Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of friction | 0.33 [-] Show Supplier Material materials with Coefficient of friction of 0.33 [-] | ||
Coefficient of friction, kinetic | 0.33 [-] Show Supplier Material materials with Coefficient of friction, kinetic of 0.33 [-] | ASTM D 3702 Modified: Manual | |
Dichte | 23.0 °C | 1.12 g/cm³ Show Supplier Material materials with Dichte of 1.12 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 0.1 % Show Supplier Material materials with Moisture absorption of 0.1 % | ASTM D 570 | (23°C/50% RH/24 hrs) |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegemodul | 23.0 °C | 2.1 GPa Show Supplier Material materials with Biegemodul of 2.1 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 5 % Show Supplier Material materials with Dehnung of 5 % | ISO 527 | yield, 50 mm/min |
Elastizitätsmodul | 23.0 °C | 2.2 GPa Show Supplier Material materials with Elastizitätsmodul of 2.2 GPa | ISO 527 | 1 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 463 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 463 J/m | ASTM D 256 | notched, -30°C |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 49 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 49 kJ/m² | ISO 179/1eA | V-notch Edgew, 23°C, 80*10*4 sp=62mm |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 40 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 40 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Schlagzähigkeit, Izod ungekerbt | 23.0 °C | 208 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod ungekerbt of 208 kJ/m² | ISO 180/1U | unnotched 80*10*4, 23°C |
Zugfestigkeit | 23.0 °C | 50 MPa Show Supplier Material materials with Zugfestigkeit of 50 MPa | ISO 527 | yield, 50 mm/min |
Thermisch
Property | Value | Comment |
---|---|---|
Heat deflection temperature, 0.45 MPa | 125 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 125 °C | ASTM D 648 | 3.2 mm, unannealed |
Heat deflection temperature, 1.80 MPa | 104 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 104 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
Vicat-Erweichungstemperatur | 124 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 124 °C | ISO 306 | Rate B/120 |
Wärmeformbeständigkeitstemperatur | 104 - 125 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 104 - 125 °C |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzmassenflussrate | 23 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 23 g/10min | ASTM D 1238 | 260°C/5.0 kgf | |
Schmelzvolumenflussrate | 21 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 21 cm³/10min | ISO 1133 | MVR at 260°C/5.0 kg | |
Schrumpfung | 23.0 °C | 0.7 % Show Supplier Material materials with Schrumpfung of 0.7 % | SABIC method |
Schrumpfung, diagonal | 23.0 °C | 0.8 % Show Supplier Material materials with Schrumpfung, diagonal of 0.8 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Automotive , Console, Infotainment/Telematic, Interior, Interior trims | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 105 to 110.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |