Eigenschaften
Allgemein
| Property | Temperature | Value | Condition | Testing Standard | Thickness | Comment |
|---|---|---|---|---|---|---|
Dichte | 1.34 g/cm³ Show Supplier Material materials with Dichte of 1.34 g/cm³ | dry | ISO 1183 | |||
Moisture absorption | 23 °C | 2.2 % Show Supplier Material materials with Moisture absorption of 2.2 % | 50%RH | ISO 62 | 2 mm | |
Wasserabsorption | 8 % Show Supplier Material materials with Wasserabsorption of 8 % | ISO 62 | 2 mm | immersion at 23°C |
Mechanisch
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Biegefestigkeit | 115 MPa Show Supplier Material materials with Biegefestigkeit of 115 MPa | dry | ISO 178 | 2mm/min | |
Biegemodul | 3.7 GPa Show Supplier Material materials with Biegemodul of 3.7 GPa | dry | ISO 178 | 2mm/min | |
Dehnung | 12 % Show Supplier Material materials with Dehnung of 12 % | dry | ISO 527-2/1A | 50mm/min | nominal | |
50 % Show Supplier Material materials with Dehnung of 50 % | 50%RH | ISO 527-2/1A | 50mm/min | nominal | ||
Elastizitätsmodul | 2.4 GPa Show Supplier Material materials with Elastizitätsmodul of 2.4 GPa | 50%RH | ISO 527-2/1A | 1mm/min | |
3.9 GPa Show Supplier Material materials with Elastizitätsmodul of 3.9 GPa | dry | ISO 527-2/1A | 1mm/min | ||
Elongation at yield | 3 % Show Supplier Material materials with Elongation at yield of 3 % | dry | ISO 527-2/1A | 50mm/min | |
10 % Show Supplier Material materials with Elongation at yield of 10 % | 50%RH | ISO 527-2/1A | 50mm/min | ||
Schlagfestigkeit, Charpy gekerbt | -30 °C | 3.5 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 3.5 kJ/m² | dry | ISO 179/1eA | |
23 °C | 4 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 4 kJ/m² | dry | ISO 179/1eA | ||
23 °C | 5.5 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 5.5 kJ/m² | 50%RH | ISO 179/1eA | ||
Schlagzähigkeit, Charpy ungekerbt | 30 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 30 kJ/m² | dry | ISO 179/1eU | -30°C | |
35 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 35 kJ/m² | dry | ISO 179/1eU | 23°C | ||
40 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 40 kJ/m² | 50%RH | ISO 179/1eU | 23°C | ||
Streckgrenze | 35 MPa Show Supplier Material materials with Streckgrenze of 35 MPa | 50%RH | ISO 527-2/1A | 50mm/min | |
65 MPa Show Supplier Material materials with Streckgrenze of 65 MPa | dry | ISO 527-2/1A | 50mm/min |
Thermisch
| Property | Value | Thickness | Testing Standard | Comment | |||
|---|---|---|---|---|---|---|---|
Glow Wire Flammability Index | 700 °C Show Supplier Material materials with Glow Wire Flammability Index of 700 °C | 2 mm | IEC 60695-2-12 | ||||
Schmelzpunkt | 220 °C Show Supplier Material materials with Schmelzpunkt of 220 °C | ISO 11357-1/-3 | 10°C/min | ||||
Vicat-Erweichungstemperatur | 200 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 200 °C | ISO 306 | 50°C/h 50N | ||||
Wärmeformbeständigkeitstemperatur | 70 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 70 °C | ISO 75/2Af | 1.80 MPa | ||||
170 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 170 °C | ISO 75/2Bf | 0.45 MPa | |||||
Entflammbarkeit | Thickness tested (mm): 0.8, Class: HB, Standard: UL 94 | Automotive Interior Flammability(mm/min): 0 ,method: ISO 3795 and thickness tested (mm): 3 | ||||||
Elektrisch
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Kriechstromfestigkeit | 450 V Show Supplier Material materials with Kriechstromfestigkeit of 450 V | dry | IEC 60112 | Sol.A |
Surface resistivity | 1e+10 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+10 Ω/sq | 50%RH | IEC 60093 | 500V |
1e+12 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq | dry | IEC 60093 | 500V | |
Volume resistivity | 1e+11 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+11 Ω·cm | 50%RH | IEC 60093 | 500V |
1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | dry | IEC 60093 | 500V |
Rheological Properties
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Schrumpfung | 1.1 % Show Supplier Material materials with Schrumpfung of 1.1 % | 280/80/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa] |
1.1 % Show Supplier Material materials with Schrumpfung of 1.1 % | 280/80/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa], Transverse |
Technological properties
| Property | ||
|---|---|---|
| Additives | Release agent | |
| Certifications | RoHS 2011/65/UE | |
| Color | Natural | |
| Fillers | 30% Glass Bead | |
| Processing methods | Injection Molding | |