Eigenschaften
Allgemein
| Property | Temperature | Value | Condition | Testing Standard | Thickness | Comment |
|---|---|---|---|---|---|---|
Dichte | 1.39 g/cm³ Show Supplier Material materials with Dichte of 1.39 g/cm³ | dry | ISO 1183 | |||
Moisture absorption | 23 °C | 1.5 % Show Supplier Material materials with Moisture absorption of 1.5 % | 50%RH | ISO 62 | 2 mm | |
Wasserabsorption | 6.3 % Show Supplier Material materials with Wasserabsorption of 6.3 % | ISO 62 | 2 mm | immersion at 23°C |
Mechanisch
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Biegefestigkeit | 190 MPa Show Supplier Material materials with Biegefestigkeit of 190 MPa | 50%RH | ISO 178 | 2mm/min | |
270 MPa Show Supplier Material materials with Biegefestigkeit of 270 MPa | dry | ISO 178 | 2mm/min | ||
Biegemodul | 7 GPa Show Supplier Material materials with Biegemodul of 7 GPa | 50%RH | ISO 178 | 2mm/min | |
9.4 GPa Show Supplier Material materials with Biegemodul of 9.4 GPa | dry | ISO 178 | 2mm/min | ||
Dehnung | 3.5 % Show Supplier Material materials with Dehnung of 3.5 % | dry | ISO 527-2/1A | 5mm/min | |
6.5 % Show Supplier Material materials with Dehnung of 6.5 % | 50%RH | ISO 527-2/1A | 5mm/min | ||
Elastizitätsmodul | 7.6 GPa Show Supplier Material materials with Elastizitätsmodul of 7.6 GPa | 50%RH | ISO 527-2/1A | 1mm/min | |
10.5 GPa Show Supplier Material materials with Elastizitätsmodul of 10.5 GPa | dry | ISO 527-2/1A | 1mm/min | ||
Schlagfestigkeit, Charpy gekerbt | -30 °C | 14 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 14 kJ/m² | dry | ISO 179/1eA | |
23 °C | 16 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 16 kJ/m² | dry | ISO 179/1eA | ||
23 °C | 20 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 20 kJ/m² | 50%RH | ISO 179/1eA | ||
Schlagzähigkeit, Charpy ungekerbt | -30 °C | 95 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 95 kJ/m² | dry | ISO 179/1eU | |
23 °C | 90 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 90 kJ/m² | 50%RH | ISO 179/1eU | ||
23 °C | 95 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 95 kJ/m² | dry | ISO 179/1eU | ||
Zugfestigkeit | 120 MPa Show Supplier Material materials with Zugfestigkeit of 120 MPa | 50%RH | ISO 527-2/1A | 5mm/min | |
170 MPa Show Supplier Material materials with Zugfestigkeit of 170 MPa | dry | ISO 527-2/1A | 5mm/min |
Thermisch
| Property | Value | Testing Standard | Thickness | Comment | |||
|---|---|---|---|---|---|---|---|
Ball pressure temperature | 160 °C Show Supplier Material materials with Ball pressure temperature of 160 °C | IEC 60695-10-2 | |||||
Glow Wire Flammability Index | 700 °C Show Supplier Material materials with Glow Wire Flammability Index of 700 °C | IEC 60695-2-12 | 2 mm | ||||
Schmelzpunkt | 260 °C Show Supplier Material materials with Schmelzpunkt of 260 °C | ISO 11357-1/-3 | 10°C/min | ||||
Wärmeformbeständigkeitstemperatur | 240 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 240 °C | ISO 75/2Af | 1.80 MPa | ||||
Entflammbarkeit | Thickness tested (mm): 0.8, Class: HB, Standard: UL 94 | Automotive Interior Flammability(mm/min): method: ISO 3795 and thickness tested (mm): 3 | ||||||
Elektrisch
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Kriechstromfestigkeit | 350 V Show Supplier Material materials with Kriechstromfestigkeit of 350 V | dry | IEC 60112 | Sol.A |
Surface resistivity | 1e+10 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+10 Ω/sq | 50%RH | IEC 60093 | 500V |
1e+12 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq | dry | IEC 60093 | 500V | |
Volume resistivity | 1e+11 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+11 Ω·cm | 50%RH | IEC 60093 | 500V |
1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | dry | IEC 60093 | 500V |
Rheological Properties
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Schrumpfung | 0.4 % Show Supplier Material materials with Schrumpfung of 0.4 % | 300/90/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa] |
0.9 % Show Supplier Material materials with Schrumpfung of 0.9 % | 300/90/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa], Transverse |
Technological properties
| Property | ||
|---|---|---|
| Additives | Release agent | |
| Certifications | Yellow Card, RoHS 2011/65/UE | |
| Features | Heat Stabilized | |
| Fillers | 35% Glass Fiber | |
| Processing methods | Injection Molding | |