Eigenschaften
Allgemein
| Property | Value |
|---|---|
Dichte | 8.85 g/cm³ Show Supplier Material materials with Dichte of 8.85 g/cm³ |
Abmessung
| Property | Value |
|---|---|
Dimensions | Strip thickness 0.08 - 3.0 mm, other gauges on request. Strip width from 8.5 mm. Electroplated and Hot-dip tinned strip available. |
Mechanisch
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Biegefestigkeit 180°, in longitudinaler Richtung | 0.5 [-] Show Supplier Material materials with Biegefestigkeit 180°, in longitudinaler Richtung of 0.5 [-] | ASTM B820 | R585(TM00) | bending thickness: ≤ 0.5 mm & bending width: 10 mm |
1 [-] Show Supplier Material materials with Biegefestigkeit 180°, in longitudinaler Richtung of 1 [-] | ASTM B820 | R655(TM02) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
1.5 [-] Show Supplier Material materials with Biegefestigkeit 180°, in longitudinaler Richtung of 1.5 [-] | ASTM B820 | R725(TM03) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
2 [-] Show Supplier Material materials with Biegefestigkeit 180°, in longitudinaler Richtung of 2 [-] | ASTM B820 | R760(TM04) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
Biegefähigkeit 180°, in transversaler Richtung | 1 [-] Show Supplier Material materials with Biegefähigkeit 180°, in transversaler Richtung of 1 [-] | ASTM B820 | R585(TM00) | bending thickness: ≤ 0.5 mm & bending width: 10 mm |
2.5 [-] Show Supplier Material materials with Biegefähigkeit 180°, in transversaler Richtung of 2.5 [-] | ASTM B820 | R655(TM02) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
3.5 [-] Show Supplier Material materials with Biegefähigkeit 180°, in transversaler Richtung of 3.5 [-] | ASTM B820 | R725(TM03) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
6 [-] Show Supplier Material materials with Biegefähigkeit 180°, in transversaler Richtung of 6 [-] | ASTM B820 | R760(TM04) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
Biegefähigkeit 90°, in longitudinaler Richtung | 0 [-] Show Supplier Material materials with Biegefähigkeit 90°, in longitudinaler Richtung of 0 [-] | EN ISO 7438 | R585(TM00) | bending thickness: ≤ 0.5 mm & bending width: 10 mm |
0.5 [-] Show Supplier Material materials with Biegefähigkeit 90°, in longitudinaler Richtung of 0.5 [-] | EN ISO 7438 | R655(TM02) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
1 [-] Show Supplier Material materials with Biegefähigkeit 90°, in longitudinaler Richtung of 1 [-] | EN ISO 7438 | R725(TM03) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
1.5 [-] Show Supplier Material materials with Biegefähigkeit 90°, in longitudinaler Richtung of 1.5 [-] | EN ISO 7438 | R760(TM04) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
Biegefähigkeit 90°, in transversaler Richtung | 0 [-] Show Supplier Material materials with Biegefähigkeit 90°, in transversaler Richtung of 0 [-] | EN ISO 7438 | R585(TM00) | bending thickness: ≤ 0.5 mm & bending width: 10 mm |
1 [-] Show Supplier Material materials with Biegefähigkeit 90°, in transversaler Richtung of 1 [-] | EN ISO 7438 | R655(TM02) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
1.5 [-] Show Supplier Material materials with Biegefähigkeit 90°, in transversaler Richtung of 1.5 [-] | EN ISO 7438 | R725(TM03) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
3 [-] Show Supplier Material materials with Biegefähigkeit 90°, in transversaler Richtung of 3 [-] | EN ISO 7438 | R760(TM04) | bending thickness: ≤ 0.5 mm & bending width: 10 mm | |
Dehnung | 1 % Show Supplier Material materials with Dehnung of 1 % | R760(TM04), A50 | |
2 % Show Supplier Material materials with Dehnung of 2 % | R725(TM03), A50 | ||
5 % Show Supplier Material materials with Dehnung of 5 % | R655(TM02), A50 | ||
10 % Show Supplier Material materials with Dehnung of 10 % | R585(TM00), A50 | ||
Elastizitätsmodul | 132 GPa Show Supplier Material materials with Elastizitätsmodul of 132 GPa | ||
Härte, Vickers | 160 - 210 [-] Show Supplier Material materials with Härte, Vickers of 160 - 210 [-] | R585(TM00) | For reference only | |
190 - 225 [-] Show Supplier Material materials with Härte, Vickers of 190 - 225 [-] | R655(TM02) | For reference only | ||
200 - 240 [-] Show Supplier Material materials with Härte, Vickers of 200 - 240 [-] | R725(TM03) | For reference only | ||
220 - 260 [-] Show Supplier Material materials with Härte, Vickers of 220 - 260 [-] | R760(TM04) | For reference only | ||
Poissonzahl | 0.33 [-] Show Supplier Material materials with Poissonzahl of 0.33 [-] | ||
Streckgrenze | 450 MPa Show Supplier Material materials with Streckgrenze of 450 MPa | min. | R585(TM00) | |
620 - 725 MPa Show Supplier Material materials with Streckgrenze of 620 - 725 MPa | R655(TM02) | ||
655 MPa Show Supplier Material materials with Streckgrenze of 655 MPa | min. | R725(TM03) | ||
690 MPa Show Supplier Material materials with Streckgrenze of 690 MPa | R760(TM04) | ||
Zugfestigkeit | 585 - 655 MPa Show Supplier Material materials with Zugfestigkeit of 585 - 655 MPa | R585(TM00) | |
655 - 745 MPa Show Supplier Material materials with Zugfestigkeit of 655 - 745 MPa | R655(TM02) | ||
725 - 830 MPa Show Supplier Material materials with Zugfestigkeit of 725 - 830 MPa | R725(TM03) | ||
760 - 860 MPa Show Supplier Material materials with Zugfestigkeit of 760 - 860 MPa | R760(TM04) |
Thermisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 1.7e-05 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.7e-05 1/K | average value between 20-300°C | |
Spezifische Wärmekapazität | 399 J/(kg·K) Show Supplier Material materials with Spezifische Wärmekapazität of 399 J/(kg·K) | ||
Wärmeleitfähigkeit | 20 °C | 190 W/(m·K) Show Supplier Material materials with Wärmeleitfähigkeit of 190 W/(m·K) |
Elektrisch
| Property | Temperature | Value |
|---|---|---|
Elektrische Leitfähigkeit | 20 °C | 0.0028 S/m Show Supplier Material materials with Elektrische Leitfähigkeit of 0.0028 S/m |
Specific Electrical conductivity | 20 °C | 49 % IACS Show Supplier Material materials with Specific Electrical conductivity of 49 % IACS |
Chemical properties
Technological properties
| Property | ||
|---|---|---|
| Application areas | Application target: Ideal for automotive connectors | |
| Chemical composition | The chemical composition is the nominal composition of the alloy | |
| Coating | Electroplating: Good Hot dip tinning: Good | |
| Cold Forming | Very good | |
| Machining | Not suitable | |
| Packaging size | Standard coils with outside diameters up to 1200 mm. Traverse-wound coils with drum weights up to 500 kg. Multiple-coil up to 3 tons. | |
| Soldering general | Soft soldering: Good | |
| Testings | Fatigue strength: The fatigue strength is defined as the maximum bending stress amplitude which a material withstands for 10.000.000 load cycles under symmetrical alternate load without breaking. It depends on the temper selected and can be estimated typically by 1/3 of tensile strength. For solid solution fine grain materials fatigue strength might increase up to 0,5 * of tensile strength. Bending test: 90° bend test According to EN ISO 7438, 180° bend test acc. to ASTM B820, shown values might show orange- peel, however no crack. | |
| Welding | Resistance welding: Average | |