Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 90 MPa Show Supplier Material materials with Biegefestigkeit of 90 MPa | ISO 178 | 2 mm/min |
Biegemodul | 23.0 °C | 2.6 GPa Show Supplier Material materials with Biegemodul of 2.6 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 50 % Show Supplier Material materials with Dehnung of 50 % | ISO 527 | break, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 2.6 GPa Show Supplier Material materials with Elastizitätsmodul of 2.6 GPa | ISO 527 | 1 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 650 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 650 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 2150 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 2150 J/m | ASTM D 4812 | 23°C |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 15 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 15 kJ/m² | ISO 179/1eA | V-notch Edgew, 23°C, 80*10*4 sp=62mm |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 15 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 15 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Schlagzähigkeit, Izod ungekerbt | 23.0 °C | 130 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod ungekerbt of 130 kJ/m² | ISO 180/1U | unnotched 80*10*4, 23°C |
Zugfestigkeit | 23.0 °C | 40 MPa Show Supplier Material materials with Zugfestigkeit of 40 MPa | ISO 527 | break, 5 mm/min |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 117 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 117 °C | ASTM D 648 | 3.2 mm, unannealed | |||
Heat deflection temperature, 1.80 MPa | 105 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 105 °C | ASTM D 648 | 3.2mm, unannealed | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 6.4E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 6.4E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Wärmeformbeständigkeitstemperatur | 105 - 117 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 105 - 117 °C | ||||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 7.2E-5 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 7.2E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Entflammbarkeit | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=103685620- - <br> UL Recognized, 94V-0 Flame Class Rating: 0.8mm UL 94 |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric constant, 10GHz | 23.0 °C | 2.9 [-] Show Supplier Material materials with Dielectric constant, 10GHz of 2.9 [-] | SABIC method |
Dielectric constant, 1GHz | 23.0 °C | 3 [-] Show Supplier Material materials with Dielectric constant, 1GHz of 3 [-] | SABIC method | 1.1 GHz |
Dielectric constant, 5GHz | 23.0 °C | 2.9 [-] Show Supplier Material materials with Dielectric constant, 5GHz of 2.9 [-] | SABIC method |
Dielektrizitätskonstante | 23.0 °C | 2.8 [-] Show Supplier Material materials with Dielektrizitätskonstante of 2.8 [-] | SABIC method | 20 GHz |
Dissipation factor, 1GHz | 23.0 °C | 7E-3 [-] Show Supplier Material materials with Dissipation factor, 1GHz of 7E-3 [-] | SABIC method | |
Dissipation factor, 5GHz | 23.0 °C | 7E-3 [-] Show Supplier Material materials with Dissipation factor, 5GHz of 7E-3 [-] | SABIC method |
Verlustfaktor | 23.0 °C | 6E-3 [-] Show Supplier Material materials with Verlustfaktor of 6E-3 [-] | SABIC method |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzvolumenflussrate | 16 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 16 cm³/10min | ISO 1133 | MVR at 280°C/2.16 kg | |
Schrumpfung | 23.0 °C | 0.5 % Show Supplier Material materials with Schrumpfung of 0.5 % | ASTM D 955 | 24 hrs |
Schrumpfung, diagonal | 23.0 °C | 0.5 % Show Supplier Material materials with Schrumpfung, diagonal of 0.5 % | ASTM D 955 | 24 hrs |
Technological properties
Property | ||
---|---|---|
Application areas | Electronic Components | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 110 to 120.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |