| Property | Value | Condition | Testing Standard |
|---|---|---|---|
Dichte | 1.4 g/cm³ Show Supplier Material materials with Dichte of 1.4 g/cm³ | dry | ISO 1183 |
Mechanisch
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Biegefestigkeit | 275 MPa Show Supplier Material materials with Biegefestigkeit of 275 MPa | dry | ISO 178 | 2mm/min | |
Biegemodul | 10.1 GPa Show Supplier Material materials with Biegemodul of 10.1 GPa | dry | ISO 178 | 2mm/min | |
Dehnung | 3.1 % Show Supplier Material materials with Dehnung of 3.1 % | dry | ISO 527-2/1A | 5mm/min | |
Elastizitätsmodul | 11.4 GPa Show Supplier Material materials with Elastizitätsmodul of 11.4 GPa | dry | ISO 527-2/1A | 1mm/min | |
Schlagfestigkeit, Charpy gekerbt | 23 °C | 12 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 12 kJ/m² | dry | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | 78 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 78 kJ/m² | dry | ISO 179/1eU | 23°C | |
Zugfestigkeit | 170 MPa Show Supplier Material materials with Zugfestigkeit of 170 MPa | dry | ISO 527-2/1A | 5mm/min |
Thermisch
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Schmelzpunkt | 220 °C Show Supplier Material materials with Schmelzpunkt of 220 °C | ISO 11357-1/-3 | 10°C/min |
Technological properties
| Property | ||
|---|---|---|
| Additives | Release agent | |
| Certifications | RoHS 2011/65/UE | |
| Color | Black | |
| Fillers | 35% Glass Fiber | |
| Processing methods | Injection Molding | |