Eigenschaften
Allgemein
| Property | Temperature | Value | Condition | Testing Standard | Thickness | Comment |
|---|---|---|---|---|---|---|
Dichte | 1.56 g/cm³ Show Supplier Material materials with Dichte of 1.56 g/cm³ | dry | ISO 1183 | |||
Moisture absorption | 23 °C | 1.4 % Show Supplier Material materials with Moisture absorption of 1.4 % | 50%RH | ISO 62 | 2 mm | |
Wasserabsorption | 4.8 % Show Supplier Material materials with Wasserabsorption of 4.8 % | ISO 62 | 2 mm | immersion at 23°C |
Mechanisch
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Biegefestigkeit | 190 MPa Show Supplier Material materials with Biegefestigkeit of 190 MPa | 50%RH | ISO 178 | 2mm/min | |
350 MPa Show Supplier Material materials with Biegefestigkeit of 350 MPa | dry | ISO 178 | 2mm/min | ||
Biegemodul | 8.7 GPa Show Supplier Material materials with Biegemodul of 8.7 GPa | 50%RH | ISO 178 | 2mm/min | |
15.1 GPa Show Supplier Material materials with Biegemodul of 15.1 GPa | dry | ISO 178 | 2mm/min | ||
Dehnung | 3 % Show Supplier Material materials with Dehnung of 3 % | dry | ISO 527-2/1A | 5mm/min | |
6 % Show Supplier Material materials with Dehnung of 6 % | 50%RH | ISO 527-2/1A | 5mm/min | ||
Elastizitätsmodul | 9.8 GPa Show Supplier Material materials with Elastizitätsmodul of 9.8 GPa | 50%RH | ISO 527-2/1A | 1mm/min | |
16.8 GPa Show Supplier Material materials with Elastizitätsmodul of 16.8 GPa | dry | ISO 527-2/1A | 1mm/min | ||
Schlagfestigkeit, Charpy gekerbt | -30 °C | 14 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 14 kJ/m² | dry | ISO 179/1eA | |
-30 °C | 18 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 18 kJ/m² | 50%RH | ISO 179/1eA | ||
23 °C | 19 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 19 kJ/m² | dry | ISO 179/1eA | ||
23 °C | 25 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 25 kJ/m² | 50%RH | ISO 179/1eA | ||
Schlagzähigkeit, Charpy ungekerbt | 90 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 90 kJ/m² | dry | ISO 179/1eU | -30°C | |
95 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 95 kJ/m² | dry | ISO 179/1eU | 23°C | ||
100 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 100 kJ/m² | 50%RH | ISO 179/1eU | -30°C | ||
110 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 110 kJ/m² | 50%RH | ISO 179/1eU | 23°C | ||
Zugfestigkeit | 130 MPa Show Supplier Material materials with Zugfestigkeit of 130 MPa | 50%RH | ISO 527-2/1A | 5mm/min | |
220 MPa Show Supplier Material materials with Zugfestigkeit of 220 MPa | dry | ISO 527-2/1A | 5mm/min |
Thermisch
| Property | Value | Testing Standard | Comment | ||
|---|---|---|---|---|---|
Schmelzpunkt | 220 °C Show Supplier Material materials with Schmelzpunkt of 220 °C | ISO 11357-1/-3 | 10°C/min | ||
Wärmeformbeständigkeitstemperatur | 200 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 200 °C | ISO 75/2Af | 1.80 MPa | ||
Entflammbarkeit | Automotive Interior Flammability(mm/min): 0 ,method: ISO 3795 and thickness tested (mm): 3 | ||||
Technological properties
| Property | ||
|---|---|---|
| Additives | Release agent | |
| Certifications | RoHS 2011/65/UE | |
| Color | Black | |
| Features | DPPD Free, Heat Stabilized | |
| Fillers | 50% Glass Fiber | |
| Processing methods | Injection Molding | |