Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.48 g/cm³ Show Supplier Material materials with Dichte of 1.48 g/cm³ | ASTM D 792 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 166 MPa Show Supplier Material materials with Biegefestigkeit of 166 MPa | ISO 178 | break, 2 mm/min |
Biegemodul | 23.0 °C | 7.4 GPa Show Supplier Material materials with Biegemodul of 7.4 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 2.5 % Show Supplier Material materials with Dehnung of 2.5 % | ISO 527 | yield, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 8.2 GPa Show Supplier Material materials with Elastizitätsmodul of 8.2 GPa | ISO 527 | 1 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 124 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 124 J/m | ASTM D 256 | notched, -30°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 840 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 840 J/m | ASTM D 4812 | 23°C |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 12 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 12 kJ/m² | ISO 179/2C | -30°C |
Schlagzähigkeit, Charpy ungekerbt | 23.0 °C | 62 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 62 kJ/m² | ISO 179/2C | 23°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 11 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 11 kJ/m² | ISO 180/1A | notched 80*10*4, -30°C |
Schlagzähigkeit, Izod ungekerbt | 23.0 °C | 52 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod ungekerbt of 52 kJ/m² | ISO 180/1U | unnotched 80*10*4, 23°C |
Zugfestigkeit | 23.0 °C | 120 MPa Show Supplier Material materials with Zugfestigkeit of 120 MPa | ISO 527 | yield, 5 mm/min |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 158 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 158 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 2.2E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 2.2E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Relative temperature index, electrical | 75 °C Show Supplier Material materials with Relative temperature index, electrical of 75 °C | UL 746B | |||
Relative temperature index, mechanical impact | 75 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 75 °C | UL 746B | |||
Relative temperature index, mechanical strength | 75 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 75 °C | UL 746B | |||
Vicat-Erweichungstemperatur | 157 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 157 °C | ISO 306 | Rate B/50 | |||
Wärmeformbeständigkeitstemperatur | 158 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 158 °C | ||||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 8.2E-5 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 8.2E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Entflammbarkeit | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=104047809- - <br> UL Recognized, 94HB Flame Class Rating: ≥0.7mm UL 94 |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric constant, 1GHz | 23.0 °C | 3.53 [-] Show Supplier Material materials with Dielectric constant, 1GHz of 3.53 [-] | SABIC method | 1.1 GHz |
Dielektrizitätskonstante | 23.0 °C | 3.54 [-] Show Supplier Material materials with Dielektrizitätskonstante of 3.54 [-] | SABIC method | 1.9 GHz |
Dissipation factor, 1GHz | 23.0 °C | 0.01 [-] Show Supplier Material materials with Dissipation factor, 1GHz of 0.01 [-] | SABIC method | |
Verlustfaktor | 23.0 °C | 0.01 [-] Show Supplier Material materials with Verlustfaktor of 0.01 [-] | SABIC method |
Volume resistivity | 23.0 °C | 1.05E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 1.05E+15 Ω·cm | ASTM D 257 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzvolumenflussrate | 8.5 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 8.5 cm³/10min | ISO 1133 | MVR at 250°C/5.0 kg | |
Schrumpfung | 23.0 °C | 0.2 % Show Supplier Material materials with Schrumpfung of 0.2 % | SABIC method |
Schrumpfung, diagonal | 23.0 °C | 0.4 % Show Supplier Material materials with Schrumpfung, diagonal of 0.4 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Auto Electrical, Personal Computing, Wireless Communications | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 100 to 120.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |