Allgemein
Property | Value | Condition | Testing Standard | Thickness | Comment |
---|---|---|---|---|---|
Dichte | 1.62 g/cm³ Show Supplier Material materials with Dichte of 1.62 g/cm³ | dry | ISO 1183 | ||
Wasserabsorption | 0.2 % Show Supplier Material materials with Wasserabsorption of 0.2 % | ISO 62 | 2 mm | 24h immersion at 23°C |
Mechanisch
Property | Temperature | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|---|
Biegefestigkeit | 360 MPa Show Supplier Material materials with Biegefestigkeit of 360 MPa | dry | ISO 178 | 2mm/min | |
Biegemodul | 15.5 GPa Show Supplier Material materials with Biegemodul of 15.5 GPa | dry | ISO 178 | 2mm/min | |
Dehnung | 2 % Show Supplier Material materials with Dehnung of 2 % | dry | ISO 527-2/1A | 5mm/min | |
Elastizitätsmodul | 18.1 GPa Show Supplier Material materials with Elastizitätsmodul of 18.1 GPa | dry | ISO 527-2/1A | 1mm/min | |
Schlagfestigkeit, Charpy gekerbt | 23 °C | 16 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 16 kJ/m² | dry | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | 23 °C | 80 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 80 kJ/m² | dry | ISO 179/1eU | |
Zugfestigkeit | 250 MPa Show Supplier Material materials with Zugfestigkeit of 250 MPa | dry | ISO 527-2/1A | 5mm/min |
Thermisch
Property | Value | Thickness | Testing Standard | Comment | |||
---|---|---|---|---|---|---|---|
Schmelzpunkt | 310 °C Show Supplier Material materials with Schmelzpunkt of 310 °C | 1e+12 mm | ISO 11357-1/-3 | 10°C/min | |||
Entflammbarkeit | Thickness tested (mm): 3 Class: HB, Standard: UL 94 |
Elektrisch
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Volume resistivity | 1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | dry | IEC 60093 | 500V |
Technological properties
Property | ||
---|---|---|
Additives | Release agent | |
Certifications | RoHS 2011/65/UE | |
Color | Black | |
Features | Heat Stabilized | |
Fillers | 50% Glass Fiber | |
Processing methods | Injection Molding |