Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.31 g/cm³ Show Supplier Material materials with Dichte of 1.31 g/cm³ | ISO 1183 |
Relative Dichte | 23.0 °C | 1.31 [-] Show Supplier Material materials with Relative Dichte of 1.31 [-] | ASTM D 792 | |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 148 MPa Show Supplier Material materials with Biegefestigkeit of 148 MPa | ISO 178 | yield, 2 mm/min |
Biegemodul | 23.0 °C | 3.3 GPa Show Supplier Material materials with Biegemodul of 3.3 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 6 % Show Supplier Material materials with Dehnung of 6 % | ISO 527 | break, 5 mm/min |
Elastizitätsmodul | 23.0 °C | 3.3 GPa Show Supplier Material materials with Elastizitätsmodul of 3.3 GPa | ISO 527 | 1 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 37 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 37 J/m | ASTM D 256 | notched, 23°C |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 4 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 4 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Zugfestigkeit | 23.0 °C | 89 MPa Show Supplier Material materials with Zugfestigkeit of 89 MPa | ISO 527 | break, 5 mm/min |
Thermisch
Property | Value | Comment |
---|---|---|
Heat deflection temperature, 1.80 MPa | 189 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 189 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
Vicat-Erweichungstemperatur | 213 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 213 °C | ISO 306 | Rate B/120 |
Wärmeformbeständigkeitstemperatur | 189 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 189 °C |
Rheological Properties
Property | Value | Comment |
---|---|---|
Schmelzmassenflussrate | 12.3 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 12.3 g/10min | ASTM D 1238 | 337°C/6.6 kgf |
Schmelzvolumenflussrate | 10 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 10 cm³/10min | ISO 1133 | MVR at 340°C/5.0 kg |
Technological properties
Property | ||
---|---|---|
Application areas | Surgical Devices, Medical Device | |
Availability | Europe,Asia,Americas | |
Processing methods | Nozzle Temperature: 390 to 400.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |