Eigenschaften
Allgemein
| Property | Value | Condition | Testing Standard |
|---|---|---|---|
Dichte | 1.07 g/cm³ Show Supplier Material materials with Dichte of 1.07 g/cm³ | dry | ISO 1183 |
Mechanisch
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Biegefestigkeit | 9 MPa Show Supplier Material materials with Biegefestigkeit of 9 MPa | 50%RH | ISO 178 | 2mm/min | |
10 MPa Show Supplier Material materials with Biegefestigkeit of 10 MPa | dry | ISO 178 | 2mm/min | ||
Biegemodul | 0.2 GPa Show Supplier Material materials with Biegemodul of 0.2 GPa | 50%RH | ISO 178 | 2mm/min | |
0.25 GPa Show Supplier Material materials with Biegemodul of 0.25 GPa | dry | ISO 178 | 2mm/min | ||
Dehnung | 100 % Show Supplier Material materials with Dehnung of 100 % | dry, 50%RH | ISO 527-2/1A | min. | 50mm/min | nominal | |
Elastizitätsmodul | 0.23 GPa Show Supplier Material materials with Elastizitätsmodul of 0.23 GPa | 50%RH | ISO 527-2/1A | 1mm/min | |
0.26 GPa Show Supplier Material materials with Elastizitätsmodul of 0.26 GPa | dry | ISO 527-2/1A | 1mm/min | ||
Modul bei 100 % Dehnung | 0.022 GPa Show Supplier Material materials with Modul bei 100 % Dehnung of 0.022 GPa | dry | ISO 527-2/1A | ||
Modulus at 50% elongation | 0.019 GPa Show Supplier Material materials with Modulus at 50% elongation of 0.019 GPa | dry | ISO 527-2/1A | ||
Schlagfestigkeit, Charpy gekerbt | -30 °C | 13 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 13 kJ/m² | dry | ISO 179/1eA | |
23 °C | 100 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 100 kJ/m² | 50%RH | ISO 179/1eA | ||
23 °C | 105 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 105 kJ/m² | dry | ISO 179/1eA | ||
Streckgrenze | 19 MPa Show Supplier Material materials with Streckgrenze of 19 MPa | 50%RH | ISO 527-2/1A | 50mm/min | |
23 MPa Show Supplier Material materials with Streckgrenze of 23 MPa | dry | ISO 527-2/1A | 50mm/min |
Thermisch
| Property | Value | Testing Standard | Comment | ||
|---|---|---|---|---|---|
Schmelzpunkt | 212 °C Show Supplier Material materials with Schmelzpunkt of 212 °C | ISO 11357-1/-3 | 10°C/min | ||
Entflammbarkeit | Thickness tested (mm): 0.8, Class: HB, Standard: UL 94 | Automotive Interior Flammability(mm/min): <30 ,method: ISO 3795 and thickness tested (mm): 3 | ||||
Elektrisch
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Surface resistivity | 1e+10 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+10 Ω/sq | 50%RH | IEC 60093 | 500V |
1e+12 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq | dry | IEC 60093 | 500V | |
Volume resistivity | 1e+11 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+11 Ω·cm | 50%RH | IEC 60093 | 500V |
1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | dry | IEC 60093 | 500V |
Technological properties
| Property | ||
|---|---|---|
| Additives | Plasticizer | |
| Certifications | RoHS 2011/65/UE | |
| Color | Natural | |
| Features | Impact Modified | |
| Processing methods | Injection Molding,Profile Extrusion | |