show Material materials with Dehnung of 70 % | T451 | Elongation in 50 mm | ||
Elastizitätsmodul | 72 GPa Show Material materials with Elastizitätsmodul of 72 GPa | T451 | |||
73.0 GPa Show Material materials with Elastizitätsmodul of 73.0 GPa | T451 | AA Standards, ASTM B211 | |||
Härte, Brinell | 105.0 [-] Show Material materials with Härte, Brinell of 105.0 [-] | T451 | AA Standards | ||
105.0 [-] Show Material materials with Härte, Brinell of 105.0 [-] | T451 | 500 kg load, 10 mm ball | |||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | |||
Poissonzahl | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | Typical for Wrought 2000 Series Aluminium | |||
Scherfestigkeit | 262.0 MPa Show Material materials with Scherfestigkeit of 262.0 MPa | T451 | |||
Schubmodule | 27.5 GPa Show Material materials with Schubmodule of 27.5 GPa | T451 | |||
28.0 GPa Show Material materials with Schubmodule of 28.0 GPa | T451 | ||||
Streckgrenze | -195 °C | 365 MPa Show Material materials with Streckgrenze of 365 MPa | T451 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | |
-80 °C | 290 MPa Show Material materials with Streckgrenze of 290 MPa | T451 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
-28 °C | 283 MPa Show Material materials with Streckgrenze of 283 MPa | T451 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
220.0 MPa Show Material materials with Streckgrenze of 220.0 MPa | T451 | AA Standards, ASTM B211 | RP02 | ||
260.0 MPa Show Material materials with Streckgrenze of 260.0 MPa | T451 | ||||
275.0 MPa Show Material materials with Streckgrenze of 275.0 MPa | T451 | AA Standards | RP02 | ||
24 °C | 275 MPa Show Material materials with Streckgrenze of 275 MPa | T451 | RP02, up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
100 °C | 270 MPa Show Material materials with Streckgrenze of 270 MPa | T451 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
150 °C | 207 MPa Show Material materials with Streckgrenze of 207 MPa | T451 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
205 °C | 90 MPa Show Material materials with Streckgrenze of 90 MPa | T451 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
260 °C | 50 MPa Show Material materials with Streckgrenze of 50 MPa | T451 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
315 °C | 35 MPa Show Material materials with Streckgrenze of 35 MPa | T451 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
371 °C | 3.5 MPa Show Material materials with Streckgrenze of 3.5 MPa | T451 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture, RP02 | ||
Zugfestigkeit | -195 °C | 550 MPa Show Material materials with Zugfestigkeit of 550 MPa | T451 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | |
-80 °C | 448 MPa Show Material materials with Zugfestigkeit of 448 MPa | T451 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
380.0 MPa Show Material materials with Zugfestigkeit of 380.0 MPa | T451 | AA Standards, ASTM B211 | |||
420.0 MPa Show Material materials with Zugfestigkeit of 420.0 MPa | T451 | ||||
425.0 MPa Show Material materials with Zugfestigkeit of 425.0 MPa | T451 | AA Standards | |||
425 MPa Show Material materials with Zugfestigkeit of 425 MPa | T451 | ||||
0 °C | 440 MPa Show Material materials with Zugfestigkeit of 440 MPa | T451 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
24 °C | 427 MPa Show Material materials with Zugfestigkeit of 427 MPa | T451 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
100 °C | 393 MPa Show Material materials with Zugfestigkeit of 393 MPa | T451 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
150 °C | 275 MPa Show Material materials with Zugfestigkeit of 275 MPa | T451 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
205 °C | 110 MPa Show Material materials with Zugfestigkeit of 110 MPa | T451 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
260 °C | 62 MPa Show Material materials with Zugfestigkeit of 62 MPa | T451 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
315 °C | 40 MPa Show Material materials with Zugfestigkeit of 40 MPa | T451 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture | ||
370 °C | 30 MPa Show Material materials with Zugfestigkeit of 30 MPa | T451 | up to 10000 h at temperature, at 35 MPa/min to yield strength and then at strain rate of 5%/min to fracture |
Thermisch
| Property | Temperature | Value | Condition | Related Standards |
|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 2.4e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.4e-05 1/K | T451 | ||
20 °C | 2.36e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.36e-05 1/K | T451 | AA Standards, ASTM B211 | |
100 °C | 2.36e-05 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.36e-05 1/K | T451 | AA Standards, ASTM B211 | |
Schmelzpunkt | 510.0 - 640.0 °C Show Material materials with Schmelzpunkt of 510.0 - 640.0 °C | T451 | AA Standards, ASTM B211 | |
510.0 °C Show Material materials with Schmelzpunkt of 510.0 °C | T451 | |||
Spezifische Wärmekapazität | 870.0 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 870.0 J/(kg·K) | T451 | ||
Wärmeleitfähigkeit | 134.0 - 193.0 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 134.0 - 193.0 W/(m·K) | T451 | AA Standards, ASTM B211 |
Elektrisch
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Elektrische Leitfähigkeit | 20000000.0 - 29000000.0 S/m Show Material materials with Elektrische Leitfähigkeit of 20000000.0 - 29000000.0 S/m | T451 | AA Standards, ASTM B211 |
spezifischer Widerstand | 3.45e-08 - 5e-08 Ω·m Show Material materials with spezifischer Widerstand of 3.45e-08 - 5e-08 Ω·m | T451 | AA Standards, ASTM B211 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 91.6 - 95.5 % Show Material materials with Aluminium of 91.6 - 95.5 % | T451 | |
Andere | 0.15 % Show Material materials with Andere of 0.15 % | T451 | |
Chrom | 0.1 % Show Material materials with Chrom of 0.1 % | T451 | AA Standards, ASTM B211 |
Eisen | 0.70 % Show Material materials with Eisen of 0.70 % | T451 | AA Standards, ASTM B211 |
0.7 % Show Material materials with Eisen of 0.7 % | T451 | ||
Kupfer | 3.5 - 4.5 % Show Material materials with Kupfer of 3.5 - 4.5 % | T451 | AA Standards, ASTM B211 |
Magnesium | 0.4 - 0.8 % Show Material materials with Magnesium of 0.4 - 0.8 % | T451 | AA Standards, ASTM B211 |
Mangan | 0.4 - 1.0 % Show Material materials with Mangan of 0.4 - 1.0 % | T451 | AA Standards, ASTM B211 |
Silizium | 0.2 - 0.8 % Show Material materials with Silizium of 0.2 - 0.8 % | T451 | AA Standards, ASTM B211 |
Titan | 0.15 % Show Material materials with Titan of 0.15 % | T451 | AA Standards, ASTM B211 |
Zink | 0.25 % Show Material materials with Zink of 0.25 % | T451 | AA Standards, ASTM B211 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: Operational damage in areas with tensile stresses transverse to the grain structure, limited damage to laboratory samples, general: sufficient, in principle it should be protected | |
| General machinability | General: good to acceptable | |
| Workability | general (condition): poor(T4, T451) | |