Eigenschaften
Allgemein
| Property | Temperature | Value | Condition | Testing Standard | Thickness | Comment |
|---|---|---|---|---|---|---|
Dichte | 1.51 g/cm³ Show Supplier Material materials with Dichte of 1.51 g/cm³ | dry | ISO 1183 | |||
Moisture absorption | 23 °C | 0.6 % Show Supplier Material materials with Moisture absorption of 0.6 % | 50%RH | ISO 62 | 2 mm | |
Wasserabsorption | 1.5 % Show Supplier Material materials with Wasserabsorption of 1.5 % | ISO 62 | 2 mm | immersion at 23°C |
Mechanisch
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Biegefestigkeit | 265 MPa Show Supplier Material materials with Biegefestigkeit of 265 MPa | 50%RH | ISO 178 | 2mm/min | |
295 MPa Show Supplier Material materials with Biegefestigkeit of 295 MPa | dry | ISO 178 | 2mm/min | ||
Biegemodul | 11.9 GPa Show Supplier Material materials with Biegemodul of 11.9 GPa | 50%RH | ISO 178 | 2mm/min | |
13 GPa Show Supplier Material materials with Biegemodul of 13 GPa | dry | ISO 178 | 2mm/min | ||
Dehnung | 3 % Show Supplier Material materials with Dehnung of 3 % | dry | ISO 527-2/1A | 5mm/min | |
3.2 % Show Supplier Material materials with Dehnung of 3.2 % | 50%RH | ISO 527-2/1A | 5mm/min | ||
Elastizitätsmodul | 13.4 GPa Show Supplier Material materials with Elastizitätsmodul of 13.4 GPa | 50%RH | ISO 527-2/1A | 1mm/min | |
14.9 GPa Show Supplier Material materials with Elastizitätsmodul of 14.9 GPa | dry | ISO 527-2/1A | 1mm/min | ||
Schlagfestigkeit, Charpy gekerbt | -30 °C | 14 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 14 kJ/m² | dry | ISO 179/1eA | |
23 °C | 15 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 15 kJ/m² | dry | ISO 179/1eA | ||
23 °C | 17 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 17 kJ/m² | 50%RH | ISO 179/1eA | ||
Schlagzähigkeit, Charpy ungekerbt | 80 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 80 kJ/m² | dry | ISO 179/1eU | -30°C | |
95 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 95 kJ/m² | dry | ISO 179/1eU | 23°C | ||
100 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 100 kJ/m² | 50%RH | ISO 179/1eU | 23°C | ||
Zugfestigkeit | 170 MPa Show Supplier Material materials with Zugfestigkeit of 170 MPa | 50%RH | ISO 527-2/1A | 5mm/min | |
190 MPa Show Supplier Material materials with Zugfestigkeit of 190 MPa | dry | ISO 527-2/1A | 5mm/min |
Thermisch
| Property | Value | Testing Standard | Comment | ||
|---|---|---|---|---|---|
Schmelzpunkt | 220 °C Show Supplier Material materials with Schmelzpunkt of 220 °C | ISO 11357-1/-3 | 10°C/min | ||
Wärmeformbeständigkeitstemperatur | 200 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 200 °C | ISO 75/2Af | 1.00E+12mm | ||
Entflammbarkeit | Thickness tested (mm): 1.6, Class: HB, Standard: UL 94 | Automotive Interior Flammability(mm/min): 0 ,method: ISO 3795 and thickness tested (mm): 3 | ||||
Elektrisch
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Volume resistivity | 1e+11 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+11 Ω·cm | 50%RH | IEC 60093 | 500V |
1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | dry | IEC 60093 | 500V |
Rheological Properties
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Schrumpfung | 0.2 % Show Supplier Material materials with Schrumpfung of 0.2 % | 280/90/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa] |
0.6 % Show Supplier Material materials with Schrumpfung of 0.6 % | 280/90/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa], Transverse |
Technological properties
| Property | ||
|---|---|---|
| Additives | Release agent | |
| Certifications | Food Contact, Drinking Water, RoHS 2011/65/UE | |
| Color | Black | |
| Features | Hydrolysis Resistance, Heat Stabilized | |
| Fillers | 50% Glass Fiber | |
| Processing methods | Injection Molding | |