Allgemein
Property | Temperature | Value | Condition | Testing Standard | Thickness | Comment |
---|---|---|---|---|---|---|
Dichte | 1.44 g/cm³ Show Supplier Material materials with Dichte of 1.44 g/cm³ | dry | ISO 1183 | |||
Moisture absorption | 23 °C | 1.5 % Show Supplier Material materials with Moisture absorption of 1.5 % | 50%RH | ISO 62 | 2 mm | |
Wasserabsorption | 0.2 % Show Supplier Material materials with Wasserabsorption of 0.2 % | ISO 62 | 2 mm | 24h immersion at 23°C |
Mechanisch
Property | Temperature | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|---|
Biegefestigkeit | 235 MPa Show Supplier Material materials with Biegefestigkeit of 235 MPa | 50%RH | ISO 178 | 2mm/min | |
250 MPa Show Supplier Material materials with Biegefestigkeit of 250 MPa | dry | ISO 178 | 2mm/min | ||
Biegemodul | 9.5 GPa Show Supplier Material materials with Biegemodul of 9.5 GPa | 50%RH | ISO 178 | 2mm/min | |
10.2 GPa Show Supplier Material materials with Biegemodul of 10.2 GPa | dry | ISO 178 | 2mm/min | ||
Dehnung | 1.6 % Show Supplier Material materials with Dehnung of 1.6 % | dry | ISO 527-2/1A | 5mm/min | |
1.8 % Show Supplier Material materials with Dehnung of 1.8 % | 50%RH | ISO 527-2/1A | 5mm/min | ||
Elastizitätsmodul | 11 GPa Show Supplier Material materials with Elastizitätsmodul of 11 GPa | 50%RH | ISO 527-2/1A | 1mm/min | |
11.6 GPa Show Supplier Material materials with Elastizitätsmodul of 11.6 GPa | dry | ISO 527-2/1A | 1mm/min | ||
Schlagfestigkeit, Charpy gekerbt | -30 °C | 7 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 7 kJ/m² | dry | ISO 179/1eA | |
23 °C | 8 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 8 kJ/m² | dry | ISO 179/1eA | ||
23 °C | 10 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 10 kJ/m² | 50%RH | ISO 179/1eA | ||
Schlagzähigkeit, Charpy ungekerbt | -30 °C | 45 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 45 kJ/m² | dry | ISO 179/1eU | |
23 °C | 50 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 50 kJ/m² | dry | ISO 179/1eU | ||
Zugfestigkeit | 150 MPa Show Supplier Material materials with Zugfestigkeit of 150 MPa | 50%RH | ISO 527-2/1A | 5mm/min | |
160 MPa Show Supplier Material materials with Zugfestigkeit of 160 MPa | dry | ISO 527-2/1A | 5mm/min |
Thermisch
Property | Value | Testing Standard | Comment | ||
---|---|---|---|---|---|
Schmelzpunkt | 312 °C Show Supplier Material materials with Schmelzpunkt of 312 °C | ISO 11357-1/-3 | 10°C/min | ||
Wärmeformbeständigkeitstemperatur | 285 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 285 °C | ISO 75/2Af | 1.80 MPa | ||
Entflammbarkeit | Thickness tested (mm): 0.8, Class: HB, Standard: UL 94 |
Elektrisch
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Surface resistivity | 1e+12 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq | dry | IEC 60093 | 500V |
Volume resistivity | 1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | dry | IEC 60093 | 500V |
Rheological Properties
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Schrumpfung | 0.3 % Show Supplier Material materials with Schrumpfung of 0.3 % | 325/140/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa] |
0.8 % Show Supplier Material materials with Schrumpfung of 0.8 % | 325/140/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa], Transverse |
Technological properties
Property | ||
---|---|---|
Additives | Release agent | |
Certifications | RoHS 2011/65/UE, Drinking Water | |
Color | Black | |
Fillers | 30% Glass Fiber | |
Processing methods | Injection Molding |