Allgemein
Property | Temperature | Value | Condition | Testing Standard | Thickness | Comment |
---|---|---|---|---|---|---|
Dichte | 1.14 g/cm³ Show Supplier Material materials with Dichte of 1.14 g/cm³ | dry | ISO 1183 | |||
Moisture absorption | 23 °C | 1.7 % Show Supplier Material materials with Moisture absorption of 1.7 % | 50%RH | ISO 62 | 2 mm | |
Wasserabsorption | 5.5 % Show Supplier Material materials with Wasserabsorption of 5.5 % | ISO 62 | 2 mm | immersion at 23°C |
Mechanisch
Property | Temperature | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|---|
Biegefestigkeit | 45 MPa Show Supplier Material materials with Biegefestigkeit of 45 MPa | 50%RH | ISO 178 | 2mm/min | |
90 MPa Show Supplier Material materials with Biegefestigkeit of 90 MPa | dry | ISO 178 | 2mm/min | ||
Biegemodul | 1.3 GPa Show Supplier Material materials with Biegemodul of 1.3 GPa | 50%RH | ISO 178 | 2mm/min | |
2.9 GPa Show Supplier Material materials with Biegemodul of 2.9 GPa | dry | ISO 178 | 2mm/min | ||
Dehnung | 45 % Show Supplier Material materials with Dehnung of 45 % | dry | ISO 527-2/1A | 50mm/min | nominal | |
100 % Show Supplier Material materials with Dehnung of 100 % | 50%RH | ISO 527-2/1A | 50mm/min | nominal | ||
Elastizitätsmodul | 1.3 GPa Show Supplier Material materials with Elastizitätsmodul of 1.3 GPa | 50%RH | ISO 527-2/1A | 1mm/min | |
2.8 GPa Show Supplier Material materials with Elastizitätsmodul of 2.8 GPa | dry | ISO 527-2/1A | 1mm/min | ||
Elongation at yield | 3 % Show Supplier Material materials with Elongation at yield of 3 % | dry | ISO 527-2/1A | 50mm/min | |
15 % Show Supplier Material materials with Elongation at yield of 15 % | 50%RH | ISO 527-2/1A | 50mm/min | ||
Schlagfestigkeit, Charpy gekerbt | -30 °C | 9 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 9 kJ/m² | dry | ISO 179/1eA | |
23 °C | 10 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 10 kJ/m² | dry | ISO 179/1eA | ||
23 °C | 18 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 18 kJ/m² | 50%RH | ISO 179/1eA | ||
Schlagzähigkeit, Charpy ungekerbt | No Break at 23°C | dry, 50%RH | ISO 179/1eU | ||
Streckgrenze | 35 MPa Show Supplier Material materials with Streckgrenze of 35 MPa | 50%RH | ISO 527-2/1A | 50mm/min | |
55 MPa Show Supplier Material materials with Streckgrenze of 55 MPa | dry | ISO 527-2/1A | 50mm/min |
Thermisch
Technological properties
Property | ||
---|---|---|
Additives | Release agent | |
Certifications | RoHS 2011/65/UE | |
Color | Natural | |
Features | Amorphous, Improved Dimensional Stability, High Surface Aspect, Low moisture absorption, Heat Stabilized | |
Fillers | 10% Mineral Powder | |
Processing methods | Injection Molding |