Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.39 g/cm³ Show Supplier Material materials with Dichte of 1.39 g/cm³ | ASTM D 792 |
Moisture absorption | 23.0 °C | 0.2 % Show Supplier Material materials with Moisture absorption of 0.2 % | ASTM D 570 | (23°C/50% RH/24 hrs) |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 270 MPa Show Supplier Material materials with Biegefestigkeit of 270 MPa | ASTM D 790 | brk, 1.3 mm/min, 50 mm span |
Biegemodul | 23.0 °C | 18.1 GPa Show Supplier Material materials with Biegemodul of 18.1 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Dehnung | 23.0 °C | 1.9 % Show Supplier Material materials with Dehnung of 1.9 % | ASTM D 638 | brk, Type I, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 21.8 GPa Show Supplier Material materials with Elastizitätsmodul of 21.8 GPa | ASTM D 638 | 50 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 48 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 48 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 375 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 375 J/m | ASTM D 4812 | 23°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 48 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 48 kJ/m² | ASTM D 256 | notched, 23°C |
Zugfestigkeit | 23.0 °C | 211 MPa Show Supplier Material materials with Zugfestigkeit of 211 MPa | ASTM D 638 | brk, Type I, 5 mm/min |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 203 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 203 °C | ASTM D 648 | 6.4 mm, unannealed | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 4.6E-6 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 4.6E-6 1/K | ASTM E 831 | -40°C to 40°C | ||
Relative temperature index, mechanical impact | 105 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 105 °C | UL 746B | |||
Relative temperature index, mechanical strength | 105 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 105 °C | UL 746B | |||
Wärmeformbeständigkeitstemperatur | 203 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 203 °C | ||||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 4.3E-5 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 4.3E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Entflammbarkeit | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101260584- - <br> UL Recognized, 94V-0 Flame Class Rating: 0.4mm UL 94 |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Sheet resistivity, ROA | 23.0 °C | 5000 - 500000 Ω Show Supplier Material materials with Sheet resistivity, ROA of 5000 - 500000 Ω | ASTM D 257 |
Volume resistivity | 23.0 °C | 5.00E+3 - 5.00E+6 Ω·cm Show Supplier Material materials with Volume resistivity of 5.00E+3 - 5.00E+6 Ω·cm | ASTM D 257 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Data Management | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 150°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |