Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of friction | 0.39 - 0.41 [-] Show Supplier Material materials with Coefficient of friction of 0.39 - 0.41 [-] | ||
Coefficient of friction, kinetic | 0.41 [-] Show Supplier Material materials with Coefficient of friction, kinetic of 0.41 [-] | ASTM D 3702 Modified: Manual | |
Coefficient of friction, static | 0.39 [-] Show Supplier Material materials with Coefficient of friction, static of 0.39 [-] | ASTM D 3702 Modified: Manual | |
Dichte | 23.0 °C | 1.32 g/cm³ Show Supplier Material materials with Dichte of 1.32 g/cm³ | ASTM D 792 |
Moisture absorption | 23.0 °C | 0.1 % Show Supplier Material materials with Moisture absorption of 0.1 % | ASTM D 570 | (23°C/50% RH/24 hrs) |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 158 MPa Show Supplier Material materials with Biegefestigkeit of 158 MPa | ASTM D 790 |
Biegemodul | 23.0 °C | 6 GPa Show Supplier Material materials with Biegemodul of 6 GPa | ASTM D 790 |
Dehnung | 23.0 °C | 2.8 % Show Supplier Material materials with Dehnung of 2.8 % | ASTM D 638 | break |
Elastizitätsmodul | 23.0 °C | 6.8 GPa Show Supplier Material materials with Elastizitätsmodul of 6.8 GPa | ASTM D 638 | 50 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 181 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 181 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 758 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 758 J/m | ASTM D 4812 | 23°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 181 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 181 kJ/m² | ASTM D 256 | notched, 23°C |
Zugfestigkeit | 23.0 °C | 105 MPa Show Supplier Material materials with Zugfestigkeit of 105 MPa | ASTM D 638 | break |
Thermisch
Property | Temperature | Value | Comment |
---|---|---|---|
Heat deflection temperature, 0.45 MPa | 142 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 142 °C | ASTM D 648 | 3.2 mm, unannealed | |
Heat deflection temperature, 1.80 MPa | 137 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 137 °C | ASTM D 648 | 3.2mm, unannealed | |
Koeffizient der thermischen Ausdehnung | 23.0 °C | 6.84E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 6.84E-5 1/K | ASTM E 831 | -40°C to 40°C |
Wärmeformbeständigkeitstemperatur | 137 - 142 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 137 - 142 °C | ||
Wärmeleitfähigkeit | 23.0 °C | 0.25 W/(m·K) Show Supplier Material materials with Wärmeleitfähigkeit of 0.25 W/(m·K) | ASTM E 1530 | |
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 7.38E-5 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 7.38E-5 1/K | ASTM E 831 | -40°C to 40°C |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Medical Device, Surgical Devices | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 100°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |