Eigenschaften
Allgemein
| Property | Value | Condition | Testing Standard |
|---|---|---|---|
Dichte | 1.21 g/cm³ Show Supplier Material materials with Dichte of 1.21 g/cm³ | dry | ISO 1183 |
Mechanisch
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Biegefestigkeit | 120 MPa Show Supplier Material materials with Biegefestigkeit of 120 MPa | dry | ISO 178 | 2mm/min | |
Biegemodul | 4.4 GPa Show Supplier Material materials with Biegemodul of 4.4 GPa | dry | ISO 178 | 2mm/min | |
Dehnung | 3.8 % Show Supplier Material materials with Dehnung of 3.8 % | dry | ISO 527-2/1A | 5mm/min | |
Elastizitätsmodul | 5.4 GPa Show Supplier Material materials with Elastizitätsmodul of 5.4 GPa | dry | ISO 527-2/1A | 1mm/min | |
Schlagfestigkeit, Charpy gekerbt | 23 °C | 15 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 15 kJ/m² | dry | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | 23 °C | 70 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 70 kJ/m² | dry | ISO 179/1eU | |
Zugfestigkeit | 100 MPa Show Supplier Material materials with Zugfestigkeit of 100 MPa | dry | ISO 527-2/1A | 5mm/min |
Thermisch
| Property | Value | Testing Standard | Comment | ||
|---|---|---|---|---|---|
Schmelzpunkt | 255 °C Show Supplier Material materials with Schmelzpunkt of 255 °C | ISO 11357-1/-3 | 10°C/min | ||
Wärmeformbeständigkeitstemperatur | 210 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 210 °C | ISO 75/2Af | 1.80 MPa | ||
Entflammbarkeit | Thickness tested (mm): 0.8, Class: HB, Standard: UL 94 | ||||
Rheological Properties
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 5 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 5 g/10min | ISO 1133 | 275°C/10Kg |
Technological properties
| Property | ||
|---|---|---|
| Certifications | Yellow Card, RoHS 2011/65/UE | |
| Color | Black | |
| Features | Heat Stabilized | |
| Fillers | 15% Glass Fiber | |
| Processing methods | Injection Molding,Blow Molding | |