Eigenschaften
Allgemein
| Property | Temperature | Value | Condition | Testing Standard | Thickness | Comment |
|---|---|---|---|---|---|---|
Dichte | 1.23 g/cm³ Show Supplier Material materials with Dichte of 1.23 g/cm³ | dry | ISO 1183 | |||
Moisture absorption | 23 °C | 2.3 % Show Supplier Material materials with Moisture absorption of 2.3 % | 50%RH | ISO 62 | 2 mm | |
Wasserabsorption | 7.9 % Show Supplier Material materials with Wasserabsorption of 7.9 % | ISO 62 | 2 mm | immersion at 23°C |
Mechanisch
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Biegefestigkeit | 185 MPa Show Supplier Material materials with Biegefestigkeit of 185 MPa | dry | ISO 178 | 2mm/min | |
Biegemodul | 5 GPa Show Supplier Material materials with Biegemodul of 5 GPa | dry | ISO 178 | 2mm/min | |
Dehnung | 4.2 % Show Supplier Material materials with Dehnung of 4.2 % | dry | ISO 527-2/1A | 5mm/min | |
Elastizitätsmodul | 5.6 GPa Show Supplier Material materials with Elastizitätsmodul of 5.6 GPa | dry | ISO 527-2/1A | 1mm/min | |
Schlagfestigkeit, Charpy gekerbt | 23 °C | 9 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 9 kJ/m² | dry | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | -30 °C | 45 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 45 kJ/m² | dry | ISO 179/1eU | |
23 °C | 70 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 70 kJ/m² | dry | ISO 179/1eU | ||
Zugfestigkeit | 120 MPa Show Supplier Material materials with Zugfestigkeit of 120 MPa | dry | ISO 527-2/1A | 5mm/min |
Thermisch
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Schmelzpunkt | 260 °C Show Supplier Material materials with Schmelzpunkt of 260 °C | ISO 11357-1/-3 | 10°C/min |
Vicat-Erweichungstemperatur | 245 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 245 °C | ISO 306 | 3mm |
Wärmeformbeständigkeitstemperatur | 226 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 226 °C | ISO 75/2Af | 1.80 MPa |
240 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 240 °C | ISO 75/2Bf | 0.45 MPa |
Elektrisch
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Surface resistivity | 1e+12 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq | dry | IEC 60093 | 500V |
Rheological Properties
| Property | Value | Testing Standard | Condition | Comment |
|---|---|---|---|---|
Schmelzmassenflussrate | 27 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 27 g/10min | ISO 1133 | 275°C/3.25Kg | |
Schrumpfung | 0.5 % Show Supplier Material materials with Schrumpfung of 0.5 % | ISO 294-4 | 300/90/60* | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa] |
0.8 % Show Supplier Material materials with Schrumpfung of 0.8 % | ISO 294-4 | 300/90/60* | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa], Transverse | |
Viscosity number | 140 cm³/gr Show Supplier Material materials with Viscosity number of 140 cm³/gr | ISO 307 | Sulfuric acid |
Technological properties
| Property | ||
|---|---|---|
| Certifications | RoHS 2011/65/UE | |
| Color | Black | |
| Fillers | 15% Glass Fiber | |
| Processing methods | Injection Molding | |