Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.32 g/cm³ Show Supplier Material materials with Dichte of 1.32 g/cm³ | ASTM D 792 |
Moisture absorption | 23.0 °C | 0.01 % Show Supplier Material materials with Moisture absorption of 0.01 % | ISO 62 | (23°C / 50% RH) |
Relative Dichte | 23.0 °C | 1.33 [-] Show Supplier Material materials with Relative Dichte of 1.33 [-] | ASTM D 792 | |
Wasserabsorption | 23.0 °C | 0.06 % Show Supplier Material materials with Wasserabsorption of 0.06 % | ISO 62-1 | (23°C/saturated) |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 168 MPa Show Supplier Material materials with Biegefestigkeit of 168 MPa | ISO 178 |
Biegemodul | 23.0 °C | 8 GPa Show Supplier Material materials with Biegemodul of 8 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 2 % Show Supplier Material materials with Dehnung of 2 % | ISO 527 | yield, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 8.3 GPa Show Supplier Material materials with Elastizitätsmodul of 8.3 GPa | ISO 527 | 1 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 98 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 98 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 449 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 449 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, Total Energy | 23.0 °C | 7 J Show Supplier Material materials with Instrumented Impact, Total Energy of 7 J | ASTM D 3763 | 23°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 9 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 9 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Schlagzähigkeit, Izod ungekerbt | 23.0 °C | 27 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod ungekerbt of 27 kJ/m² | ISO 180/1U | 80*10*4, 23°C |
Zugfestigkeit | 23.0 °C | 105 MPa Show Supplier Material materials with Zugfestigkeit of 105 MPa | ISO 527 | yield, 5 mm/min |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 135 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 135 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |||
Heat deflection temperature, 1.80 MPa | 130 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 130 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 2.68E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 2.68E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Vicat-Erweichungstemperatur | 129 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 129 °C | ISO 306 | Rate B/50 | |||
Wärmeformbeständigkeitstemperatur | 130 - 135 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 130 - 135 °C | ||||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 5.67E-5 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 5.67E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Entflammbarkeit | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=104050517- - <br> UL Recognized, 94HB Flame Class Rating: ≥0.75mm UL 94 | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Kriechstromfestigkeit | 23.0 °C | 200 V Show Supplier Material materials with Kriechstromfestigkeit of 200 V | IEC 60112 | |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 56 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 56 g/10min | ASTM D 1238 | 260°C/5.0 kgf | |
Schmelzvolumenflussrate | 47 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 47 cm³/10min | ISO 1133 | MVR at 260°C/5.0 kg | |
Schrumpfung | 23.0 °C | 0.34 % Show Supplier Material materials with Schrumpfung of 0.34 % | ISO 294 | 24 hrs |
Schrumpfung, diagonal | 23.0 °C | 0.53 % Show Supplier Material materials with Schrumpfung, diagonal of 0.53 % | ISO 294 | 24 hrs |
Technological properties
| Property | ||
|---|---|---|
| Availability | Europe,Asia,Americas | |
| Processing methods | Drying Time: 2hrs | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |