Eigenschaften
Allgemein
| Property | Temperature | Value | Condition | Testing Standard | Thickness |
|---|---|---|---|---|---|
Dichte | 1.24 g/cm³ Show Supplier Material materials with Dichte of 1.24 g/cm³ | dry | ISO 1183 | ||
Moisture absorption | 23 °C | 1.7 % Show Supplier Material materials with Moisture absorption of 1.7 % | 50%RH | ISO 62 | 2 mm |
Mechanisch
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Biegefestigkeit | 100 MPa Show Supplier Material materials with Biegefestigkeit of 100 MPa | dry | ISO 178 | 2mm/min | |
Biegemodul | 3 GPa Show Supplier Material materials with Biegemodul of 3 GPa | dry | ISO 178 | 2mm/min | |
Dehnung | 17 % Show Supplier Material materials with Dehnung of 17 % | dry | ISO 527-2/1A | 50mm/min | nominal | |
Elastizitätsmodul | 3.2 GPa Show Supplier Material materials with Elastizitätsmodul of 3.2 GPa | dry | ISO 527-2/1A | 1mm/min | |
Elongation at yield | 10 % Show Supplier Material materials with Elongation at yield of 10 % | dry | ISO 527-2/1A | 50mm/min | |
Schlagfestigkeit, Charpy gekerbt | -30 °C | 4 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 4 kJ/m² | dry | ISO 179/1eA | |
23 °C | 4.5 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 4.5 kJ/m² | dry | ISO 179/1eA | ||
Schlagzähigkeit, Charpy ungekerbt | -30 °C | 97 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 97 kJ/m² | dry | ISO 179/1eU | |
23 °C | 96 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 96 kJ/m² | dry | ISO 179/1eU | ||
Streckgrenze | 73 MPa Show Supplier Material materials with Streckgrenze of 73 MPa | dry | ISO 527-2/1A | 50mm/min |
Thermisch
| Property | Value | Testing Standard | Comment | ||
|---|---|---|---|---|---|
Schmelzpunkt | 260 °C Show Supplier Material materials with Schmelzpunkt of 260 °C | ISO 11357-1/-3 | 10°C/min | ||
Wärmeformbeständigkeitstemperatur | 70 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 70 °C | ISO 75/2Af | 1.80 MPa | ||
Entflammbarkeit | Thickness tested (mm): 0.8, Class: HB, Standard: UL 94 | Automotive Interior Flammability(mm/min): 0 ,method: ISO 3795 and thickness tested (mm): 3 | ||||
Technological properties
| Property | ||
|---|---|---|
| Additives | Release agent | |
| Certifications | RoHS 2011/65/UE | |
| Color | Black | |
| Features | Metal Detectable | |