Eigenschaften
Allgemein
| Property | Temperature | Value | Condition | Testing Standard | Thickness | Comment |
|---|---|---|---|---|---|---|
Dichte | 1.34 g/cm³ Show Supplier Material materials with Dichte of 1.34 g/cm³ | dry | ISO 1183 | |||
Moisture absorption | 23 °C | 1.7 % Show Supplier Material materials with Moisture absorption of 1.7 % | 50%RH | ISO 62 | 2 mm | |
Wasserabsorption | 6 % Show Supplier Material materials with Wasserabsorption of 6 % | ISO 62 | 2 mm | immersion at 23°C |
Mechanisch
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Biegefestigkeit | 190 MPa Show Supplier Material materials with Biegefestigkeit of 190 MPa | 50%RH | ISO 178 | 2mm/min | |
270 MPa Show Supplier Material materials with Biegefestigkeit of 270 MPa | dry | ISO 178 | 2mm/min | ||
Biegemodul | 7.5 GPa Show Supplier Material materials with Biegemodul of 7.5 GPa | 50%RH | ISO 178 | 2mm/min | |
11.2 GPa Show Supplier Material materials with Biegemodul of 11.2 GPa | dry | ISO 178 | 2mm/min | ||
Dehnung | 2.7 % Show Supplier Material materials with Dehnung of 2.7 % | dry | ISO 527-2/1A | 5mm/min | |
5 % Show Supplier Material materials with Dehnung of 5 % | 50%RH | ISO 527-2/1A | 5mm/min | ||
Elastizitätsmodul | 8.1 GPa Show Supplier Material materials with Elastizitätsmodul of 8.1 GPa | 50%RH | ISO 527-2/1A | 1mm/min | |
11.8 GPa Show Supplier Material materials with Elastizitätsmodul of 11.8 GPa | dry | ISO 527-2/1A | 1mm/min | ||
Schlagfestigkeit, Charpy gekerbt | -30 °C | 5.5 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 5.5 kJ/m² | dry | ISO 179/1eA | |
23 °C | 8.5 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 8.5 kJ/m² | dry | ISO 179/1eA | ||
23 °C | 11 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 11 kJ/m² | 50%RH | ISO 179/1eA | ||
Schlagzähigkeit, Charpy ungekerbt | -30 °C | 50 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 50 kJ/m² | dry | ISO 179/1eU | |
23 °C | 65 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 65 kJ/m² | dry | ISO 179/1eU | ||
23 °C | 70 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 70 kJ/m² | 50%RH | ISO 179/1eU | ||
Zugfestigkeit | 125 MPa Show Supplier Material materials with Zugfestigkeit of 125 MPa | 50%RH | ISO 527-2/1A | 5mm/min | |
175 MPa Show Supplier Material materials with Zugfestigkeit of 175 MPa | dry | ISO 527-2/1A | 5mm/min |
Thermisch
| Property | Value | Thickness | Testing Standard | Comment | |||
|---|---|---|---|---|---|---|---|
Glow Wire Flammability Index | 700 °C Show Supplier Material materials with Glow Wire Flammability Index of 700 °C | 2 mm | IEC 60695-2-12 | ||||
Schmelzpunkt | 260 °C Show Supplier Material materials with Schmelzpunkt of 260 °C | 1000 mm | ISO 11357-1/-3 | 10°C/min | |||
Entflammbarkeit | Thickness tested (mm): 1.6, Class: HB, Standard: UL 94 | Automotive Interior Flammability(mm/min): <10 ,method: ISO 3795 and thickness tested (mm): 3 | ||||||
Elektrisch
Technological properties
| Property | ||
|---|---|---|
| Additives | Release agent | |
| Certifications | RoHS 2011/65/UE | |
| Color | Black | |
| Features | Increased Electrical Conductivity | |
| Fillers | 30% Glass Fiber and Carbon Fiber | |
| Processing methods | Injection Molding | |