Property | Value | Testing Standard |
---|---|---|
Dichte | 1.67 g/cm³ Show Supplier Material materials with Dichte of 1.67 g/cm³ | ISO 1183 |
Mechanisch
Property | Temperature | Value | Testing Standard | Comment |
---|---|---|---|---|
Biegefestigkeit | 210 MPa Show Supplier Material materials with Biegefestigkeit of 210 MPa | ISO 178 | 2mm/min | |
Biegemodul | 10.1 GPa Show Supplier Material materials with Biegemodul of 10.1 GPa | ISO 178 | 2mm/min | |
Dehnung | 2.5 % Show Supplier Material materials with Dehnung of 2.5 % | ISO 527-2/1A | 5mm/min | |
Elastizitätsmodul | 10.6 GPa Show Supplier Material materials with Elastizitätsmodul of 10.6 GPa | ISO 527-2/1A | 1mm/min | |
Schlagfestigkeit, Charpy gekerbt | 23 °C | 10 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 10 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | 23 °C | 60 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 60 kJ/m² | ISO 179/1eU | |
Zugfestigkeit | 135 MPa Show Supplier Material materials with Zugfestigkeit of 135 MPa | ISO 527-2/1A | 5mm/min |
Thermisch
Property | Value | Thickness | Testing Standard | Comment | |||
---|---|---|---|---|---|---|---|
Glow Wire Flammability Index | 960 °C Show Supplier Material materials with Glow Wire Flammability Index of 960 °C | 1 mm, 2 mm | IEC 60695-2-12 | ||||
Schmelzpunkt | 225 °C Show Supplier Material materials with Schmelzpunkt of 225 °C | ISO 11357-1/-3 | 10°C/min | ||||
Vicat-Erweichungstemperatur | 210 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 210 °C | ISO 306 | 50°C/h 50N | ||||
Wärmeformbeständigkeitstemperatur | 205 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 205 °C | ISO 75/2Af | 1.80 MPa | ||||
220 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 220 °C | ISO 75/2Bf | 0.45 MPa | |||||
Entflammbarkeit | Thickness tested (mm): 0.4 and 0.8, Class: V-0, Standard: UL 94 | Automotive Interior Flammability(mm/min): 0 ,method: ISO 3795 and thickness tested (mm): 3 |
Elektrisch
Property | Value | Testing Standard | Comment |
---|---|---|---|
Kriechstromfestigkeit | 250 V Show Supplier Material materials with Kriechstromfestigkeit of 250 V | IEC 60112 | Sol.A |
Surface resistivity | 1e+10 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+10 Ω/sq | IEC 60093 | 500V |
1e+12 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq | IEC 60093 | 500V | |
Volume resistivity | 1e+11 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+11 Ω·cm | IEC 60093 | 500V |
1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | IEC 60093 | 500V |
Rheological Properties
Property | Value | Testing Standard | Condition | Comment |
---|---|---|---|---|
Schmelzmassenflussrate | 3.5 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 3.5 g/10min | ISO 1133 | 250°C/2.16Kg | |
Schrumpfung | 0.4 % Show Supplier Material materials with Schrumpfung of 0.4 % | ISO 294-4 | 270/80/60* | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa] |
0.9 % Show Supplier Material materials with Schrumpfung of 0.9 % | ISO 294-4 | 270/80/60* | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa], Transverse |
Technological properties
Property | ||
---|---|---|
Additives | Release agent, Flame retarding agent | |
Certifications | Yellow Card, RoHS 2011/65/UE | |
Color | Black | |
Features | Flame Retardant, Heat Stabilized | |
Fillers | 30% Glass Fiber | |
Processing methods | Injection Molding |