Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Relative Dichte | 23.0 °C | 1.26 [-] Show Supplier Material materials with Relative Dichte of 1.26 [-] | ASTM D 792 | |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 155 MPa Show Supplier Material materials with Biegefestigkeit of 155 MPa | ASTM D 790 | yld, 2.6 mm/min, 100 mm span |
Biegemodul | 23.0 °C | 9.7 GPa Show Supplier Material materials with Biegemodul of 9.7 GPa | ASTM D 790 | 2.6 mm/min, 100 mm span |
Dehnung | 23.0 °C | 6.6 % Show Supplier Material materials with Dehnung of 6.6 % | SABIC - Japan Method | brk, Type I, 10 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 66.4 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 66.4 J/m | ASTM D 256 | notched, 23°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 66.4 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 66.4 kJ/m² | ASTM D 256 | notched, 23°C |
Zugfestigkeit | 23.0 °C | 120.7 MPa Show Supplier Material materials with Zugfestigkeit of 120.7 MPa | SABIC - Japan Method | yld, Type I, 10 mm/min |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Aschegehalt | 23.0 °C | 17.82 % Show Supplier Material materials with Aschegehalt of 17.82 % | w/w | ||
Heat deflection temperature, 1.80 MPa | 133.4 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 133.4 °C | ASTM D 648 | 6.4 mm, unannealed | |||
Wärmeformbeständigkeitstemperatur | 133.4 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 133.4 °C | ||||
Entflammbarkeit | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=237042- - <br> UL Recognized, 94V-1 Flame Class Rating: ≥1.5mm UL 94 <br> UL Recognized, 94V-0 Flame Class Rating: ≥3mm UL 94 |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Sheet resistivity, ROA | 23.0 °C | 42000 Ω Show Supplier Material materials with Sheet resistivity, ROA of 42000 Ω | ASTM D 257 |
Rheological Properties
Property | Value | Comment |
---|---|---|
Schmelzmassenflussrate | 10.6 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 10.6 g/10min | ASTM D 1238 | 300°C/5.0 kgf |
Technological properties
Property | ||
---|---|---|
Application areas | Electrical Components & Infrastructure | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 120°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |