Allgemein
Property | Temperature | Value | Condition | Testing Standard | Thickness | Comment |
---|---|---|---|---|---|---|
Dichte | 1.06 g/cm³ Show Supplier Material materials with Dichte of 1.06 g/cm³ | dry | ISO 1183 | |||
Moisture absorption | 23 °C | 1.8 % Show Supplier Material materials with Moisture absorption of 1.8 % | 50%RH | ISO 62 | 2 mm | |
Wasserabsorption | 7 % Show Supplier Material materials with Wasserabsorption of 7 % | ISO 62 | 2 mm | immersion at 23°C |
Mechanisch
Property | Temperature | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|---|
Biegefestigkeit | 55 MPa Show Supplier Material materials with Biegefestigkeit of 55 MPa | dry | ISO 178 | 2mm/min | |
Biegemodul | 1.4 GPa Show Supplier Material materials with Biegemodul of 1.4 GPa | dry | ISO 178 | 2mm/min | |
Dehnung | 90 % Show Supplier Material materials with Dehnung of 90 % | dry | ISO 527-2/1A | 50mm/min | nominal | |
100 % Show Supplier Material materials with Dehnung of 100 % | 50%RH | ISO 527-2/1A | min. | 50mm/min | nominal | ||
Elastizitätsmodul | 0.85 GPa Show Supplier Material materials with Elastizitätsmodul of 0.85 GPa | 50%RH | ISO 527-2/1A | 1mm/min | |
1.6 GPa Show Supplier Material materials with Elastizitätsmodul of 1.6 GPa | dry | ISO 527-2/1A | 1mm/min | ||
Elongation at yield | 15 % Show Supplier Material materials with Elongation at yield of 15 % | dry | ISO 527-2/1A | 50mm/min | |
30 % Show Supplier Material materials with Elongation at yield of 30 % | 50%RH | ISO 527-2/1A | 50mm/min | ||
Schlagfestigkeit, Charpy gekerbt | -30 °C | 80 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 80 kJ/m² | dry | ISO 179/1eA | |
23 °C | 100 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 100 kJ/m² | dry | ISO 179/1eA | ||
23 °C | 125 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 125 kJ/m² | 50%RH | ISO 179/1eA | ||
Streckgrenze | 25 MPa Show Supplier Material materials with Streckgrenze of 25 MPa | 50%RH | ISO 527-2/1A | 50mm/min | |
42 MPa Show Supplier Material materials with Streckgrenze of 42 MPa | dry | ISO 527-2/1A | 50mm/min |
Thermisch
Property | Value | Thickness | Testing Standard | Comment | |||
---|---|---|---|---|---|---|---|
Glow Wire Flammability Index | 650 °C Show Supplier Material materials with Glow Wire Flammability Index of 650 °C | 2 mm | IEC 60695-2-12 | ||||
Glow Wire Ignition Temperature | 675 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 675 °C | 2 mm | IEC 60695-2-13 | ||||
Schmelzpunkt | 260 °C Show Supplier Material materials with Schmelzpunkt of 260 °C | ISO 11357-1/-3 | 10°C/min | ||||
Vicat-Erweichungstemperatur | 180 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 180 °C | ISO 306 | 50°C/h 50N | ||||
Wärmeformbeständigkeitstemperatur | 65 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 65 °C | ISO 75/2Af | 1.80 MPa | ||||
Entflammbarkeit | Thickness tested (mm): 0.8, Class: HB, Standard: UL 94 | Automotive Interior Flammability(mm/min): <30 ,method: ISO 3795 and thickness tested (mm): 3 |
Elektrisch
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Kriechstromfestigkeit | 600 V Show Supplier Material materials with Kriechstromfestigkeit of 600 V | dry | IEC 60112 | Sol.A |
Surface resistivity | 1e+10 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+10 Ω/sq | 50%RH | IEC 60093 | 500V |
1e+12 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq | dry | IEC 60093 | 500V | |
Volume resistivity | 1e+11 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+11 Ω·cm | 50%RH | IEC 60093 | 500V |
1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | dry | IEC 60093 | 500V |
Rheological Properties
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Schrumpfung | 1.7 % Show Supplier Material materials with Schrumpfung of 1.7 % | 290/70/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa], Transverse |
1.9 % Show Supplier Material materials with Schrumpfung of 1.9 % | 290/70/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa] |
Technological properties
Property | ||
---|---|---|
Additives | Release agent | |
Certifications | RoHS 2011/65/UE | |
Color | Natural | |
Features | Impact Modified | |
Processing methods | Injection Molding |