Property | Temperature | Value | Condition | Testing Standard | Thickness | Comment |
---|---|---|---|---|---|---|
Dichte | 1.35 g/cm³ Show Supplier Material materials with Dichte of 1.35 g/cm³ | dry | ISO 1183 | |||
Moisture absorption | 23 °C | 2.1 % Show Supplier Material materials with Moisture absorption of 2.1 % | 50%RH | ISO 62 | 2 mm | |
Wasserabsorption | 7.3 % Show Supplier Material materials with Wasserabsorption of 7.3 % | ISO 62 | 2 mm | immersion at 23°C |
Mechanisch
Property | Temperature | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|---|
Biegefestigkeit | 130 MPa Show Supplier Material materials with Biegefestigkeit of 130 MPa | dry | ISO 178 | 2mm/min | |
Biegemodul | 4.6 GPa Show Supplier Material materials with Biegemodul of 4.6 GPa | dry | ISO 178 | 2mm/min | |
Dehnung | 20 % Show Supplier Material materials with Dehnung of 20 % | dry | ISO 527-2/1A | 5mm/min | |
35 % Show Supplier Material materials with Dehnung of 35 % | 50%RH | ISO 527-2/1A | 5mm/min | ||
Elastizitätsmodul | 2.4 GPa Show Supplier Material materials with Elastizitätsmodul of 2.4 GPa | 50%RH | ISO 527-2/1A | 1mm/min | |
4.9 GPa Show Supplier Material materials with Elastizitätsmodul of 4.9 GPa | dry | ISO 527-2/1A | 1mm/min | ||
Elongation at yield | 4 % Show Supplier Material materials with Elongation at yield of 4 % | dry | ISO 527-2/1A | 50mm/min | |
Schlagfestigkeit, Charpy gekerbt | 23 °C | 6 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 6 kJ/m² | dry | ISO 179/1eA | |
23 °C | 6.5 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 6.5 kJ/m² | 50%RH | ISO 179/1eA | ||
Streckgrenze | 55 MPa Show Supplier Material materials with Streckgrenze of 55 MPa | 50%RH | ISO 527-2/1A | 50mm/min | |
80 MPa Show Supplier Material materials with Streckgrenze of 80 MPa | dry | ISO 527-2/1A | 50mm/min |
Thermisch
Property | Value | Testing Standard | Comment | ||
---|---|---|---|---|---|
Glow Wire Flammability Index | 700 °C Show Supplier Material materials with Glow Wire Flammability Index of 700 °C | IEC 60695-2-12 | |||
Schmelzpunkt | 220 °C Show Supplier Material materials with Schmelzpunkt of 220 °C | ISO 11357-1/-3 | 10°C/min | ||
Vicat-Erweichungstemperatur | 205 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 205 °C | ISO 306 | 1mm | ||
Wärmeformbeständigkeitstemperatur | 90 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 90 °C | ISO 75/2Af | 1.80 MPa | ||
190 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 190 °C | ISO 75/2Bf | 0.45 MPa | |||
Entflammbarkeit | Thickness tested (mm): 0.8, Class: HB, Standard: UL 94 | Automotive Interior Flammability(mm/min): 0 ,method: ISO 3795 and thickness tested (mm): 3 |
Elektrisch
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Surface resistivity | 1e+10 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+10 Ω/sq | 50%RH | IEC 60093 | 500V |
1e+12 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq | dry | IEC 60093 | 500V | |
Volume resistivity | 1e+11 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+11 Ω·cm | 50%RH | IEC 60093 | 500V |
1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | dry | IEC 60093 | 500V |
Rheological Properties
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Schrumpfung | 0.9 % Show Supplier Material materials with Schrumpfung of 0.9 % | 280/80/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa] |
0.9 % Show Supplier Material materials with Schrumpfung of 0.9 % | 280/80/60* | ISO 294-4 | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa], Transverse |
Technological properties
Property | ||
---|---|---|
Additives | Release agent | |
Certifications | RoHS 2011/65/UE | |
Color | Natural | |
Features | Heat Stabilized | |
Fillers | 30% Mineral Powder | |
Processing methods | Injection Molding |