Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Moisture absorption | 23.0 °C | 0.39 % Show Supplier Material materials with Moisture absorption of 0.39 % | ISO 62-4 | (23°C/50% RH/Equilibrium) |
Relative Dichte | 23.0 °C | 1.1 [-] Show Supplier Material materials with Relative Dichte of 1.1 [-] | ASTM D 792 |
Wasserabsorption | 23.0 °C | 1.99 % Show Supplier Material materials with Wasserabsorption of 1.99 % | ISO 62-1 | (23°C/24hrs) |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 98 MPa Show Supplier Material materials with Biegefestigkeit of 98 MPa | ISO 178 | break, 2 mm/min |
Biegemodul | 23.0 °C | 2.4 GPa Show Supplier Material materials with Biegemodul of 2.4 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 51 % Show Supplier Material materials with Dehnung of 51 % | ISO 527 | break, 50 mm/min |
Elastizitätsmodul | 23.0 °C | 2.3 GPa Show Supplier Material materials with Elastizitätsmodul of 2.3 GPa | ASTM D 638 | 50 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 100 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 100 J/m | ASTM D 256 |
Instrumented Impact, at Peak | 23.0 °C | 48 J Show Supplier Material materials with Instrumented Impact, at Peak of 48 J | ASTM D 3763 | 23°C |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 10 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 10 kJ/m² | ISO 179/2C | -20°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 8 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 8 kJ/m² | ISO 180/4A | notched 63.5*12.7*3.2, -30°C |
Zugfestigkeit | 23.0 °C | 66 MPa Show Supplier Material materials with Zugfestigkeit of 66 MPa | ISO 527 | yield, 50 mm/min |
Thermisch
Property | Temperature | Value | Comment |
---|---|---|---|
Heat deflection temperature, 0.45 MPa | 181 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 181 °C | ISO 75/Be | Edgew 120*10*4 sp=100mm | |
Koeffizient der thermischen Ausdehnung | 23.0 °C | 9E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 9E-5 1/K | ASTM E 831 | -40°C to 40°C |
Wärmeformbeständigkeitstemperatur | 181 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 181 °C | ||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 1.53E-4 1/K Show Supplier Material materials with thermischer Ausdehnungskoeffizient, transversal of 1.53E-4 1/K | ASTM E 831 | 60°C to 138°C |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 0.02 [-] | ASTM D 150 |
Durchschlagfestigkeit | 23.0 °C | 22.4 kV/mm Show Supplier Material materials with Durchschlagfestigkeit of 22.4 kV/mm | ASTM D 149 | in oil, 1.6 mm |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzmassenflussrate | 24 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 24 g/10min | ASTM D 1238 | 280°C/2.16 kgf | |
Schrumpfung | 23.0 °C | 1.4 % Show Supplier Material materials with Schrumpfung of 1.4 % | ASTM D 955 | 24 hrs |
Schrumpfung, diagonal | 23.0 °C | 1.2 % Show Supplier Material materials with Schrumpfung, diagonal of 1.2 % | ASTM D 955 | 24 hrs |
Technological properties
Property | ||
---|---|---|
Application areas | Auto Electrical, Circuit Protection, Auto Aftermarket, Electronic Components, Recreational Vehicle | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 95 to 105.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |