Eigenschaften
Allgemein
| Property | Value | Condition | Testing Standard |
|---|---|---|---|
Dichte | 1.38 g/cm³ Show Supplier Material materials with Dichte of 1.38 g/cm³ | dry | ISO 1183 |
Mechanisch
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Biegefestigkeit | 70 MPa Show Supplier Material materials with Biegefestigkeit of 70 MPa | 50%RH | ISO 178 | 2mm/min | |
115 MPa Show Supplier Material materials with Biegefestigkeit of 115 MPa | dry | ISO 178 | 2mm/min | ||
Biegemodul | 3.4 GPa Show Supplier Material materials with Biegemodul of 3.4 GPa | 50%RH | ISO 178 | 2mm/min | |
6.8 GPa Show Supplier Material materials with Biegemodul of 6.8 GPa | dry | ISO 178 | 2mm/min | ||
Dehnung | 3.6 % Show Supplier Material materials with Dehnung of 3.6 % | dry | ISO 527-2/1A | 5mm/min | |
12 % Show Supplier Material materials with Dehnung of 12 % | 50%RH | ISO 527-2/1A | 5mm/min | ||
Elastizitätsmodul | 3.5 GPa Show Supplier Material materials with Elastizitätsmodul of 3.5 GPa | 50%RH | ISO 527-2/1A | 1mm/min | |
6.9 GPa Show Supplier Material materials with Elastizitätsmodul of 6.9 GPa | dry | ISO 527-2/1A | 1mm/min | ||
Schlagfestigkeit, Charpy gekerbt | 23 °C | 3.5 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 3.5 kJ/m² | dry | ISO 179/1eA | |
23 °C | 5 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 5 kJ/m² | 50%RH | ISO 179/1eA | ||
Zugfestigkeit | 35 MPa Show Supplier Material materials with Zugfestigkeit of 35 MPa | 50%RH | ISO 527-2/1A | 5mm/min | |
65 MPa Show Supplier Material materials with Zugfestigkeit of 65 MPa | dry | ISO 527-2/1A | 5mm/min |
Thermisch
| Property | Value | Testing Standard | Comment | ||
|---|---|---|---|---|---|
Schmelzpunkt | 220 °C Show Supplier Material materials with Schmelzpunkt of 220 °C | ISO 11357-1/-3 | 10°C/min | ||
Vicat-Erweichungstemperatur | 205 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 205 °C | ISO 306 | 50°C/h 50N | ||
Wärmeformbeständigkeitstemperatur | 95 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 95 °C | ISO 75/2Af | 1.80 MPa | ||
195 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 195 °C | ISO 75/2Bf | 0.45 MPa | |||
Entflammbarkeit | Thickness tested (mm): 1.6, Class: HB, Standard: UL 94 | Automotive Interior Flammability(mm/min): 0 ,method: ISO 3795 and thickness tested (mm): 3 | ||||
Elektrisch
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Surface resistivity | 1e+10 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+10 Ω/sq | 50%RH | IEC 60093 | 500V |
1e+12 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq | dry | IEC 60093 | 500V | |
Volume resistivity | 1e+11 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+11 Ω·cm | 50%RH | IEC 60093 | 500V |
1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | dry | IEC 60093 | 500V |
Rheological Properties
| Property | Value | Testing Standard | Condition | Comment |
|---|---|---|---|---|
Schmelzmassenflussrate | 25 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 25 g/10min | ISO 1133 | 250°C/2.16Kg | |
Schrumpfung | 0.7 % Show Supplier Material materials with Schrumpfung of 0.7 % | ISO 294-4 | 280/80/60* | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa] |
0.8 % Show Supplier Material materials with Schrumpfung of 0.8 % | ISO 294-4 | 280/80/60* | *Melt Temp. [°C] / Mold Temp. [°C] / Cavity Press. [MPa], Transverse |
Technological properties
| Property | ||
|---|---|---|
| Additives | Release agent | |
| Certifications | RoHS 2011/65/UE | |
| Color | Grey colour | |
| Fillers | 30% Mineral Powder | |
| Processing methods | Injection Molding | |