Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.25 g/cm³ Show Supplier Material materials with Dichte of 1.25 g/cm³ | ASTM D 792 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 61 MPa Show Supplier Material materials with Biegefestigkeit of 61 MPa | ISO 178 |
Biegemodul | 23.0 °C | 1.9 GPa Show Supplier Material materials with Biegemodul of 1.9 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 116 % Show Supplier Material materials with Dehnung of 116 % | ISO 527 | break, 5 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 474 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 474 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 1510 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 1510 J/m | ASTM D 4812 | 23°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 41 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 41 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Zugfestigkeit | 23.0 °C | 46 MPa Show Supplier Material materials with Zugfestigkeit of 46 MPa | ISO 527 | break, 5 mm/min |
Technological properties
Property | ||
---|---|---|
Availability | Asia,Americas | |
Processing methods | Screw Speed: 30 to 60.0rpm | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |