Eigenschaften
Allgemein
| Property | Temperature | Value | Condition | Testing Standard | Thickness | Comment |
|---|---|---|---|---|---|---|
Dichte | 1.42 g/cm³ Show Supplier Material materials with Dichte of 1.42 g/cm³ | dry | ISO 1183 | |||
Moisture absorption | 23 °C | 1.6 % Show Supplier Material materials with Moisture absorption of 1.6 % | 50%RH | ISO 62 | 2 mm | |
Wasserabsorption | 5.2 % Show Supplier Material materials with Wasserabsorption of 5.2 % | ISO 62 | 2 mm | immersion at 23°C |
Mechanisch
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Biegefestigkeit | 140 MPa Show Supplier Material materials with Biegefestigkeit of 140 MPa | 50%RH | ISO 178 | 2mm/min | |
220 MPa Show Supplier Material materials with Biegefestigkeit of 220 MPa | dry | ISO 178 | 2mm/min | ||
Biegemodul | 6.3 GPa Show Supplier Material materials with Biegemodul of 6.3 GPa | 50%RH | ISO 178 | 2mm/min | |
9.9 GPa Show Supplier Material materials with Biegemodul of 9.9 GPa | dry | ISO 178 | 2mm/min | ||
Dehnung | 3 % Show Supplier Material materials with Dehnung of 3 % | dry | ISO 527-2/1A | 5mm/min | |
4.5 % Show Supplier Material materials with Dehnung of 4.5 % | 50%RH | ISO 527-2/1A | 5mm/min | ||
Elastizitätsmodul | 7.2 GPa Show Supplier Material materials with Elastizitätsmodul of 7.2 GPa | 50%RH | ISO 527-2/1A | 1mm/min | |
10.6 GPa Show Supplier Material materials with Elastizitätsmodul of 10.6 GPa | dry | ISO 527-2/1A | 1mm/min | ||
Schlagfestigkeit, Charpy gekerbt | 23 °C | 7 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 7 kJ/m² | dry | ISO 179/1eA | |
23 °C | 15 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 15 kJ/m² | 50%RH | ISO 179/1eA | ||
Schlagzähigkeit, Charpy ungekerbt | 23 °C | 70 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 70 kJ/m² | dry | ISO 179/1eU | |
23 °C | 85 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 85 kJ/m² | 50%RH | ISO 179/1eU | ||
Zugfestigkeit | 90 MPa Show Supplier Material materials with Zugfestigkeit of 90 MPa | 50%RH | ISO 527-2/1A | 5mm/min | |
137 MPa Show Supplier Material materials with Zugfestigkeit of 137 MPa | dry | ISO 527-2/1A | 5mm/min |
Thermisch
| Property | Value | Thickness | Testing Standard | Comment | |||
|---|---|---|---|---|---|---|---|
Glow Wire Flammability Index | 960 °C Show Supplier Material materials with Glow Wire Flammability Index of 960 °C | 1 mm, 2 mm | IEC 60695-2-12 | ||||
Glow Wire Ignition Temperature | 725 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 725 °C | 1 mm | IEC 60695-2-13 | ||||
775 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 775 °C | 2 mm | IEC 60695-2-13 | |||||
Schmelzpunkt | 220 °C Show Supplier Material materials with Schmelzpunkt of 220 °C | ISO 11357-1/-3 | 10°C/min | ||||
Vicat-Erweichungstemperatur | 210 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 210 °C | ISO 306 | 50°C/h 50N | ||||
Wärmeformbeständigkeitstemperatur | 190 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 190 °C | ISO 75/2Af | 1.80 MPa | ||||
Entflammbarkeit | Thickness tested (mm): 0.8, Class: V-0, Standard: UL 94 | Automotive Interior Flammability(mm/min): 0 ,method: ISO 3795 and thickness tested (mm): 3 | ||||||
Elektrisch
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Kriechstromfestigkeit | 600 V Show Supplier Material materials with Kriechstromfestigkeit of 600 V | dry | IEC 60112 | Sol.A |
Surface resistivity | 1e+10 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+10 Ω/sq | 50%RH | IEC 60093 | 500V |
1e+12 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq | dry | IEC 60093 | 500V | |
Volume resistivity | 1e+11 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+11 Ω·cm | 50%RH | IEC 60093 | 500V |
1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | dry | IEC 60093 | 500V |
Rheological Properties
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Schrumpfung | 0.3 % Show Supplier Material materials with Schrumpfung of 0.3 % | 270/80/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa] |
0.6 % Show Supplier Material materials with Schrumpfung of 0.6 % | 270/80/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa], Transverse |
Technological properties
| Property | ||
|---|---|---|
| Additives | Release agent, Flame retarding agent | |
| Certifications | Yellow Card, RoHS 2011/65/UE | |
| Color | Black | |
| Features | Flame Retardant, Halogen-free, Phosphorus-free, Heat Stabilized | |
| Fillers | 30% Glass Fiber | |
| Other | Federal Motor Vehicle Safety Standards (FMVSS) : Standard-ISO 3795, Assessment-DNI | |
| Processing methods | Injection Molding | |