Eigenschaften
Allgemein
| Property | Temperature | Value | Condition | Testing Standard | Thickness | Comment |
|---|---|---|---|---|---|---|
Dichte | 1.73 g/cm³ Show Supplier Material materials with Dichte of 1.73 g/cm³ | dry | ISO 1183 | |||
Moisture absorption | 23 °C | 0.8 % Show Supplier Material materials with Moisture absorption of 0.8 % | 50%RH | ISO 62 | 2 mm | |
Wasserabsorption | 3.2 % Show Supplier Material materials with Wasserabsorption of 3.2 % | ISO 62 | 2 mm | immersion at 23°C |
Mechanisch
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Biegefestigkeit | 320 MPa Show Supplier Material materials with Biegefestigkeit of 320 MPa | 50%RH | ISO 178 | 2mm/min | |
390 MPa Show Supplier Material materials with Biegefestigkeit of 390 MPa | dry | ISO 178 | 2mm/min | ||
Biegemodul | 17 GPa Show Supplier Material materials with Biegemodul of 17 GPa | 50%RH | ISO 178 | 2mm/min | |
20.9 GPa Show Supplier Material materials with Biegemodul of 20.9 GPa | dry | ISO 178 | 2mm/min | ||
Dehnung | 2.2 % Show Supplier Material materials with Dehnung of 2.2 % | dry | ISO 527-2/1A | 5mm/min | |
2.3 % Show Supplier Material materials with Dehnung of 2.3 % | 50%RH | ISO 527-2/1A | 5mm/min | ||
Elastizitätsmodul | 17 GPa Show Supplier Material materials with Elastizitätsmodul of 17 GPa | 50%RH | ISO 527-2/1A | 1mm/min | |
22 GPa Show Supplier Material materials with Elastizitätsmodul of 22 GPa | dry | ISO 527-2/1A | 1mm/min | ||
Schlagfestigkeit, Charpy gekerbt | -30 °C | 15 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 15 kJ/m² | dry | ISO 179/1eA | |
-30 °C | 16 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 16 kJ/m² | 50%RH | ISO 179/1eA | ||
23 °C | 17 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 17 kJ/m² | dry | ISO 179/1eA | ||
23 °C | 18 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 18 kJ/m² | 50%RH | ISO 179/1eA | ||
Schlagzähigkeit, Charpy ungekerbt | 83 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 83 kJ/m² | dry | ISO 179/1eU | -30°C | |
85 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 85 kJ/m² | dry | ISO 179/1eU | 23°C | ||
85 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 85 kJ/m² | 50%RH | ISO 179/1eU | -30°C | ||
90 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 90 kJ/m² | 50%RH | ISO 179/1eU | 23°C | ||
Zugfestigkeit | 190 MPa Show Supplier Material materials with Zugfestigkeit of 190 MPa | 50%RH | ISO 527-2/1A | 5mm/min | |
275 MPa Show Supplier Material materials with Zugfestigkeit of 275 MPa | dry | ISO 527-2/1A | 5mm/min |
Thermisch
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 1.3e-05 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.3e-05 1/K | ISO 11359-1/-2 | 23°C-55°C |
7.3e-05 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 7.3e-05 1/K | ISO 11359-1/-2 | 23°C-55°C, Transverse | |
Schmelzpunkt | 255 °C Show Supplier Material materials with Schmelzpunkt of 255 °C | ISO 11357-1/-3 | 10°C/min |
Wärmeformbeständigkeitstemperatur | 245 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 245 °C | ISO 75/2Af | 1.80 MPa |
Elektrisch
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Surface resistivity | 1e+10 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+10 Ω/sq | 50%RH | IEC 60093 | 500V |
1e+12 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq | dry | IEC 60093 | 500V | |
Volume resistivity | 1e+11 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+11 Ω·cm | 50%RH | IEC 60093 | 500V |
1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | dry | IEC 60093 | 500V |
Rheological Properties
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Schrumpfung | 0.1 % Show Supplier Material materials with Schrumpfung of 0.1 % | 290/100/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa] |
0.3 % Show Supplier Material materials with Schrumpfung of 0.3 % | 290/100/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa], Transverse |
Technological properties
| Property | ||
|---|---|---|
| Additives | Release agent | |
| Certifications | RoHS 2011/65/UE | |
| Color | Black | |
| Features | Heat Stabilized | |
| Fillers | 60% Glass Fiber | |
| Processing methods | Injection Molding | |