Eigenschaften
Allgemein
| Property | Temperature | Value | Condition | Testing Standard | Thickness | Comment |
|---|---|---|---|---|---|---|
Dichte | 1.16 g/cm³ Show Supplier Material materials with Dichte of 1.16 g/cm³ | dry | ISO 1183 | |||
Moisture absorption | 23 °C | 2 % Show Supplier Material materials with Moisture absorption of 2 % | 50%RH | ISO 62 | 2 mm | |
Sauerstoffindex | 23 °C | 35 % Show Supplier Material materials with Sauerstoffindex of 35 % | ISO 4589-2 | |||
Wasserabsorption | 8 % Show Supplier Material materials with Wasserabsorption of 8 % | ISO 62 | 2 mm | immersion at 23°C |
Mechanisch
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Biegefestigkeit | 110 MPa Show Supplier Material materials with Biegefestigkeit of 110 MPa | dry | ISO 178 | 2mm/min | |
Biegemodul | 3.3 GPa Show Supplier Material materials with Biegemodul of 3.3 GPa | dry | ISO 178 | 2mm/min | |
Dehnung | 12 % Show Supplier Material materials with Dehnung of 12 % | dry | ISO 527-2/1A | 50mm/min | nominal | |
Elastizitätsmodul | 3.5 GPa Show Supplier Material materials with Elastizitätsmodul of 3.5 GPa | dry | ISO 527-2/1A | 1mm/min | |
Elongation at yield | 3 % Show Supplier Material materials with Elongation at yield of 3 % | dry | ISO 527-2/1A | 50mm/min | |
Schlagfestigkeit, Charpy gekerbt | 23 °C | 5 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 5 kJ/m² | dry | ISO 179/1eA | |
Streckgrenze | 75 MPa Show Supplier Material materials with Streckgrenze of 75 MPa | dry | ISO 527-2/1A | 50mm/min |
Thermisch
| Property | Value | Thickness | Testing Standard | Comment | |||
|---|---|---|---|---|---|---|---|
Glow Wire Flammability Index | 960 °C Show Supplier Material materials with Glow Wire Flammability Index of 960 °C | 1 mm, 2 mm | IEC 60695-2-12 | ||||
Glow Wire Ignition Temperature | 800 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 800 °C | 1 mm, 2 mm | IEC 60695-2-13 | ||||
Schmelzpunkt | 220 °C Show Supplier Material materials with Schmelzpunkt of 220 °C | ISO 11357-1/-3 | 10°C/min | ||||
Vicat-Erweichungstemperatur | 195 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 195 °C | ISO 306 | 50°C/h 50N | ||||
Wärmeformbeständigkeitstemperatur | 75 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 75 °C | ISO 75/2Af | 1.80 MPa | ||||
160 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 160 °C | ISO 75/2Bf | 0.45 MPa | |||||
Entflammbarkeit | Thickness tested (mm): 0.4 and 0.8, Class: V-0, Standard: UL 94 | Automotive Interior Flammability(mm/min): 0 ,method: ISO 3795 and thickness tested (mm): 3 | ||||||
Elektrisch
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Surface resistivity | 1e+10 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+10 Ω/sq | 50%RH | IEC 60093 | 500V |
1e+12 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq | dry | IEC 60093 | 500V | |
Volume resistivity | 1e+11 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+11 Ω·cm | 50%RH | IEC 60093 | 500V |
1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | dry | IEC 60093 | 500V |
Rheological Properties
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Schrumpfung | 1 % Show Supplier Material materials with Schrumpfung of 1 % | 270/70/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa] |
1 % Show Supplier Material materials with Schrumpfung of 1 % | 270/70/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa], Transverse |
Technological properties
| Property | ||
|---|---|---|
| Additives | Release agent, Flame retarding agent | |
| Certifications | Yellow Card, RoHS 2011/65/UE | |
| Color | Deep black | |
| Features | Flame Retardant, Heat Stabilized | |
| Other | Fire Classification I2/F2, Standard: NF F16-101, for thickness 0.75 mm HL1-HL2-HL3/R22, Standard: EN 45545-2, for thickness 0.75 mm | |
| Processing methods | Injection Molding,Profile Extrusion | |