Eigenschaften
Allgemein
| Property | Temperature | Value | Condition | Testing Standard | Thickness | Comment |
|---|---|---|---|---|---|---|
Dichte | 1.36 g/cm³ Show Supplier Material materials with Dichte of 1.36 g/cm³ | dry | ISO 1183 | |||
Moisture absorption | 23 °C | 1.8 % Show Supplier Material materials with Moisture absorption of 1.8 % | 50%RH | ISO 62 | 2 mm | |
Wasserabsorption | 1.2 % Show Supplier Material materials with Wasserabsorption of 1.2 % | ISO 62 | 2 mm | 24h immersion at 23°C | ||
2 % Show Supplier Material materials with Wasserabsorption of 2 % | ISO 62 | 1mm |
Mechanisch
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Biegefestigkeit | 185 MPa Show Supplier Material materials with Biegefestigkeit of 185 MPa | 50%RH | ISO 178 | 2mm/min | |
265 MPa Show Supplier Material materials with Biegefestigkeit of 265 MPa | dry | ISO 178 | 2mm/min | ||
Biegemodul | 6 GPa Show Supplier Material materials with Biegemodul of 6 GPa | 50%RH | ISO 178 | 2mm/min | |
8.3 GPa Show Supplier Material materials with Biegemodul of 8.3 GPa | dry | ISO 178 | 2mm/min | ||
Dehnung | 3.1 % Show Supplier Material materials with Dehnung of 3.1 % | dry | ISO 527-2/1A | 5mm/min | |
6 % Show Supplier Material materials with Dehnung of 6 % | 50%RH | ISO 527-2/1A | 5mm/min | ||
Elastizitätsmodul | 6.5 GPa Show Supplier Material materials with Elastizitätsmodul of 6.5 GPa | 50%RH | ISO 527-2/1A | 1mm/min | |
9.5 GPa Show Supplier Material materials with Elastizitätsmodul of 9.5 GPa | dry | ISO 527-2/1A | 1mm/min | ||
Schlagfestigkeit, Charpy gekerbt | -30 °C | 8 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 8 kJ/m² | dry | ISO 179/1eA | |
23 °C | 10 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 10 kJ/m² | dry | ISO 179/1eA | ||
23 °C | 13 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 13 kJ/m² | 50%RH | ISO 179/1eA | ||
Schlagzähigkeit, Charpy ungekerbt | 60 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 60 kJ/m² | dry | ISO 179/1eU | -30°C | |
75 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 75 kJ/m² | dry | ISO 179/1eU | 23°C | ||
80 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 80 kJ/m² | 50%RH | ISO 179/1eU | 23°C | ||
Schlagzähigkeit, Izod gekerbt | 23 °C | 10 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 10 kJ/m² | dry | ISO 180/1A | |
Zugfestigkeit | 120 MPa Show Supplier Material materials with Zugfestigkeit of 120 MPa | 50%RH | ISO 527-2/1A | 5mm/min | |
180 MPa Show Supplier Material materials with Zugfestigkeit of 180 MPa | dry | ISO 527-2/1A | 5mm/min |
Thermisch
| Property | Value | Testing Standard | Comment | ||
|---|---|---|---|---|---|
Schmelzpunkt | 262 °C Show Supplier Material materials with Schmelzpunkt of 262 °C | ISO 11357-1/-3 | 10°C/min | ||
Wärmeformbeständigkeitstemperatur | 245 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 245 °C | ISO 75/2Af | 1.80 MPa | ||
250 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 250 °C | ISO 75/2Bf | 0.45 MPa | |||
Entflammbarkeit | Thickness tested (mm): 0.8, Class: HB, Standard: UL 94 | Automotive Interior Flammability(mm/min): <30 ,method: ISO 3795 and thickness tested (mm): 3 | ||||
Rheological Properties
Technological properties
| Property | ||
|---|---|---|
| Additives | Release agent | |
| Certifications | Yellow Card, RoHS 2011/65/UE | |
| Color | Black | |
| Features | Heat Stabilized | |
| Fillers | 30% Glass Fiber | |
| Processing methods | Injection Molding | |