Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.57 g/cm³ Show Supplier Material materials with Dichte of 1.57 g/cm³ | ASTM D 792 |
Moisture absorption | 23.0 °C | 0.02 % Show Supplier Material materials with Moisture absorption of 0.02 % | ISO 62 | (23°C / 50% RH) |
Relative Dichte | 23.0 °C | 1.57 [-] Show Supplier Material materials with Relative Dichte of 1.57 [-] | ASTM D 792 | |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 391 MPa Show Supplier Material materials with Biegefestigkeit of 391 MPa | ISO 178 |
Biegemodul | 23.0 °C | 36.5 GPa Show Supplier Material materials with Biegemodul of 36.5 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 0.7 % Show Supplier Material materials with Dehnung of 0.7 % | ISO 527 | break, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 41.1 GPa Show Supplier Material materials with Elastizitätsmodul of 41.1 GPa | ISO 527 | 1 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 80 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 80 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 711 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 711 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, Total Energy | 23.0 °C | 17 J Show Supplier Material materials with Instrumented Impact, Total Energy of 17 J | ASTM D 3763 | 23°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 8 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 8 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Schlagzähigkeit, Izod ungekerbt | 23.0 °C | 47 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod ungekerbt of 47 kJ/m² | ISO 180/1U | 80*10*4, 23°C |
Zugfestigkeit | 23.0 °C | 196 MPa Show Supplier Material materials with Zugfestigkeit of 196 MPa | ISO 527 | break, 5 mm/min |
Thermisch
Property | Value | Comment |
---|---|---|
Heat deflection temperature, 0.45 MPa | 290 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 290 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
Heat deflection temperature, 1.80 MPa | 290 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 290 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
Wärmeformbeständigkeitstemperatur | 290 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 290 °C |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Availability | Europe,Asia,Americas | |
Processing methods | Melt Temperature: 380 to 390.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |