Eigenschaften
Allgemein
| Property | Value | Condition | Testing Standard |
|---|---|---|---|
Dichte | 1.33 g/cm³ Show Supplier Material materials with Dichte of 1.33 g/cm³ | dry | ISO 1183 |
Mechanisch
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Biegefestigkeit | 80 MPa Show Supplier Material materials with Biegefestigkeit of 80 MPa | 50%RH | ISO 178 | 2mm/min | |
160 MPa Show Supplier Material materials with Biegefestigkeit of 160 MPa | dry | ISO 178 | 2mm/min | ||
Biegemodul | 2.8 GPa Show Supplier Material materials with Biegemodul of 2.8 GPa | 50%RH | ISO 178 | 2mm/min | |
6.7 GPa Show Supplier Material materials with Biegemodul of 6.7 GPa | dry | ISO 178 | 2mm/min | ||
Dehnung | 5 % Show Supplier Material materials with Dehnung of 5 % | dry | ISO 527-2/1A | 5mm/min | |
25 % Show Supplier Material materials with Dehnung of 25 % | 50%RH | ISO 527-2/1A | 5mm/min | ||
Elastizitätsmodul | 3 GPa Show Supplier Material materials with Elastizitätsmodul of 3 GPa | 50%RH | ISO 527-2/1A | 1mm/min | |
6.9 GPa Show Supplier Material materials with Elastizitätsmodul of 6.9 GPa | dry | ISO 527-2/1A | 1mm/min | ||
Schlagfestigkeit, Charpy gekerbt | 23 °C | 5 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 5 kJ/m² | dry | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | -30 °C | 35 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 35 kJ/m² | dry | ISO 179/1eU | |
23 °C | 70 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 70 kJ/m² | dry | ISO 179/1eU | ||
Zugfestigkeit | 55 MPa Show Supplier Material materials with Zugfestigkeit of 55 MPa | 50%RH | ISO 527-2/1A | 5mm/min | |
95 MPa Show Supplier Material materials with Zugfestigkeit of 95 MPa | dry | ISO 527-2/1A | 5mm/min |
Thermisch
| Property | Value | Testing Standard | Comment | ||
|---|---|---|---|---|---|
Schmelzpunkt | 260 °C Show Supplier Material materials with Schmelzpunkt of 260 °C | ISO 11357-1/-3 | 10°C/min | ||
Entflammbarkeit | Thickness tested (mm): 0.8, Class: HB, Standard: UL 94 | Automotive Interior Flammability(mm/min): 0 ,method: ISO 3795 and thickness tested (mm): 3 | ||||
Elektrisch
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Surface resistivity | 1e+10 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+10 Ω/sq | 50%RH | IEC 60093 | 500V |
1e+12 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq | dry | IEC 60093 | 500V | |
Volume resistivity | 1e+11 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+11 Ω·cm | 50%RH | IEC 60093 | 500V |
1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | dry | IEC 60093 | 500V |
Rheological Properties
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 76 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 76 g/10min | ISO 1133 | 275°C/2.16Kg |
Schmelzvolumenflussrate | 66 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 66 cm³/10min | ISO 1133 | 275°C/2.16Kg |
Technological properties
| Property | ||
|---|---|---|
| Additives | Release agent | |
| Certifications | RoHS 2011/65/UE | |
| Color | Black | |
| Features | Heat Stabilized | |
| Fillers | 25% Mineral Powder | |
| Processing methods | Injection Molding | |